- 断裂伸长率 [%]: 550
- 弯曲强度 [MPa]: 2700.0
- 弯曲模量 [MPa]: 70.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 2700 MPa | 392000 psi | Vf=59% |
| Tensile Modulus | 140 GPa | 20300 ksi | Vf=59% |
| Flexural Yield Strength | 550 MPa | 79800 psi | Vf=58% |
| Flexural Modulus | 70.0 GPa | 10200 ksi | Vf=58% |
| Poissons Ratio | 0.30 | 0.30 | Vf=59% |
| Shear Strength | 70.0 MPa | 10200 psi | Interlaminar shear strength; Vf=54%; L/d = 4. |
| Impact Test | 18.0 J | 13.3 ft-lb | Absorbed energy with 3.5 kN maximum load. 12.7 mm hemisphere insert; 38.1 mm circle support; 5.51 kg weight; 4.47 m/s impact velocity. |