- 拉伸强度 [MPa]: 2648.0
- 断裂伸长率 [%]: 1675
- 弯曲模量 [MPa]: 149.6
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 2648 MPa | 384100 psi | Room temperature |
| 2137 MPa @Temperature 71.0 °C | 309900 psi @Temperature 160 °F | 1/2 hr | |
| Tensile Modulus | 155.1 GPa | 22500 ksi | Room temperature |
| 137.9 GPa @Temperature 71.0 °C | 20000 ksi @Temperature 160 °F | 1/2 hr | |
| Flexural Yield Strength | 1675 MPa | 242900 psi | Room temperature |
| 1448 MPa @Temperature 71.0 °C | 210000 psi @Temperature 160 °F | 1/2 hr | |
| Flexural Modulus | 149.6 GPa | 21700 ksi | Room temperature |
| 149.6 GPa @Temperature 71.0 °C | 21700 ksi @Temperature 160 °F | 1/2 hr | |
| Compressive Yield Strength | 1634 MPa | 237000 psi | Room temperature |
| 1413 MPa @Temperature 71.0 °C | 204900 psi @Temperature 160 °F | 1/2 hr | |
| Compressive Modulus | 137.9 GPa | 20000 ksi | Room temperature |
| Shear Strength | 82.0 MPa | 11900 psi | Short Beam, Room temperature |
| 71.7 MPa @Temperature 71.0 °C | 10400 psi @Temperature 160 °F | Short Beam, 1/2 hr | |