- 弯曲强度 [MPa]: 11.4
- 弯曲模量 [MPa]: 1.18
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.630 g/cc | 0.630 g/cc | ASTM D792-66 | ||
| Brookfield Viscosity | 600 cP @Temperature 23.9 °C | 600 cP @Temperature 75.0 °F | Part A; ASTM D2393 | ||
| 700 cP @Temperature 23.9 °C | 700 cP @Temperature 75.0 °F | Mixed; ASTM D2393 | |||
| 800 cP @Temperature 23.9 °C | 800 cP @Temperature 75.0 °F | Part B; ASTM D2393 | |||
| Linear Mold Shrinkage | 0.0029 cm/cm | 0.0029 in/in | ASTM D2566-69 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 65 @Temperature 23.9 °C | 65 @Temperature 75.0 °F | ASTM D2240 | ||
| Tensile Strength, Ultimate | 11.4 MPa | 1660 psi | ASTM D638 | ||
| Flexural Strength | 18.8 MPa | 2730 psi | ASTM D790 | ||
| Flexural Modulus | 1.18 GPa | 171 ksi | ASTM-D-790 | ||
| Compressive Strength | 21.0 MPa | 3050 psi | ASTM D695 | ||
| Izod Impact Resistance | 0.122 J/cm² | 0.580 ft-lb/in² | |||
| Thermal Properties | Metric | English | Comments | ||
| Heat Distortion Temperature | 56.1 °C | 133 °F | ASTM-D-648-56 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 - 120 min @Temperature 24.0 °C | 1.00 - 2.00 hour @Temperature 75.2 °F | demold time | ||
| Pot Life | 5.0 - 6.0 min @Temperature 24.0 °C | 5.0 - 6.0 min @Temperature 75.2 °F | 1 lb. mass | ||
| Descriptive Properties | |||||
| Mix Ratio | 1:1 by weight or volume | ||||