- 拉伸强度 [MPa]: 745.0
- 断裂伸长率 [%]: 276
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Tensile Strength, Yield | 745 MPa @Temperature -55.0 °C | 108000 psi @Temperature -67.0 °F | Dry | ||
| 855 MPa @Temperature 24.0 °C | 124000 psi @Temperature 75.2 °F | Dry | |||
| 855 MPa @Temperature 71.0 °C | 124000 psi @Temperature 160 °F | Dry | |||
| Tensile Modulus | 62.7 GPa @Temperature 71.0 °C | 9090 ksi @Temperature 160 °F | Dry | ||
| 63.4 GPa @Temperature 24.0 °C | 9200 ksi @Temperature 75.2 °F | Dry | |||
| 64.8 GPa @Temperature -55.0 °C | 9400 ksi @Temperature -67.0 °F | Dry | |||
| Flexural Yield Strength | 276 MPa | 40000 psi | Long Beam, dry | ||
| Compressive Yield Strength | 400 MPa @Temperature 71.0 °C | 58000 psi @Temperature 160 °F | Wet (14 ± 1/2 days of water immersion at 160 ± 5°F (71 ± 3°C) | ||
| 655 MPa @Temperature 24.0 °C | 95000 psi @Temperature 75.2 °F | Dry | |||
| Compressive Modulus | 59.3 GPa @Temperature 71.0 °C | 8600 ksi @Temperature 160 °F | Wet (14 ± 1/2 days of water immersion at 160 ± 5°F (71 ± 3°C) | ||
| 64.1 GPa @Temperature 24.0 °C | 9300 ksi @Temperature 75.2 °F | Dry | |||
| Bearing Yield Strength | 848 MPa @Temperature 24.0 °C | 123000 psi @Temperature 75.2 °F | Dry | ||
| Shear Strength | 26.2 MPa @Temperature 71.0 °C | 3800 psi @Temperature 160 °F | Short Beam, Wet (14 ± 1/2 days of water immersion at 160 ± 5°F (71 ± 3°C) | ||
| 60.0 MPa @Temperature 24.0 °C | 8700 psi @Temperature 75.2 °F | Short Beam, Jet Fuel (30 ± 1 days of Jet A Fuel (ASTM D1655) at 75 ± 5°F (24 ± 3°C) | |||
| 61.0 MPa @Temperature 24.0 °C | 8850 psi @Temperature 75.2 °F | Short Beam, Dry | |||
| 61.4 MPa @Temperature 24.0 °C | 8910 psi @Temperature 75.2 °F | Short Beam, Skydrol (30 ± 1 days of Type 2 Skydrol Hydraulic Fluid at 140 ± 5°F (60 ± 3°C) | |||
| Descriptive Properties | |||||
| Dry Resin Content (%) | 37-41 | Prepreg | |||
| Fiber Volume (%) | 0.02 | Laminate | |||
| Flow (%) | 8-20 | ||||
| Wet Resin Content (%) | 52 | Laminate | |||