- 熔体流动速率 [g/10min]: 10.0
- 缺口冲击强度: 6.675
- 拉伸强度 [MPa]: 55.1
- 弯曲模量 [MPa]: 2.068
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 3.80 kg, Temperature 260 °C | 10 g/10 min @Load 8.38 lb, Temperature 500 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 55.1 MPa | 7990 psi | chs 2.0 in/min; ASTM D638 |
| Flexural Modulus | 2.068 GPa | 299.9 ksi | chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 6.675 J/cm @Thickness 3.17 mm | 12.51 ft-lb/in @Thickness 0.125 in | ASTM D256 |