- 拉伸强度 [MPa]: 2.4
- 脆化温度 [℃]: -24.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.85 g/cc | 1.85 g/cc | at 25°C |
| Mooney Viscosity | 30 @Temperature 121 °C | 30 @Temperature 250 °F | ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 69 | 69 | Peak value, at 25°C |
| Tensile Strength at Break | 14.6 MPa | 2120 psi | |
| Tensile Strength, Yield | 2.40 MPa @Strain 100 % | 348 psi @Strain 100 % | |
| Elongation at Break | 310 % | 310 % | |
| Tear Strength | 23.5 kN/m | 134 pli | at 25°C |
| Compression Set | 20 % | 20 % | 70 hours at 25°C |
| 11 % @Temperature 100 °C | 11 % @Temperature 212 °F | 70 hours | |
| 16 % @Temperature 175 °C | 16 % @Temperature 347 °F | 70 hours | |
| 27 % @Temperature 200 °C | 27 % @Temperature 392 °F | 70 hours | |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -18.0 °C | -0.400 °F | TR test, TR10 |
| -13.0 °C | 8.60 °F | Gehman torsion test, T10 | |
| -9.00 °C | 15.8 °F | TR test, TR70 | |
| -6.00 °C | 21.2 °F | Gehman torsion test, T2 | |
| Brittleness Temperature | -24.0 °C | -11.2 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 170 °C | 338 °F | Cure Measuring Temperature |
| Cure Time | 2.90 min | 0.0483 hour | Curelastmeter |