- 密度 [g/cm3]: 0.6
- 吸水率 [%]: 0.3
- 弯曲强度 [MPa]: 21.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.600 g/cc | 0.0217 lb/in³ | |
| Water Absorption | 0.30 % | 0.30 % | Saturation in water |
| Water Absorption at Saturation | 0.30 % | 0.30 % | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | |
| Elongation at Break | 7.0 % | 7.0 % | |
| Tensile Modulus | 0.800 GPa | 116 ksi | |
| Charpy Impact Unnotched | 1.80 J/cm² | 8.57 ft-lb/in² | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 7.00e+14 ohm-cm | 7.00e+14 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 73.0 µm/m-°C @Temperature 20.0 °C | 40.6 µin/in-°F @Temperature 68.0 °F | in flow direction |
| CTE, linear, Transverse to Flow | 73.0 µm/m-°C @Temperature 20.0 °C | 40.6 µin/in-°F @Temperature 68.0 °F | |
| Flammability, UL94 | V-0 @Thickness 6.00 mm | V-0 @Thickness 0.236 in | |