- 拉伸强度 [MPa]: 4.4
- 脆化温度 [℃]: -21.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.89 g/cc | 1.89 g/cc | at 25°C |
| Mooney Viscosity | 48 @Temperature 121 °C | 48 @Temperature 250 °F | ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 74 | 74 | Peak value, at 25°C |
| Tensile Strength at Break | 15.9 MPa | 2310 psi | |
| Tensile Strength, Yield | 4.40 MPa @Strain 100 % | 638 psi @Strain 100 % | |
| Elongation at Break | 210 % | 210 % | |
| Tear Strength | 20.6 kN/m | 118 pli | at 25°C |
| Compression Set | 13 % | 13 % | 70 hours at 25°C |
| 9.0 % @Temperature 100 °C | 9.0 % @Temperature 212 °F | 70 hours | |
| 18 % @Temperature 175 °C | 18 % @Temperature 347 °F | 70 hours | |
| 25 % @Temperature 200 °C | 25 % @Temperature 392 °F | 70 hours | |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -14.0 °C | 6.80 °F | TR test, TR10 |
| -12.0 °C | 10.4 °F | Gehman torsion test, T10 | |
| -8.00 °C | 17.6 °F | TR test, TR70 | |
| -7.00 °C | 19.4 °F | Gehman torsion test, T2 | |
| Brittleness Temperature | -21.0 °C | -5.80 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 170 °C | 338 °F | Cure Measuring Temperature |
| Cure Time | 2.40 min | 0.0400 hour | Curelastmeter |