- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.11
- 吸水率 [%]: 0.06
- 缺口冲击强度: 0.267
- 拉伸强度 [MPa]: 49.0
- 断裂伸长率 [%]: 75.0
- 弯曲强度 [MPa]: 11.1
- 弯曲模量 [MPa]: 0.373
- 硬度: 117.0
- 热变形温度 [℃]: 113.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 - 1.55 g/cc | 0.0401 - 0.0560 lb/in³ | Average value: 1.40 g/cc Grade Count:82 |
| Filler Content | 5.00 - 15.0 % | 5.00 - 15.0 % | Average value: 10.0 % Grade Count:15 |
| Water Absorption | 0.0600 - 0.500 % | 0.0600 - 0.500 % | Average value: 0.259 % Grade Count:23 |
| Moisture Absorption at Equilibrium | 0.0400 - 0.220 % | 0.0400 - 0.220 % | Average value: 0.154 % Grade Count:27 |
| Viscosity | 48000 - 514000 cP @Temperature 240 - 260 °C | 48000 - 514000 cP @Temperature 464 - 500 °F | Average value: 174000 cP Grade Count:1 |
| 48000 - 514000 cP @Shear Rate 100 - 10000 1/s | 48000 - 514000 cP @Shear Rate 100 - 10000 1/s | Average value: 174000 cP Grade Count:1 | |
| Viscosity Measurement | 70.0 - 120 @Temperature 240 - 300 °C | 70.0 - 120 @Temperature 464 - 572 °F | Average value: 99.5 Grade Count:1 |
| Viscosity Test | 80.0 - 145 cm³/g | 80.0 - 145 cm³/g | Average value: 110 cm³/g Grade Count:6 |
| Maximum Moisture Content | 0.0200 | 0.0200 | Average value: 0.0200 Grade Count:6 |
| Linear Mold Shrinkage | 0.00100 - 0.0200 cm/cm | 0.00100 - 0.0200 in/in | Average value: 0.00803 cm/cm Grade Count:70 |
| Linear Mold Shrinkage, Transverse | 0.00100 - 0.0160 cm/cm | 0.00100 - 0.0160 in/in | Average value: 0.00979 cm/cm Grade Count:31 |
| Melt Flow | 4.00 - 60.0 g/10 min | 4.00 - 60.0 g/10 min | Average value: 24.0 g/10 min Grade Count:37 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 83.0 - 120 | 83.0 - 120 | Average value: 98.2 Grade Count:6 |
| Hardness, Rockwell R | 117 - 119 | 117 - 119 | Average value: 118 Grade Count:7 |
| Ball Indentation Hardness | 160 - 170 MPa | 23200 - 24700 psi | Average value: 163 MPa Grade Count:3 |
| Tensile Strength, Ultimate | 11.1 - 110 MPa | 1610 - 16000 psi | Average value: 73.0 MPa Grade Count:59 |
| 50.0 - 130 MPa @Temperature -20.0 - 100 °C | 7250 - 18900 psi @Temperature -4.00 - 212 °F | Average value: 39.1 MPa Grade Count:1 | |
| 3.06 - 125 MPa @Temperature -40.0 - 160 °C | 444 - 18100 psi @Temperature -40.0 - 320 °F | Average value: 39.1 MPa Grade Count:3 | |
| 3.06 - 125 MPa @Strain 0.250 - 10.0 % | 444 - 18100 psi @Strain 0.250 - 10.0 % | Average value: 39.1 MPa Grade Count:3 | |
| Tensile Strength, Yield | 49.0 - 100 MPa | 7100 - 14500 psi | Average value: 77.3 MPa Grade Count:27 |
| Elongation at Break | 2.50 - 100 % | 2.50 - 100 % | Average value: 7.68 % Grade Count:69 |
| Elongation at Yield | 3.50 - 4.00 % | 3.50 - 4.00 % | Average value: 3.80 % Grade Count:4 |
| Modulus of Elasticity | 2.80 - 6.20 GPa | 406 - 899 ksi | Average value: 4.56 GPa Grade Count:52 |
| Flexural Yield Strength | 75.0 - 165 MPa | 10900 - 23900 psi | Average value: 122 MPa Grade Count:60 |
| 50.0 - 50.0 MPa @Temperature 90.0 - 90.0 °C | 7250 - 7250 psi @Temperature 194 - 194 °F | Average value: 50.0 MPa Grade Count:1 | |
| Flexural Modulus | 0.373 - 9.00 GPa | 54.0 - 1310 ksi | Average value: 4.07 GPa Grade Count:57 |
| Shear Modulus | 0.219 - 1.77 GPa @Temperature -50.0 - 200 °C | 31.8 - 257 ksi @Temperature -58.0 - 392 °F | Average value: 0.830 GPa Grade Count:2 |
| Izod Impact, Notched | 0.267 - 1.60 J/cm | 0.500 - 3.00 ft-lb/in | Average value: 0.536 J/cm Grade Count:27 |
| 0.48051 - 0.48051 J/cm @Temperature -28.9 - -28.9 °C | 0.90019 - 0.90019 ft-lb/in @Temperature -20.0 - -20.0 °F | Average value: 0.481 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 3.20 - 9.61 J/cm | 6.00 - 18.0 ft-lb/in | Average value: 5.96 J/cm Grade Count:8 |
| Izod Impact, Notched (ISO) | 3.80 - 13.0 kJ/m² | 1.81 - 6.19 ft-lb/in² | Average value: 5.79 kJ/m² Grade Count:18 |
| 3.00 - 5.00 kJ/m² @Temperature -30.0 - -30.0 °C | 1.43 - 2.38 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 4.50 kJ/m² Grade Count:4 | |
| Izod Impact, Unnotched (ISO) | 23.0 - 45.0 kJ/m² | 10.9 - 21.4 ft-lb/in² | Average value: 34.9 kJ/m² Grade Count:13 |
| 26.0 - 40.0 kJ/m² @Temperature -30.0 - -30.0 °C | 12.4 - 19.0 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 31.0 kJ/m² Grade Count:3 | |
| Charpy Impact Unnotched | 2.00 J/cm² - NB | 9.52 ft-lb/in² - NB | Average value: 3.93 J/cm² Grade Count:42 |
| 2.00 - 19.0 J/cm² @Temperature -30.0 - 30.0 °C | 9.52 - 90.4 ft-lb/in² @Temperature -22.0 - 86.0 °F | Average value: 5.00 J/cm² Grade Count:30 | |
| Charpy Impact, Notched | 0.230 - 1.80 J/cm² | 1.09 - 8.57 ft-lb/in² | Average value: 0.704 J/cm² Grade Count:48 |
| 0.210 - 1.00 J/cm² @Temperature -30.0 - 30.0 °C | 0.999 - 4.76 ft-lb/in² @Temperature -22.0 - 86.0 °F | Average value: 0.584 J/cm² Grade Count:30 | |
| Puncture Energy | 1.50 - 1.50 J @Temperature -30.0 - -30.0 °C | 1.11 - 1.11 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 1.50 J Grade Count:1 |
| Tensile Creep Modulus, 1 hour | 0.000 - 5500 MPa | 0.000 - 798000 psi | Average value: 2120 MPa Grade Count:5 |
| 0.000 - 35.0 MPa @Temperature 60.0 - 60.0 °C | 0.000 - 5080 psi @Temperature 140 - 140 °F | Average value: 17.5 MPa Grade Count:2 | |
| 0.000 - 35.0 MPa @Strain 0.000 - 2.38 % | 0.000 - 5080 psi @Strain 0.000 - 2.38 % | Average value: 17.5 MPa Grade Count:2 | |
| Tensile Creep Modulus, 1000 hours | 0.000 - 5000 MPa | 0.000 - 725000 psi | Average value: 514 MPa Grade Count:5 |
| 0.000 - 35.0 MPa @Temperature 60.0 - 60.0 °C | 0.000 - 5080 psi @Temperature 140 - 140 °F | Average value: 17.5 MPa Grade Count:2 | |
| 0.000 - 35.0 MPa @Strain 0.000 - 2.70 % | 0.000 - 5080 psi @Strain 0.000 - 2.70 % | Average value: 17.5 MPa Grade Count:2 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+6 - 1.00e+17 ohm-cm | 1.00e+6 - 1.00e+17 ohm-cm | Average value: 8.62e+15 ohm-cm Grade Count:52 |
| Surface Resistance | 1.00e+6 - 1.00e+17 ohm | 1.00e+6 - 1.00e+17 ohm | Average value: 7.79e+15 ohm Grade Count:36 |
| Dielectric Constant | 3.00 - 4.30 | 3.00 - 4.30 | Average value: 3.55 Grade Count:32 |
| Dielectric Strength | 17.0 - 100 kV/mm | 432 - 2540 kV/in | Average value: 25.9 kV/mm Grade Count:47 |
| Dissipation Factor | 0.00100 - 0.0600 | 0.00100 - 0.0600 | Average value: 0.0118 Grade Count:23 |
| Dielectric Loss Index | 0.00200 - 0.0200 | 0.00200 - 0.0200 | Average value: 0.0170 Grade Count:6 |
| Arc Resistance | 60.0 - 180 sec | 60.0 - 180 sec | Average value: 117 sec Grade Count:14 |
| Comparative Tracking Index | 125 - 600 V | 125 - 600 V | Average value: 286 V Grade Count:39 |
| Hot Wire Ignition, HWI | 7.00 - 60.0 sec | 7.00 - 60.0 sec | Average value: 20.5 sec Grade Count:5 |
| High Amp Arc Ignition, HAI | 0.000 - 120 arcs | 0.000 - 120 arcs | Average value: 75.0 arcs Grade Count:5 |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 150 mm/min | 1.00 - 5.91 in/min | Average value: 104 mm/min Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.400 - 500 µm/m-°C | 0.222 - 278 µin/in-°F | Average value: 112 µm/m-°C Grade Count:28 |
| CTE, linear, Transverse to Flow | 80.0 - 138 µm/m-°C | 44.4 - 76.7 µin/in-°F | Average value: 112 µm/m-°C Grade Count:12 |
| Specific Heat Capacity | 1.60 - 1.97 J/g-°C | 0.382 - 0.471 BTU/lb-°F | Average value: 1.82 J/g-°C Grade Count:5 |
| Thermal Conductivity | 0.131 - 0.230 W/m-K | 0.909 - 1.60 BTU-in/hr-ft²-°F | Average value: 0.171 W/m-K Grade Count:6 |
| Melting Point | 200 - 226 °C | 392 - 439 °F | Average value: 222 °C Grade Count:40 |
| Maximum Service Temperature, Air | 75.0 - 290 °C | 167 - 554 °F | Average value: 188 °C Grade Count:8 |
| Transformation Temperature, Tg | 60.0 °C | 140 °F | Average value: 60.0 °C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 113 - 225 °C | 235 - 437 °F | Average value: 207 °C Grade Count:51 |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.7 - 210 °C | 170 - 410 °F | Average value: 164 °C Grade Count:75 |
| Deflection Temperature at 8.0 MPa | 50.0 - 70.0 °C | 122 - 158 °F | Average value: 57.9 °C Grade Count:8 |
| Vicat Softening Point | 100 - 220 °C | 212 - 428 °F | Average value: 198 °C Grade Count:29 |
| UL RTI, Electrical | 50.0 - 140 °C | 122 - 284 °F | Average value: 121 °C Grade Count:9 |
| UL RTI, Mechanical with Impact | 50.0 - 140 °C | 122 - 284 °F | Average value: 114 °C Grade Count:9 |
| UL RTI, Mechanical without Impact | 50.0 - 140 °C | 122 - 284 °F | Average value: 120 °C Grade Count:9 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:75 |
| Oxygen Index | 19.0 - 34.0 % | 19.0 - 34.0 % | Average value: 25.5 % Grade Count:13 |
| Glow Wire Test | 700 - 960 °C | 1290 - 1760 °F | Average value: 822 °C Grade Count:19 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 270 °C | 68.0 - 518 °F | Average value: 116 °C Grade Count:9 |
| Feed Temperature | 50.0 - 240 °C | 122 - 464 °F | Average value: 199 °C Grade Count:6 |
| Nozzle Temperature | 240 - 271 °C | 464 - 520 °F | Average value: 250 °C Grade Count:19 |
| Die Temperature | 240 - 270 °C | 464 - 518 °F | Average value: 256 °C Grade Count:5 |
| Melt Temperature | 223 - 280 °C | 433 - 536 °F | Average value: 248 °C Grade Count:52 |
| Mold Temperature | 30.0 - 130 °C | 86.0 - 266 °F | Average value: 77.6 °C Grade Count:55 |
| Injection Velocity | 200 - 300 mm/sec | 7.87 - 11.8 in/sec | Average value: 280 mm/sec Grade Count:5 |
| Drying Temperature | 80.0 - 140 °C | 176 - 284 °F | Average value: 119 °C Grade Count:37 |
| Dry Time | 2.00 - 5.00 hour | 2.00 - 5.00 hour | Average value: 3.82 hour Grade Count:37 |
| Moisture Content | 0.0200 - 0.0800 % | 0.0200 - 0.0800 % | Average value: 0.0396 % Grade Count:23 |
| Dew Point | -30.0 - -28.9 °C | -22.0 - -20.0 °F | Average value: -29.1 °C Grade Count:5 |
| Injection Pressure | 40.0 - 120 MPa | 5800 - 17400 psi | Average value: 77.8 MPa Grade Count:21 |
| Hold Pressure | 30.0 - 100 MPa | 4350 - 14500 psi | Average value: 63.4 MPa Grade Count:6 |
| Back Pressure | 0.000 - 15.0 MPa | 0.000 - 2180 psi | Average value: 3.66 MPa Grade Count:14 |
| Screw Speed | 40.0 - 120 rpm | 40.0 - 120 rpm | Average value: 87.0 rpm Grade Count:8 |
| Hot-Working Temperature | 250 - 270 °C | 482 - 518 °F | Average value: 257 °C Grade Count:5 |