- 拉伸强度 [MPa]: 490.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.60 - 1.70 g/cc @Thickness 1.57 mm | 1.60 - 1.70 g/cc @Thickness 0.0620 in | ASTM D792 | ||
| Moisture Absorption at Equilibrium | 0.10 % @Thickness 1.57 mm | 0.10 % @Thickness 0.0620 in | ASTM D229 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 95 - 115 @Thickness 1.57 mm | 95 - 115 @Thickness 0.0620 in | ASTM D785 | ||
| Tensile Strength, Yield | 490 MPa @Thickness 1.57 mm | 71000 psi @Thickness 0.0620 in | CW; ASTM D638 | ||
| 496 MPa @Thickness 1.57 mm | 72000 psi @Thickness 0.0620 in | LW; ASTM D638 | |||
| Modulus of Elasticity | 36.5 GPa @Thickness 1.57 mm | 5300 ksi @Thickness 0.0620 in | CW; ASTM D229 | ||
| 41.4 GPa @Thickness 1.57 mm | 6000 ksi @Thickness 0.0620 in | LW; ASTM D229 | |||
| Flexural Strength | 676 MPa @Thickness 1.57 mm | 98000 psi @Thickness 0.0620 in | CW; ASTM D790 | ||
| 679 MPa @Thickness 1.57 mm | 98500 psi @Thickness 0.0620 in | LW; ASTM D790 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 4.00 µm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C | 2.22 µin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F | x-axis; IPC-TM 650-2.4.24 | ||
| CTE, linear, Transverse to Flow | 8.00 µm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C | 4.44 µin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F | x-axis; IPC-TM 650-2.4.24 | ||
| Maximum Service Temperature, Air | 177 °C | 351 °F | |||
| Glass Transition Temp, Tg | 125 °C | 257 °F | Tg | ||
| Flammability, UL94 | HB @Thickness 1.57 mm | HB @Thickness 0.0620 in | |||
| Descriptive Properties | |||||
| Bond Strength | 1200 lb | 0.5", ASTM D229 | |||
| Color | Black | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.
Users of our Advanced Search (registration required) may exclude discontinued materials from search results.