BASF Ultradur S 4090 G6 LS High Speed BK15077 30% Glass Filled PBT物性表参数

BASF Ultradur S 4090 G6 LS High Speed BK15077 30% Glass Filled PBT

BASF Ultradur S 4090 G6 LS High Speed BK15077 30% Glass Filled PBT 物性表: BASF Ultradur S 4090 G6 LS High Speed BK15077 30% Glass Filled PBT物性表及特性介绍,BASF Ultradur S 4090 G6 LS High Speed BK15077 30% Glass Filled PBT注塑参数详情,如需BASF Ultradur S 4090 G6 LS High Speed BK15077 30% Glass Filled PBT下载, 可到相关下载区下载

熔体流动速率 [g/10min]: 33.9
密度 [g/cm3]: 1.47
弯曲强度 [MPa]: 125.0
热变形温度 [℃]: 215.0

Physical Properties	Metric	English	Comments

Density	1.47 g/cc	0.0531 lb/in³	ISO 1183
Viscosity Test	102 cm³/g	102 cm³/g	Viscosity number
Melt Flow	33.9 g/10 min @Load 2.16 kg, Temperature 275 °C	33.9 g/10 min @Load 4.76 lb, Temperature 527 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	125 MPa	18100 psi	5mm/min; ISO 527
Elongation at Break	2.1 %	2.1 %	5mm/min; ISO 527
Tensile Modulus	9.90 GPa	1440 ksi	1mm/min; ISO 527

Thermal Properties	Metric	English	Comments
Melting Point	223 °C	433 °F	10 K/min
Deflection Temperature at 0.46 MPa (66 psi)	215 °C	419 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	190 °C	374 °F	ISO 75

Descriptive Properties
Color	BK15077
Commercial Status	Active America
Impact Modified	No
Primary Processing Technique	Injection Molding

关键词:
PBT
供应
BASF Ultradur S 4090 G6 LS High Speed BK15077 30% Glass Filled PBT

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-37920.html

免责声明: 本文 BASF Ultradur S 4090 G6 LS High Speed BK15077 30% Glass Filled PBT 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络