- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.54
- 吸水率 [%]: 0.04
- 缺口冲击强度: 0.5
- 拉伸强度 [MPa]: 80.0
- 断裂伸长率 [%]: 121
- 弯曲强度 [MPa]: 72.4
- 弯曲模量 [MPa]: 1.08
- 硬度: 115.0
- 热变形温度 [℃]: 204.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 - 1.76 g/cc | 0.0556 - 0.0636 lb/in³ | Average value: 1.63 g/cc Grade Count:35 |
| Filler Content | 35.0 - 43.0 % | 35.0 - 43.0 % | Average value: 39.0 % Grade Count:12 |
| Water Absorption | 0.0400 - 0.250 % | 0.0400 - 0.250 % | Average value: 0.0890 % Grade Count:10 |
| Moisture Absorption at Equilibrium | 0.0300 - 0.150 % | 0.0300 - 0.150 % | Average value: 0.108 % Grade Count:6 |
| Linear Mold Shrinkage | 0.00100 - 0.0130 cm/cm | 0.00100 - 0.0130 in/in | Average value: 0.00364 cm/cm Grade Count:26 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00300 cm/cm | 0.00300 in/in | Average value: 0.00300 cm/cm Grade Count:4 |
| Linear Mold Shrinkage, Transverse | 0.00300 - 0.00900 cm/cm | 0.00300 - 0.00900 in/in | Average value: 0.00669 cm/cm Grade Count:7 |
| Melt Flow | 2.00 - 15.0 g/10 min | 2.00 - 15.0 g/10 min | Average value: 7.25 g/10 min Grade Count:8 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 93.0 - 95.0 | 93.0 - 95.0 | Average value: 93.7 Grade Count:3 |
| Hardness, Rockwell R | 115 - 120 | 115 - 120 | Average value: 119 Grade Count:6 |
| Tensile Strength, Ultimate | 72.4 - 180 MPa | 10500 - 26100 psi | Average value: 136 MPa Grade Count:27 |
| Tensile Strength, Yield | 80.0 - 152 MPa | 11600 - 22000 psi | Average value: 121 MPa Grade Count:7 |
| Elongation at Break | 1.00 - 7.00 % | 1.00 - 7.00 % | Average value: 2.66 % Grade Count:30 |
| Modulus of Elasticity | 8.27 - 16.8 GPa | 1200 - 2440 ksi | Average value: 12.2 GPa Grade Count:22 |
| Flexural Yield Strength | 121 - 270 MPa | 17500 - 39200 psi | Average value: 202 MPa Grade Count:30 |
| Flexural Modulus | 1.08 - 13.4 GPa | 156 - 1940 ksi | Average value: 9.97 GPa Grade Count:32 |
| Izod Impact, Notched | 0.500 - 6.99 J/cm | 0.937 - 13.1 ft-lb/in | Average value: 1.25 J/cm Grade Count:25 |
| Izod Impact, Unnotched | 6.41 - 10.1 J/cm | 12.0 - 19.0 ft-lb/in | Average value: 7.53 J/cm Grade Count:10 |
| Izod Impact, Notched (ISO) | 8.00 - 16.0 kJ/m² | 3.81 - 7.61 ft-lb/in² | Average value: 10.8 kJ/m² Grade Count:6 |
| 9.00 - 9.00 kJ/m² @Temperature -30.0 - -30.0 °C | 4.28 - 4.28 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 9.00 kJ/m² Grade Count:1 | |
| Charpy Impact Unnotched | 4.70 - 7.00 J/cm² | 22.4 - 33.3 ft-lb/in² | Average value: 6.18 J/cm² Grade Count:4 |
| 4.50 - 6.50 J/cm² @Temperature -30.0 - -20.0 °C | 21.4 - 30.9 ft-lb/in² @Temperature -22.0 - -4.00 °F | Average value: 6.00 J/cm² Grade Count:4 | |
| Charpy Impact, Notched | 0.790 - 3.50 J/cm² | 3.76 - 16.7 ft-lb/in² | Average value: 1.59 J/cm² Grade Count:9 |
| 0.950 - 1.30 J/cm² @Temperature -30.0 - -20.0 °C | 4.52 - 6.19 ft-lb/in² @Temperature -22.0 - -4.00 °F | Average value: 1.09 J/cm² Grade Count:4 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+13 - 3.00e+16 ohm-cm | 1.00e+13 - 3.00e+16 ohm-cm | Average value: 8.40e+15 ohm-cm Grade Count:14 |
| Surface Resistance | 1.00e+13 - 2.00e+16 ohm | 1.00e+13 - 2.00e+16 ohm | Average value: 2.80e+15 ohm Grade Count:9 |
| Dielectric Constant | 3.40 - 4.10 | 3.40 - 4.10 | Average value: 3.73 Grade Count:5 |
| Dielectric Strength | 18.9 - 50.0 kV/mm | 480 - 1270 kV/in | Average value: 26.1 kV/mm Grade Count:12 |
| Dissipation Factor | 0.00100 - 0.0150 | 0.00100 - 0.0150 | Average value: 0.00660 Grade Count:4 |
| Arc Resistance | 90.0 - 127 sec | 90.0 - 127 sec | Average value: 112 sec Grade Count:3 |
| Comparative Tracking Index | 350 - 599 V | 350 - 599 V | Average value: 475 V Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 15.0 - 40.0 µm/m-°C | 8.33 - 22.2 µin/in-°F | Average value: 22.8 µm/m-°C Grade Count:8 |
| CTE, linear, Transverse to Flow | 70.0 - 101 µm/m-°C | 38.9 - 56.1 µin/in-°F | Average value: 86.0 µm/m-°C Grade Count:3 |
| Melting Point | 200 - 225 °C | 392 - 437 °F | Average value: 223 °C Grade Count:11 |
| Deflection Temperature at 0.46 MPa (66 psi) | 204 - 226 °C | 400 - 439 °F | Average value: 218 °C Grade Count:22 |
| Deflection Temperature at 1.8 MPa (264 psi) | 188 - 225 °C | 370 - 437 °F | Average value: 209 °C Grade Count:33 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:26 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 270 °C | 68.0 - 518 °F | Average value: 173 °C Grade Count:11 |
| Feed Temperature | 20.0 - 240 °C | 68.0 - 464 °F | Average value: 141 °C Grade Count:4 |
| Nozzle Temperature | 240 - 270 °C | 464 - 518 °F | Average value: 255 °C Grade Count:4 |
| Melt Temperature | 230 - 300 °C | 446 - 572 °F | Average value: 251 °C Grade Count:16 |
| Mold Temperature | 40.0 - 121 °C | 104 - 250 °F | Average value: 85.5 °C Grade Count:21 |
| Drying Temperature | 116 - 140 °C | 240 - 284 °F | Average value: 121 °C Grade Count:13 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.56 hour Grade Count:15 |
| Moisture Content | 0.0200 - 0.0800 % | 0.0200 - 0.0800 % | Average value: 0.0367 % Grade Count:9 |
| Dew Point | -30.0 - -28.9 °C | -22.0 - -20.0 °F | Average value: -29.1 °C Grade Count:5 |
| Injection Pressure | 39.2 - 124 MPa | 5690 - 18000 psi | Average value: 84.5 MPa Grade Count:15 |
| Hold Pressure | 30.0 - 80.0 MPa | 4350 - 11600 psi | Average value: 54.3 MPa Grade Count:3 |
| Back Pressure | 0.000 - 3.92 MPa | 0.000 - 569 psi | Average value: 1.06 MPa Grade Count:4 |
| Screw Speed | 40.0 - 120 rpm | 40.0 - 120 rpm | Average value: 68.3 rpm Grade Count:3 |