- 密度 [g/cm3]: 1.46
- 吸水率 [%]: 0.07
- 缺口冲击强度: 0.53
- 拉伸强度 [MPa]: 113.0
- 断裂伸长率 [%]: 83.0
- 弯曲强度 [MPa]: 57.0
- 弯曲模量 [MPa]: 3.40
- 热变形温度 [℃]: 182.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 - 1.76 g/cc | 0.0527 - 0.0636 lb/in³ | Average value: 1.62 g/cc Grade Count:20 |
| Filler Content | 10.0 - 30.0 % | 10.0 - 30.0 % | Average value: 17.5 % Grade Count:4 |
| Water Absorption | 0.0700 - 1.16 % | 0.0700 - 1.16 % | Average value: 0.200 % Grade Count:10 |
| Linear Mold Shrinkage | 0.00200 - 0.0120 cm/cm | 0.00200 - 0.0120 in/in | Average value: 0.00464 cm/cm Grade Count:18 |
| Linear Mold Shrinkage, Transverse | 0.0100 - 0.0110 cm/cm | 0.0100 - 0.0110 in/in | Average value: 0.0103 cm/cm Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 57.0 - 145 MPa | 8270 - 21000 psi | Average value: 103 MPa Grade Count:21 |
| Tensile Strength, Yield | 113 - 117 MPa | 16400 - 17000 psi | Average value: 116 MPa Grade Count:3 |
| Elongation at Break | 2.00 - 6.00 % | 2.00 - 6.00 % | Average value: 3.22 % Grade Count:12 |
| Elongation at Yield | 1.70 - 3.50 % | 1.70 - 3.50 % | Average value: 2.75 % Grade Count:10 |
| Modulus of Elasticity | 4.10 - 13.1 GPa | 595 - 1900 ksi | Average value: 8.72 GPa Grade Count:17 |
| Flexural Yield Strength | 83.0 - 207 MPa | 12000 - 30000 psi | Average value: 157 MPa Grade Count:20 |
| Flexural Modulus | 3.40 - 11.7 GPa | 493 - 1700 ksi | Average value: 7.85 GPa Grade Count:21 |
| Izod Impact, Notched | 0.530 - 1.12 J/cm | 0.993 - 2.10 ft-lb/in | Average value: 0.792 J/cm Grade Count:13 |
| Izod Impact, Unnotched | 3.74 - 8.54 J/cm | 7.00 - 16.0 ft-lb/in | Average value: 6.53 J/cm Grade Count:10 |
| Izod Impact, Notched (ISO) | 6.00 - 9.20 kJ/m² | 2.86 - 4.38 ft-lb/in² | Average value: 8.40 kJ/m² Grade Count:4 |
| Izod Impact, Unnotched (ISO) | 30.0 - 43.7 kJ/m² | 14.3 - 20.8 ft-lb/in² | Average value: 39.7 kJ/m² Grade Count:4 |
| Charpy Impact Unnotched | 2.80 - 5.00 J/cm² | 13.3 - 23.8 ft-lb/in² | Average value: 4.33 J/cm² Grade Count:7 |
| 5.70 - 5.70 J/cm² @Temperature -30.0 - -30.0 °C | 27.1 - 27.1 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 5.70 J/cm² Grade Count:3 | |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | Average value: 1.50 J/cm² Grade Count:3 |
| 1.50 - 1.50 J/cm² @Temperature -30.0 - -30.0 °C | 7.14 - 7.14 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 1.50 J/cm² Grade Count:3 | |
| Falling Dart Impact | 8.70 - 13.7 J | 6.42 - 10.1 ft-lb | Average value: 12.0 J Grade Count:3 |
| Coefficient of Friction | 0.120 - 0.570 | 0.120 - 0.570 | Average value: 0.253 Grade Count:10 |
| Coefficient of Friction, Static | 0.110 - 0.410 | 0.110 - 0.410 | Average value: 0.201 Grade Count:10 |
| K (wear) Factor | 40.3 - 242 x 10-8 mm³/N-M | 20.0 - 120 x 10-10 in³-min/ft-lb-hr | Average value: 109 x 10-8 mm³/N-M Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 - 1.00e+16 ohm-cm | 1.00e+14 - 1.00e+16 ohm-cm | Average value: 8.35e+15 ohm-cm Grade Count:3 |
| Insulation Resistance | 1.00e+12 ohm | 1.00e+12 ohm | Average value: 1.00e+12 ohm Grade Count:7 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 23.0 - 67.0 µm/m-°C | 12.8 - 37.2 µin/in-°F | Average value: 33.6 µm/m-°C Grade Count:7 |
| CTE, linear, Transverse to Flow | 67.0 - 136 µm/m-°C | 37.2 - 75.6 µin/in-°F | Average value: 90.0 µm/m-°C Grade Count:3 |
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | Average value: 0.400 W/m-K Grade Count:3 |
| Maximum Service Temperature, Air | 130 - 180 °C | 266 - 356 °F | Average value: 155 °C Grade Count:7 |
| Deflection Temperature at 0.46 MPa (66 psi) | 182 - 224 °C | 360 - 435 °F | Average value: 206 °C Grade Count:4 |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.4 - 218 °C | 175 - 424 °F | Average value: 190 °C Grade Count:15 |
| Vicat Softening Point | 210 - 215 °C | 410 - 419 °F | Average value: 212 °C Grade Count:5 |
| Flammability, UL94 | HB | HB | Grade Count:7 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 232 - 257 °C | 450 - 495 °F | Average value: 249 °C Grade Count:9 |
| Nozzle Temperature | 250 - 265 °C | 482 - 509 °F | Average value: 258 °C Grade Count:7 |
| Melt Temperature | 232 - 280 °C | 450 - 536 °F | Average value: 258 °C Grade Count:17 |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | Average value: 89.1 °C Grade Count:19 |
| Drying Temperature | 80.0 - 130 °C | 176 - 266 °F | Average value: 108 °C Grade Count:15 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.83 hour Grade Count:6 |
| Moisture Content | 0.0300 - 0.150 % | 0.0300 - 0.150 % | Average value: 0.0814 % Grade Count:7 |
| Dew Point | -28.9 °C | -20.0 °F | Average value: -28.9 °C Grade Count:4 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:6 |
| Back Pressure | 0.172 - 0.345 MPa | 24.9 - 50.0 psi | Average value: 0.259 MPa Grade Count:3 |