- 拉伸强度 [MPa]: 508.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Volatiles | 1.0 - 6.0 % | 1.0 - 6.0 % | Prepreg | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 508 MPa @Temperature -54.0 °C | 73700 psi @Temperature -65.2 °F | Dry | ||
| 513 MPa @Temperature 71.0 °C | 74400 psi @Temperature 160 °F | Wet | |||
| 563 MPa @Temperature 24.0 °C | 81700 psi @Temperature 75.2 °F | Dry | |||
| 581 MPa @Temperature 71.0 °C | 84300 psi @Temperature 160 °F | Dry | |||
| Tensile Modulus | 52.4 GPa @Temperature 71.0 °C | 7600 ksi @Temperature 160 °F | Wet | ||
| 53.8 GPa @Temperature 71.0 °C | 7800 ksi @Temperature 160 °F | Dry | |||
| 55.9 GPa @Temperature 24.0 °C | 8110 ksi @Temperature 75.2 °F | Dry | |||
| 57.9 GPa @Temperature -54.0 °C | 8400 ksi @Temperature -65.2 °F | Dry | |||
| Compressive Yield Strength | 357 MPa @Temperature 71.0 °C | 51800 psi @Temperature 160 °F | Wet | ||
| 398 MPa @Temperature 71.0 °C | 57700 psi @Temperature 160 °F | Dry | |||
| 516 MPa @Temperature 24.0 °C | 74800 psi @Temperature 75.2 °F | Dry | |||
| 641 MPa @Temperature -59.0 °C | 93000 psi @Temperature -74.2 °F | Dry | |||
| Compressive Modulus | 46.9 GPa @Temperature 71.0 °C | 6800 ksi @Temperature 160 °F | Dry | ||
| 51.7 GPa @Temperature 24.0 °C | 7500 ksi @Temperature 75.2 °F | Dry | |||
| 57.9 GPa @Temperature -59.0 °C | 8400 ksi @Temperature -74.2 °F | Dry | |||
| Descriptive Properties | |||||
| Cured Thickness per Ply (cm) | 0.039-0.046 | Laminate | |||
| Dry Resin Content (%) | 38-46 | Prepreg | |||
| Fiber Volume (%) | 45-53 | Laminate | |||
| Flow (%) | <4.5 | ||||