- 熔体流动速率 [g/10min]: 11.7
- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.4
- 拉伸强度 [MPa]: 56.0
- 热变形温度 [℃]: 135.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | Saturation; DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.25 % | 0.25 % | 23°C; 50% RH | ||
| Viscosity Measurement | 160 | 160 | [ml/g]; Viscosity number; ISO 1628 | ||
| Linear Mold Shrinkage, Flow | 0.019 cm/cm | 0.019 in/in | Sheet; ISO 294 | ||
| Linear Mold Shrinkage, Transverse | 0.022 cm/cm | 0.022 in/in | Sheet; ISO 294 | ||
| Melt Flow | 11.7 g/10 min @Load 2.16 kg, Temperature 250 °C | 11.7 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 56.0 MPa | 8120 psi | 5 mm/min; ISO 527-2 | ||
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527-2 | ||
| Elongation at Break | >= 3.5 % | >= 3.5 % | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 3.5 % | 3.5 % | 50 mm/min; ISO 527-2 | ||
| >= 50 % | >= 50 % | 50 mm/min; ISO 527-2 | |||
| Modulus of Elasticity | 2.60 GPa | 377 ksi | ISO 527-2 | ||
| Flexural Strength | 76.0 MPa | 11000 psi | ISO 178 | ||
| Charpy Impact Unnotched | 22.0 J/cm² @Temperature -30.0 °C | 105 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.600 J/cm² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 5.00e+15 ohm-cm | 5.00e+15 ohm-cm | IEC 93 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 93 | ||
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz | 3.2 @Frequency 1.00e+6 Hz | IEC 250 | ||
| 3.4 @Frequency 100 Hz | 3.4 @Frequency 100 Hz | IEC 250 | |||
| Dielectric Strength | 39.0 kV/mm | 991 kV/in | IEC 243/1 | ||
| Dissipation Factor | 0.0019 @Frequency 100 Hz | 0.0019 @Frequency 100 Hz | IEC 250 | ||
| 0.0219 @Frequency 1.00e+6 Hz | 0.0219 @Frequency 1.00e+6 Hz | IEC 250 | |||
| Comparative Tracking Index | 475 V | 475 V | Test solution A; IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 9.00 - 15.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 5.00 - 8.33 µin/in-°F @Temperature 73.4 - 176 °F | DIN 53752 | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | DSC; ISO 11357-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-2 | ||
| Decomposition Temperature | >= 290 °C | >= 554 °F | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| HB @Diameter 0.400 mm | HB @Diameter 0.0157 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | Semi-finished extrusion | ||
| 250 - 270 °C | 482 - 518 °F | Pipe extrusion | |||
| 260 °C | 500 °F | for shrinkage test | |||
| 260 - 270 °C | 500 - 518 °F | Injection-molding | |||
| Mold Temperature | 60.0 °C | 140 °F | for shrinkage test | ||
| 40.0 - 80.0 °C | 104 - 176 °F | Injection molding | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | 350 °C | ASTM D1929 | |||
| Primary Processing Technique | Coating and Injection Molding | ||||