- 密度 [g/cm3]: 1.3
- 缺口冲击强度: 0.53
- 断裂伸长率 [%]: 79.0
- 弯曲强度 [MPa]: 60.0
- 弯曲模量 [MPa]: 2.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Yield Strength | 79.0 MPa | 11500 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 254 °C | 489 °F | |