| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.75 - 2.25 g/cc | 1.75 - 2.25 g/cc | ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 63 - 77 | 63 - 77 | ASTM D2240 | ||
| Tensile Strength at Break | >= 1.24 MPa | >= 180 psi | ASTM D412 | ||
| Elongation at Break | 60 - 260 % | 60 - 260 % | ASTM D412 | ||
| Tear Strength | 6.13 kN/m | 35.0 pli | ASTM D624 | ||
| Compression Set | <= 30 % @Temperature 100 °C, Time 252000 sec | <= 30 % @Temperature 212 °F, Time 70.0 hour | ASTM D395 Method B | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | <= 0.012 ohm-cm | <= 0.012 ohm-cm | MIL-DTL-83528 | ||
| <= 0.015 ohm-cm | <= 0.015 ohm-cm | Life Test/Post Tensile; MIL-DTL-83528 Para.4.6.12 | |||
| Shielding Effectiveness | >= 55 dB @Frequency 200000 Hz | >= 55 dB @Frequency 200000 Hz | H Field; MIL-DTL-83528 Para.4.6.12 | ||
| >= 75 dB @Frequency 4.00e+10 Hz | >= 75 dB @Frequency 4.00e+10 Hz | Plane Wave; MIL-DTL-83528 Para.4.6.12 | |||
| >= 90 dB @Frequency 1.00e+10 Hz | >= 90 dB @Frequency 1.00e+10 Hz | Plane Wave; MIL-DTL-83528 Para.4.6.12 | |||
| >= 95 dB @Frequency 2.00e+9 Hz | >= 95 dB @Frequency 2.00e+9 Hz | Plane Wave; MIL-DTL-83528 Para.4.6.12 | |||
| >= 100 dB @Frequency 5.00e+8 Hz | >= 100 dB @Frequency 5.00e+8 Hz | E Field; MIL-DTL-83528 Para.4.6.12 | |||
| >= 110 dB @Frequency 1.00e+8 Hz | >= 110 dB @Frequency 1.00e+8 Hz | E Field; MIL-DTL-83528 Para.4.6.12 | |||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 1.20 W/m-K @Pressure 2.07 MPa | 8.33 BTU-in/hr-ft²-°F @Pressure 300 psi | ASTM D5470 | ||
| Maximum Service Temperature, Air | 200 °C | 392 °F | |||
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | Flex TR10; ASTM D1329 | ||
| Descriptive Properties | |||||
| Binder | Fluorosilicone | ||||
| EMP Survivability | >0.9 kA / in | MIL-DTL-83528 Para.4.6.16 | |||
| Filler | Passivated Ag/Al | ||||
| Gravimetric Weight Loss, mg | 3.5 | ||||
| Heat Aging | <0.015 ohm-cm | MIL-DTL-83528 Para.4.6.15 | |||
| Type | D | MIL-DTL-83528 | |||
| Vibration Resistance, After | <0.012 ohm-cm | MIL-DTL-83528 Para.4.6.13 | |||
| Vibration Resistance, During, ohm-cm max | <0.015 ohm-cm | MIL-DTL-83528 Para.4.6.13 | |||