- 弯曲强度 [MPa]: 18.6
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | |||
| Brookfield Viscosity | 2500 cP @Temperature 23.9 °C | 2500 cP @Temperature 75.0 °F | mixed | ||
| Linear Mold Shrinkage | 0.0025 cm/cm | 0.0025 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 85 - 90 | 85 - 90 | |||
| Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | |||
| Elongation at Break | 550 % | 550 % | |||
| Tear Strength | 68.4 kN/m | 390 pli | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 240 - 360 min | 4.00 - 6.00 hour | demold time | ||
| 4320 - 7200 min | 72.0 - 120 hour | full cure | |||
| Pot Life | 20 min @Temperature 25.0 °C | 20 min @Temperature 77.0 °F | work life (100g) | ||
| 30 min @Temperature 25.0 °C | 30 min @Temperature 77.0 °F | gel time (180g) | |||
| Descriptive Properties | |||||
| Mix Ratio | 100:55 by weight, 185:100 by volume (resin/hardener) | ||||