- 缺口冲击强度: 0.801
- 弯曲强度 [MPa]: 38.6
- 弯曲模量 [MPa]: 15.2
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | |||
| Brookfield Viscosity | 50 cP @Temperature 23.9 °C | 50 cP @Temperature 75.0 °F | Part A | ||
| 100 - 150 cP @Temperature 25.0 °C | 100 - 150 cP @Temperature 77.0 °F | Part B | |||
| Linear Mold Shrinkage | 0.0029 cm/cm | 0.0029 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 73 - 83 @Temperature 23.9 °C | 73 - 83 @Temperature 75.0 °F | |||
| Tensile Strength, Ultimate | 38.6 MPa | 5600 psi | ASTM D638 | ||
| Elongation at Break | 3.5 % | 3.5 % | ASTM D790 | ||
| Flexural Strength | 54.30 MPa | 7875 psi | ASTM D790 | ||
| Flexural Modulus | 15.2 GPa | 2200 ksi | ASTM D 790 | ||
| Compressive Strength | 27.48 MPa | 3985 psi | |||
| Izod Impact, Notched | 0.801 J/cm | 1.50 ft-lb/in | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 238 µm/m-°C | 132 µin/in-°F | ASTM 696 | ||
| Heat Distortion Temperature | 57.2 °C | 135 °F | ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 20.0 - 60.0 min @Temperature 24.0 °C | 0.333 - 1.00 hour @Temperature 75.2 °F | demold time | ||
| 10080 min @Temperature 25.0 °C | 168.0 hour @Temperature 77.0 °F | full cure | |||
| Pot Life | 2.0 - 2.5 min @Temperature 24.0 °C | 2.0 - 2.5 min @Temperature 75.2 °F | 1 lb. mass | ||
| Descriptive Properties | |||||
| Mix Ratio | 100:96 by weight or 1:1 volume | ||||