- 拉伸强度 [MPa]: 1353.0
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Tensile Strength, Yield | 1353 MPa @Temperature 24.0 °C | 196200 psi @Temperature 75.2 °F | |||
| Tensile Modulus | 131.8 GPa @Temperature 24.0 °C | 19120 ksi @Temperature 75.2 °F | |||
| Compressive Yield Strength | 1185 MPa @Temperature 71.0 °C | 171900 psi @Temperature 160 °F | |||
| 1212 MPa @Temperature 24.0 °C | 175800 psi @Temperature 75.2 °F | ||||
| Shear Strength | 76.0 MPa @Temperature 132 °C | 11000 psi @Temperature 270 °F | Short Beam | ||
| 110 MPa @Temperature 24.0 °C | 16000 psi @Temperature 75.2 °F | Short Beam | |||
| 122 MPa @Temperature -54.0 °C | 17700 psi @Temperature -65.2 °F | Short Beam | |||
| Descriptive Properties | |||||
| Cured Thickness per Ply (cm) | 0.02 | Laminate | |||
| Dry Resin Content (%) | 35-39 | Prepreg | |||
| Fiber Volume (%) | 55 | Laminate | |||
| Flow (%) | 11-24 | ||||