- 拉伸强度 [MPa]: 3.3
- 脆化温度 [℃]: -21.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.85 g/cc | 1.85 g/cc | at 25°C |
| Mooney Viscosity | 29 @Temperature 121 °C | 29 @Temperature 250 °F | ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 69 | 69 | Peak value, at 25°C |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | |
| Tensile Strength, Yield | 3.30 MPa @Strain 100 % | 479 psi @Strain 100 % | |
| Elongation at Break | 240 % | 240 % | |
| Tear Strength | 22.5 kN/m | 128 pli | at 25°C |
| Compression Set | 13 % | 13 % | 70 hours at 25°C |
| 9.0 % @Temperature 100 °C | 9.0 % @Temperature 212 °F | 70 hours | |
| 13 % @Temperature 175 °C | 13 % @Temperature 347 °F | 70 hours | |
| 23 % @Temperature 200 °C | 23 % @Temperature 392 °F | 70 hours | |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -18.0 °C | -0.400 °F | TR test, TR10 |
| -15.6 °C | 3.92 °F | Gehman torsion test, T10 | |
| -8.50 °C | 16.7 °F | Gehman torsion test, T2 | |
| -8.00 °C | 17.6 °F | TR test, TR70 | |
| Brittleness Temperature | -21.0 °C | -5.80 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 170 °C | 338 °F | Cure Measuring Temperature |
| Cure Time | 3.70 min | 0.0617 hour | Curelastmeter |