- 弯曲强度 [MPa]: 20.4
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 72 | 72 | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Tensile Strength, Ultimate | 20.4 MPa | 2960 psi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Elongation at Break | 214 % | 214 % | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Modulus of Elasticity | 0.000800 GPa | 0.116 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| 100% Modulus | 0.00700 GPa | 1.02 ksi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Compression Set | 37 % @Temperature 200 °C | 37 % @Temperature 392 °F | Method B, O-rings 22 hr at 200°C (Post Cured 16 hr at 232°C) |