- 弯曲强度 [MPa]: 39.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.80 - 1.90 g/cc | 1.80 - 1.90 g/cc | |||
| Brookfield Viscosity | 2200 cP @Temperature 23.9 °C | 2200 cP @Temperature 75.0 °F | 1 minute, #3 spindle @ 20 rpm | ||
| Linear Mold Shrinkage | 0.00080 cm/cm | 0.00080 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 83 - 87 @Temperature 23.9 °C | 83 - 87 @Temperature 75.0 °F | |||
| Tensile Strength, Ultimate | 39.3 MPa | 5700 psi | |||
| Flexural Strength | 56.5 MPa | 8200 psi | |||
| Compressive Strength | 91.0 MPa | 13200 psi | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 - 120 min @Temperature 24.0 °C | 1.00 - 2.00 hour @Temperature 75.2 °F | demold time | ||
| Pot Life | 5.0 min @Temperature 24.0 °C | 5.0 min @Temperature 75.2 °F | |||
| Descriptive Properties | |||||
| Mix Ratio | 1:1 by weight or volume | ||||