- 拉伸强度 [MPa]: 46.0
- 断裂伸长率 [%]: 906
- 弯曲模量 [MPa]: 191
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 46.0 MPa @Temperature 90.0 °C | 6670 psi @Temperature 194 °F | 90º, Conditioning: 23°C; ASTM D3039 |
| 50.0 MPa @Temperature 23.0 °C | 7250 psi @Temperature 73.4 °F | 90º, Conditioning: 23°C; ASTM D3039 | |
| 1823 MPa @Temperature 23.0 °C | 264400 psi @Temperature 73.4 °F | 0º, Conditioning: 23°C; ASTM D3039 | |
| Tensile Modulus | 5.30 GPa @Temperature 90.0 °C | 769 ksi @Temperature 194 °F | 90º, Conditioning: 23°C; ASTM D3039 |
| 7.60 GPa @Temperature 23.0 °C | 1100 ksi @Temperature 73.4 °F | 90º, Conditioning: 23°C; ASTM D3039 | |
| 213 GPa @Temperature 23.0 °C | 30900 ksi @Temperature 73.4 °F | 0º, Conditioning: 23°C; ASTM D3039 | |
| Flexural Yield Strength | 906 MPa @Temperature 90.0 °C | 131000 psi @Temperature 194 °F | 0º, Conditioning: 23°C; ASTM D790 |
| 1120 MPa @Temperature 23.0 °C | 162000 psi @Temperature 73.4 °F | 0º, Conditioning: 23°C; ASTM D790 | |
| Flexural Modulus | 191 GPa @Temperature 90.0 °C | 27700 ksi @Temperature 194 °F | 0º, Conditioning: 23°C; ASTM D790 |
| 199 GPa @Temperature 23.0 °C | 28900 ksi @Temperature 73.4 °F | 0º, Conditioning: 23°C; ASTM D790 | |
| Compressive Yield Strength | 196 MPa | 28400 psi | Compression After Impact @ 6.67 J/mm |
| 965 MPa @Temperature 23.0 °C | 140000 psi @Temperature 73.4 °F | 0º, 120°C Cure, Conditioning: 23°C; ASTM D965 | |
| 1052 MPa @Temperature 23.0 °C | 152600 psi @Temperature 73.4 °F | 0º, Conditioning: 23°C; ASTM D965 | |
| Shear Strength | 46.0 MPa @Temperature 60.0 °C | 6670 psi @Temperature 140 °F | 0º Interlaminar Shear, Conditioning: 60°C-90%RH; ASTM D2344 |
| 54.0 MPa @Temperature 90.0 °C | 7830 psi @Temperature 194 °F | 0º Interlaminar Shear, Conditioning: 23°C; ASTM D2344 | |
| 58.0 MPa @Temperature 90.0 °C | 8410 psi @Temperature 194 °F | 0º Interlaminar Shear, 120°C Cure, Conditioning: 23°C; ASTM D2344 | |
| 80.0 MPa @Temperature 23.0 °C | 11600 psi @Temperature 73.4 °F | 0º Interlaminar Shear, 120°C Cure, Conditioning: 23°C; ASTM D2344 | |
| 81.0 MPa @Temperature 23.0 °C | 11700 psi @Temperature 73.4 °F | 0º Interlaminar Shear, Conditioning: 23°C; ASTM D2344 | |
| Processing Properties | Metric | English | Comments |
| Shelf Life | 12.0 Month @Temperature -18.0 °C | 12.0 Month @Temperature -0.400 °F | |