- 密度 [g/cm3]: 1.18
- 弯曲强度 [MPa]: 11.0
- 脆化温度 [℃]: -39.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | |
| Mooney Viscosity | 80 @Temperature 100 °C | 80 @Temperature 212 °F | ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 71 | 71 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 11.0 MPa | 1600 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 355 % | 355 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00440 GPa | 0.638 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.0101 GPa | 1.46 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 29.9 kN/m | 171 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 66 % @Temperature 100 °C | 66 % @Temperature 212 °F | Pellets cured MDR TC95 + 15 min at 160°C, 22 hr at 100°C; Method B |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -39.0 °C | -38.2 °F | Temperature Retraction, TR-10 |