- 密度 [g/cm3]: 1.47
- 吸水率 [%]: 0.4
- 缺口冲击强度: 7.0
- 弯曲强度 [MPa]: 120.0
- 弯曲模量 [MPa]: 8.51
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Test | 111 cm³/g | 111 cm³/g | Viscosity number | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 120 MPa | 17400 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.3 % | 2.3 % | 5mm/min; ISO 527 | ||
| Flexural Modulus | 8.51 GPa | 1230 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO Test | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 223 °C | 433 °F | 10 K/min | ||
| 223 °C | 433 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | BK15077 | ||||
| Commercial Status | North America and Europe | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||