- 弯曲强度 [MPa]: 11.2
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.02 g/cc | 1.02 g/cc | hardener | ||
| 1.05 g/cc | 1.05 g/cc | cured density | |||
| 1.07 g/cc | 1.07 g/cc | resin | |||
| Brookfield Viscosity | 2500 cP | 2500 cP | |||
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 58 - 62 | 58 - 62 | |||
| Tensile Strength, Ultimate | 11.20 MPa | 1625 psi | |||
| Elongation at Break | 700 % | 700 % | |||
| Tear Strength | 35.1 kN/m | 200 pli | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 1440 min @Temperature 24.0 °C | 24.0 hour @Temperature 75.2 °F | full cure | ||
| Pot Life | 25 min @Temperature 25.0 °C | 25 min @Temperature 77.0 °F | work life | ||
| Descriptive Properties | |||||
| Mix Ratio | 100:55 by weight (resin/hardener) | ||||