- 拉伸强度 [MPa]: 4.1
- 脆化温度 [℃]: -18.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.91 g/cc | 1.91 g/cc | at 25°C |
| Mooney Viscosity | 36 @Temperature 121 °C | 36 @Temperature 250 °F | ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 73 | 73 | Peak value, at 25°C |
| Tensile Strength at Break | 12.9 MPa | 1870 psi | |
| Tensile Strength, Yield | 4.10 MPa @Strain 100 % | 595 psi @Strain 100 % | |
| Elongation at Break | 290 % | 290 % | |
| Tear Strength | 19.8 kN/m | 113 pli | at 25°C |
| Compression Set | 32 % | 32 % | 70 hours at 25°C |
| 24 % @Temperature 100 °C | 24 % @Temperature 212 °F | 70 hours | |
| 28 % @Temperature 175 °C | 28 % @Temperature 347 °F | 70 hours | |
| 44 % @Temperature 200 °C | 44 % @Temperature 392 °F | 70 hours | |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -11.0 °C | 12.2 °F | TR test, TR10 |
| -9.00 °C | 15.8 °F | Gehman torsion test, T10 | |
| -5.00 °C | 23.0 °F | TR test, TR70 | |
| -2.50 °C | 27.5 °F | Gehman torsion test, T2 | |
| Brittleness Temperature | -18.0 °C | -0.400 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 °C | 320 °F | Cure Measuring Temperature |
| Cure Time | 6.70 min | 0.112 hour | Curelastmeter |