- 熔体流动速率 [g/10min]: 9.59
- 密度 [g/cm3]: 1.29
- 缺口冲击强度: 0.21
- 拉伸强度 [MPa]: 40.0
- 断裂伸长率 [%]: 55.0
- 弯曲强度 [MPa]: 30.0
- 弯曲模量 [MPa]: 1.90
- 硬度: 109.0
- 热变形温度 [℃]: 110.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 - 1.81 g/cc | 0.0466 - 0.0654 lb/in³ | Average value: 1.51 g/cc Grade Count:34 |
| Water Absorption | 0.000 - 0.500 % | 0.000 - 0.500 % | Average value: 0.243 % Grade Count:16 |
| Moisture Absorption at Equilibrium | 0.150 - 0.500 % | 0.150 - 0.500 % | Average value: 0.256 % Grade Count:8 |
| Viscosity Measurement | 100 - 139 | 100 - 139 | Average value: 123 Grade Count:4 |
| 1500 - 1500 @Temperature 250 - 250 °C | 1500 - 1500 @Temperature 482 - 482 °F | Average value: 1500 Grade Count:1 | |
| Linear Mold Shrinkage | 0.00100 - 0.0200 cm/cm | 0.00100 - 0.0200 in/in | Average value: 0.0117 cm/cm Grade Count:27 |
| Linear Mold Shrinkage, Transverse | 0.00100 - 0.0190 cm/cm | 0.00100 - 0.0190 in/in | Average value: 0.0127 cm/cm Grade Count:11 |
| Melt Flow | 9.59 - 58.0 g/10 min | 9.59 - 58.0 g/10 min | Average value: 26.5 g/10 min Grade Count:17 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 109 - 122 | 109 - 122 | Average value: 115 Grade Count:8 |
| Tensile Strength, Ultimate | 30.0 - 105 MPa | 4350 - 15200 psi | Average value: 56.8 MPa Grade Count:22 |
| 35.0 - 55.0 MPa @Temperature 60.0 - 120 °C | 5080 - 7980 psi @Temperature 140 - 248 °F | Average value: 43.3 MPa Grade Count:1 | |
| Tensile Strength, Yield | 40.0 - 103 MPa | 5800 - 15000 psi | Average value: 59.2 MPa Grade Count:14 |
| Elongation at Break | 2.00 - 80.0 % | 2.00 - 80.0 % | Average value: 8.64 % Grade Count:32 |
| Elongation at Yield | 3.00 - 7.00 % | 3.00 - 7.00 % | Average value: 4.33 % Grade Count:3 |
| Modulus of Elasticity | 2.20 - 7.20 GPa | 319 - 1040 ksi | Average value: 4.32 GPa Grade Count:20 |
| Flexural Yield Strength | 55.0 - 186 MPa | 7980 - 27000 psi | Average value: 101 MPa Grade Count:26 |
| Flexural Modulus | 1.90 - 9.65 GPa | 276 - 1400 ksi | Average value: 4.79 GPa Grade Count:26 |
| 2.50 - 5.00 GPa @Temperature 60.0 - 120 °C | 363 - 725 ksi @Temperature 140 - 248 °F | Average value: 3.67 GPa Grade Count:1 | |
| Izod Impact, Notched | 0.210 - 1.90 J/cm | 0.393 - 3.56 ft-lb/in | Average value: 0.585 J/cm Grade Count:16 |
| 0.400 - 0.5339 J/cm @Temperature -40.0 - -20.0 °C | 0.749 - 1.000 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.445 J/cm Grade Count:2 | |
| Izod Impact, Unnotched | 2.83 - 11.7 J/cm | 5.30 - 22.0 ft-lb/in | Average value: 5.27 J/cm Grade Count:4 |
| Izod Impact, Notched (ISO) | 5.00 - 15.0 kJ/m² | 2.38 - 7.14 ft-lb/in² | Average value: 10.0 kJ/m² Grade Count:3 |
| 5.00 - 10.0 kJ/m² @Temperature -30.0 - -30.0 °C | 2.38 - 4.76 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 7.50 kJ/m² Grade Count:2 | |
| Izod Impact, Unnotched (ISO) | 25.0 - 40.0 kJ/m² @Temperature -30.0 - -30.0 °C | 11.9 - 19.0 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 32.5 kJ/m² Grade Count:2 |
| Charpy Impact Unnotched | 1.50 - 1000 J/cm² | 7.14 - 4760 ft-lb/in² | Average value: 5.06 J/cm² Grade Count:10 |
| 2.50 - 12.0 J/cm² @Temperature -40.0 - -20.0 °C | 11.9 - 57.1 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 4.81 J/cm² Grade Count:4 | |
| Charpy Impact, Notched | 0.290 - 1.00 J/cm² | 1.38 - 4.76 ft-lb/in² | Average value: 0.471 J/cm² Grade Count:15 |
| 0.200 - 1.00 J/cm² @Temperature -30.0 - -20.0 °C | 0.952 - 4.76 ft-lb/in² @Temperature -22.0 - -4.00 °F | Average value: 0.480 J/cm² Grade Count:5 | |
| Tensile Creep Modulus, 1000 hours | 1200 - 2000 MPa | 174000 - 290000 psi | Average value: 1500 MPa Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 5.00e+14 - 4.00e+16 ohm-cm | 5.00e+14 - 4.00e+16 ohm-cm | Average value: 7.72e+15 ohm-cm Grade Count:14 |
| Surface Resistance | 1.00e+13 - 7.30e+17 ohm | 1.00e+13 - 7.30e+17 ohm | Average value: 8.24e+16 ohm Grade Count:9 |
| Dielectric Constant | 3.00 - 4.10 | 3.00 - 4.10 | Average value: 3.64 Grade Count:11 |
| Dielectric Strength | 14.0 - 100 kV/mm | 356 - 2540 kV/in | Average value: 35.8 kV/mm Grade Count:10 |
| Dissipation Factor | 0.00120 - 0.0320 | 0.00120 - 0.0320 | Average value: 0.0132 Grade Count:7 |
| Comparative Tracking Index | 150 - 425 V | 150 - 425 V | Average value: 251 V Grade Count:15 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 5.00 - 115 µm/m-°C | 2.78 - 63.9 µin/in-°F | Average value: 50.8 µm/m-°C Grade Count:13 |
| 61.0 - 61.0 µm/m-°C @Temperature 60.0 - 138 °C | 33.9 - 33.9 µin/in-°F @Temperature 140 - 280 °F | Average value: 61.0 µm/m-°C Grade Count:1 | |
| CTE, linear, Transverse to Flow | 50.0 - 115 µm/m-°C | 27.8 - 63.9 µin/in-°F | Average value: 85.6 µm/m-°C Grade Count:8 |
| 88.0 - 88.0 µm/m-°C @Temperature 60.0 - 138 °C | 48.9 - 48.9 µin/in-°F @Temperature 140 - 280 °F | Average value: 88.0 µm/m-°C Grade Count:1 | |
| Melting Point | 210 - 225 °C | 410 - 437 °F | Average value: 223 °C Grade Count:15 |
| Maximum Service Temperature, Air | 100 - 345 °C | 212 - 653 °F | Average value: 234 °C Grade Count:11 |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 - 215 °C | 230 - 419 °F | Average value: 177 °C Grade Count:30 |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 - 206 °C | 120 - 402 °F | Average value: 105 °C Grade Count:29 |
| Vicat Softening Point | 170 - 205 °C | 338 - 401 °F | Average value: 186 °C Grade Count:6 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:30 |
| Glow Wire Test | 650 - 960 °C | 1200 - 1760 °F | Average value: 753 °C Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 280 °C | 68.0 - 536 °F | Average value: 199 °C Grade Count:6 |
| Nozzle Temperature | 240 - 271 °C | 464 - 520 °F | Average value: 254 °C Grade Count:4 |
| Melt Temperature | 220 - 277 °C | 428 - 531 °F | Average value: 250 °C Grade Count:13 |
| Mold Temperature | 37.8 - 110 °C | 100 - 230 °F | Average value: 73.8 °C Grade Count:13 |
| Drying Temperature | 120 - 140 °C | 248 - 284 °F | Average value: 124 °C Grade Count:8 |
| Dry Time | 3.00 - 12.0 hour | 3.00 - 12.0 hour | Average value: 4.75 hour Grade Count:6 |
| Moisture Content | 0.000 - 0.200 % | 0.000 - 0.200 % | Average value: 0.0625 % Grade Count:4 |
| Back Pressure | 0.000 - 0.689 MPa | 0.000 - 100 psi | Average value: 0.402 MPa Grade Count:3 |