- 弯曲模量 [MPa]: 48.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Oxidative Stability | 125 hour @Pressure 1.03 MPa, Temperature 210 °C | 125 hour @Pressure 150 psi, Temperature 410 °F | 0.02% wt loss | ||
| 125 hour @Pressure 1.03 MPa, Temperature 260 °C | 125 hour @Pressure 150 psi, Temperature 500 °F | 0.05% wt loss | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 822.5 MPa @Temperature 210 °C | 119300 psi @Temperature 410 °F | Wet, 90° Direction, Ultimate; SACMA SRM 4R-94 | ||
| 856.3 MPa @Temperature 177 °C | 124200 psi @Temperature 350 °F | Wet, 0° Direction, Ultimate; SACMA SRM 4R-94 | |||
| 856.3 MPa @Temperature 19.4 °C | 124200 psi @Temperature 67.0 °F | CTD, 90° Direction, Ultimate; SACMA SRM 4R-94 | |||
| 858.4 MPa @Temperature 210 °C | 124500 psi @Temperature 410 °F | Wet, 0° Direction, Ultimate; SACMA SRM 4R-94 | |||
| 876 MPa @Temperature 177 °C | 127000 psi @Temperature 350 °F | Wet, 90° Direction, Ultimate; SACMA SRM 4R-94 | |||
| 906.0 MPa @Temperature 177 °C | 131400 psi @Temperature 350 °F | Dry, 0° Direction, Ultimate; SACMA SRM 4R-94 | |||
| 956.3 MPa @Temperature 21.1 °C | 138700 psi @Temperature 70.0 °F | Dry, 0° Direction, Ultimate; SACMA SRM 4R-94 | |||
| 957.7 MPa @Temperature 21.1 °C | 138900 psi @Temperature 70.0 °F | Wet, 0° Direction, Ultimate; SACMA SRM 4R-94 | |||
| 986.6 MPa @Temperature 21.1 °C | 143100 psi @Temperature 70.0 °F | Dry, 90° Direction, Ultimate; SACMA SRM 4R-94 | |||
| 1003 MPa @Temperature 19.4 °C | 145500 psi @Temperature 67.0 °F | CTD, 0° Direction, Ultimate; SACMA SRM 4R-94 | |||
| 1009 MPa @Temperature 21.1 °C | 146400 psi @Temperature 70.0 °F | Wet, 90° Direction, Ultimate; SACMA SRM 4R-94 | |||
| Tensile Modulus | 62.1 GPa @Temperature 177 °C | 9000 ksi @Temperature 350 °F | Wet, 0° Direction; SACMA SRM 4R-94 | ||
| 62.1 GPa @Temperature 21.1 °C | 9000 ksi @Temperature 70.0 °F | Wet, 90° Direction; SACMA SRM 4R-94 | |||
| 62.1 GPa @Temperature 177 °C | 9000 ksi @Temperature 350 °F | Wet, 90° Direction; SACMA SRM 4R-94 | |||
| 62.1 GPa @Temperature 210 °C | 9000 ksi @Temperature 410 °F | Wet, 90° Direction; SACMA SRM 4R-94 | |||
| 62.7 GPa @Temperature 210 °C | 9100 ksi @Temperature 410 °F | Wet, 0° Direction; SACMA SRM 4R-94 | |||
| 63.4 GPa @Temperature 21.1 °C | 9200 ksi @Temperature 70.0 °F | Dry, 90° Direction; SACMA SRM 4R-94 | |||
| 64.8 GPa @Temperature 19.4 °C | 9400 ksi @Temperature 67.0 °F | CTD, 90° Direction; SACMA SRM 4R-94 | |||
| 66.2 GPa @Temperature 19.4 °C | 9600 ksi @Temperature 67.0 °F | CTD, 0° Direction; SACMA SRM 4R-94 | |||
| 71.0 GPa @Temperature 177 °C | 10300 ksi @Temperature 350 °F | Dry, 0° Direction; SACMA SRM 4R-94 | |||
| 71.7 GPa @Temperature 21.1 °C | 10400 ksi @Temperature 70.0 °F | Dry, 0° Direction; SACMA SRM 4R-94 | |||
| 72.4 GPa @Temperature 21.1 °C | 10500 ksi @Temperature 70.0 °F | Wet, 0° Direction; SACMA SRM 4R-94 | |||
| Flexural Strength | 896 MPa | 130000 psi | RT, Dry; ASTM D790 | ||
| Flexural Modulus | 48.3 GPa | 7000 ksi | RT, Dry; ASTM D790 | ||
| Compressive Modulus | 55.8 GPa @Temperature 21.1 °C | 8100 ksi @Temperature 70.0 °F | Dry, 90° Direction; ASTM D6641 | ||
| 55.8 GPa @Temperature 21.1 °C | 8100 ksi @Temperature 70.0 °F | Wet, 90° Direction; ASTM D6641 | |||
| 56.5 GPa @Temperature 19.4 °C | 8200 ksi @Temperature 67.0 °F | CTD, 90° Direction; ASTM D6641 | |||
| 57.9 GPa @Temperature 177 °C | 8400 ksi @Temperature 350 °F | Dry, 0° Direction; ASTM D6641 | |||
| 57.9 GPa @Temperature 21.1 °C | 8400 ksi @Temperature 70.0 °F | Dry, 0° Direction; ASTM D6641 | |||
| 58.6 GPa @Temperature 21.1 °C | 8500 ksi @Temperature 70.0 °F | Wet, 0° Direction; ASTM D6641 | |||
| 58.6 GPa @Temperature 19.4 °C | 8500 ksi @Temperature 67.0 °F | CTD, 0° Direction; ASTM D6641 | |||
| 58.6 GPa @Temperature 177 °C | 8500 ksi @Temperature 350 °F | Wet, 90° Direction; ASTM D6641 | |||
| 58.6 GPa @Temperature 210 °C | 8500 ksi @Temperature 410 °F | Wet, 90° Direction; ASTM D6641 | |||
| 58.6 GPa @Temperature 177 °C | 8500 ksi @Temperature 350 °F | Wet, 0° Direction; ASTM D6641 | |||
| 59.3 GPa @Temperature 210 °C | 8600 ksi @Temperature 410 °F | Wet, 0° Direction; ASTM D6641 | |||
| Shear Strength | 37.9 MPa @Temperature 210 °C | 5500 psi @Temperature 410 °F | Inter-laminar, Wet; SACMA SRM 7R-94 | ||
| 46.9 MPa @Temperature 177 °C | 6800 psi @Temperature 350 °F | Inter-laminar, Wet; SACMA SRM 7R-94 | |||
| 51.0 MPa @Temperature 177 °C | 7400 psi @Temperature 350 °F | Inter-laminar, Dry; SACMA SRM 7R-94 | |||
| 68.9 MPa @Temperature 210 °C | 10000 psi @Temperature 410 °F | In-plane, Wet; SACMA SRM 7R-94 | |||
| 69.6 MPa @Temperature 21.1 °C | 10100 psi @Temperature 70.0 °F | Inter-laminar, Dry; SACMA SRM 7R-94 | |||
| 73.1 MPa @Temperature 19.4 °C | 10600 psi @Temperature 67.0 °F | Inter-laminar, CTD; SACMA SRM 7R-94 | |||
| 75.2 MPa @Temperature 21.1 °C | 10900 psi @Temperature 70.0 °F | Inter-laminar, Wet; SACMA SRM 7R-94 | |||
| 75.8 MPa @Temperature 177 °C | 11000 psi @Temperature 350 °F | In-plane, Wet; SACMA SRM 7R-94 | |||
| 81.4 MPa @Temperature 177 °C | 11800 psi @Temperature 350 °F | In-plane, Dry; SACMA SRM 7R-94 | |||
| 92.4 MPa @Temperature 19.4 °C | 13400 psi @Temperature 67.0 °F | In-plane, CTD; SACMA SRM 7R-94 | |||
| 93.8 MPa @Temperature 21.1 °C | 13600 psi @Temperature 70.0 °F | In-plane, Dry; SACMA SRM 7R-94 | |||
| 98.6 MPa @Temperature 21.1 °C | 14300 psi @Temperature 70.0 °F | In-plane, Wet; SACMA SRM 7R-94 | |||
| Thermal Properties | Metric | English | Comments | ||
| Glass Transition Temp, Tg | 247 °C | 477 °F | Wet, Storage Modulus | ||
| 316 °C | 600 °F | Dry, Storage Modulus | |||
| Descriptive Properties | |||||
| Compressive Strain | 10,339 µe | Dry, RT, 90° Direction, Ultimate | |||
| 10,377 µe | CTD, 67°F, 90° Direction, Ultimate | ||||
| 10,400 µe | Wet, RT, 90° Direction, Ultimate | ||||
| 11,249 µe | CTD, 67°F, 0° Direction, Ultimate | ||||
| 11,301 µe | Dry, RT, 0° Direction, Ultimate | ||||
| 5,367 µe | Wet, 410°F, 90° Direction, Ultimate | ||||
| 5,731 µe | Wet, 410°F, 0° Direction, Ultimate | ||||
| 7,200 µe | Wet, 350°F, 90° Direction, Ultimate | ||||
| 7,859 µe | Dry, 350°F, 0° Direction, Ultimate | ||||
| 7,969 µe | Wet, 350°F, 0° Direction, Ultimate | ||||
| 9,943 µe | Wet, RT, 0° Direction, Ultimate | ||||
| Compressive Stress | 45.7 ksi | Wet, 410°F, 90° Direction, Ultimate | |||
| Compressive Stress | 49.5 ksi | Wet, 410°F, 0° Direction, Ultimate | |||
| Compressive Stress | 61.2 ksi | Wet, 350°F, 90° Direction, Ultimate | |||
| Compressive Stress | 66.2 ksi | Dry, 350°F, 0° Direction, Ultimate | |||
| 67.9 ksi | Wet, 350°F, 0° Direction, Ultimate | ||||
| Compressive Stress | 84.4 ksi | Dry, RT, 90° Direction, Ultimate | |||
| 85.1 ksi | Wet, RT, 90° Direction, Ultimate | ||||
| 85.3 ksi | CTD, 67°F, 90° Direction, Ultimate | ||||
| Compressive Stress | 85.5 ksi | Wet, 70°F, 0° Direction, Ultimate | |||
| 95.7 ksi | Dry, 70°F, 0° Direction, Ultimate | ||||
| 96.5 ksi | CTD, 67°F, 0° Direction, Ultimate | ||||
| Tensile Strain | 12,782 µe | Dry, 350°F, 0° Direction, Ultimate | |||
| 13,105 µe | CTD, 67°F, 90° Direction, Ultimate | ||||
| 13,201 µe | Wet, 410°F, 90° Direction, Ultimate | ||||
| 13,212 µe | Wet, RT, 0° Direction, Ultimate | ||||
| 13,274 µe | Dry, RT, 0° Direction, Ultimate | ||||
| 13,565 µe | Wet, 410°F, 0° Direction, Ultimate | ||||
| 13,786 µe | Wet, 350°F, 0° Direction, Ultimate | ||||
| 13,996 µe | Wet, 350°F, 90° Direction, Ultimate | ||||
| 15,135 µe | CTD, 67°F, 0° Direction | ||||
| 15,495 µe | Dry, RT, 90° Direction, Ultimate | ||||
| 16,184 µe | Wet, RT, 90° Direction, Ultimate | ||||