- 拉伸强度 [MPa]: 903.0
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Tensile Strength, Yield | 903 MPa @Temperature 24.0 °C | 131000 psi @Temperature 75.2 °F | Dry | ||
| Tensile Modulus | 69.6 GPa @Temperature 24.0 °C | 10100 ksi @Temperature 75.2 °F | Dry | ||
| Compressive Yield Strength | 475 MPa @Temperature 71.0 °C | 68900 psi @Temperature 160 °F | Wet (14 ± 1/2 days of water immersion at 160 ± 5°F (71 ± 3°C) | ||
| 655 MPa @Temperature 24.0 °C | 95000 psi @Temperature 75.2 °F | Dry | |||
| Shear Strength | 26.2 MPa @Temperature 71.0 °C | 3800 psi @Temperature 160 °F | Short Beam, Wet (14 ± 1/2 days of water immersion at 160 ± 5°F (71 ± 3°C) | ||
| 64.8 MPa @Temperature 24.0 °C | 9400 psi @Temperature 75.2 °F | Short Beam, Dry | |||
| Descriptive Properties | |||||
| Dry Resin Content (%) | 37-41 | Prepreg | |||
| Fiber Volume (%) | 0.028 | Laminate | |||
| Flow (%) | 11-23 | ||||
| Wet Resin Content (%) | 52 | Laminate | |||