  4. DuPont Performance Polymers Crastin® LW9020 NC010 PBT

DuPont Performance Polymers Crastin® LW9020 NC010 PBT

DuPont Performance Polymers Crastin® LW9020 NC010 PBT 物性表: DuPont Performance Polymers Crastin® LW9020 NC010 PBT物性表及特性介绍,DuPont Performance Polymers Crastin® LW9020 NC010 PBT注塑参数详情,如需DuPont Performance Polymers Crastin® LW9020 NC010 PBT下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.35
  • 吸水率 [%]: 0.26
  • 缺口冲击强度: 7.0
  • 弯曲模量 [MPa]: 6.30
  • 热变形温度 [℃]: 210.0
 
Physical PropertiesMetricEnglishComments
Density 1.35 g/cc0.0488 lb/in³ISO 1183
Filler Content 20 %20 %
Water Absorption  0.26 %
@Temperature 23.0 °C		0.26 %
@Temperature 73.4 °F		Equilibrium 50%RH; ISO 62, Similar to
 0.78 %
@Temperature 23.0 °C		0.78 %
@Temperature 73.4 °F		Saturation, immersed; ISO 62, Similar to
Viscosity  41000 cP
@Shear Rate 10000 1/s,
Temperature 260 °C		41000 cP
@Shear Rate 10000 1/s,
Temperature 500 °F		ISO 11443
 47000 cP
@Shear Rate 10000 1/s,
Temperature 250 °C		47000 cP
@Shear Rate 10000 1/s,
Temperature 482 °F		ISO 11443
 53000 cP
@Shear Rate 10000 1/s,
Temperature 240 °C		53000 cP
@Shear Rate 10000 1/s,
Temperature 464 °F		ISO 11443
 64000 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		64000 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		ISO 11443
 72000 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		72000 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		ISO 11443
 83000 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		83000 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		ISO 11443
 113000 cP
@Shear Rate 2000 1/s,
Temperature 260 °C		113000 cP
@Shear Rate 2000 1/s,
Temperature 500 °F		ISO 11443
 128000 cP
@Shear Rate 2000 1/s,
Temperature 250 °C		128000 cP
@Shear Rate 2000 1/s,
Temperature 482 °F		ISO 11443
 146000 cP
@Shear Rate 2000 1/s,
Temperature 240 °C		146000 cP
@Shear Rate 2000 1/s,
Temperature 464 °F		ISO 11443
 170000 cP
@Shear Rate 1000 1/s,
Temperature 260 °C		170000 cP
@Shear Rate 1000 1/s,
Temperature 500 °F		ISO 11443
 195000 cP
@Shear Rate 1000 1/s,
Temperature 250 °C		195000 cP
@Shear Rate 1000 1/s,
Temperature 482 °F		ISO 11443
 224000 cP
@Shear Rate 1000 1/s,
Temperature 240 °C		224000 cP
@Shear Rate 1000 1/s,
Temperature 464 °F		ISO 11443
 253000 cP
@Shear Rate 500 1/s,
Temperature 260 °C		253000 cP
@Shear Rate 500 1/s,
Temperature 500 °F		ISO 11443
 292000 cP
@Shear Rate 500 1/s,
Temperature 250 °C		292000 cP
@Shear Rate 500 1/s,
Temperature 482 °F		ISO 11443
 338000 cP
@Shear Rate 500 1/s,
Temperature 240 °C		338000 cP
@Shear Rate 500 1/s,
Temperature 464 °F		ISO 11443
 537000 cP
@Shear Rate 100 1/s,
Temperature 260 °C		537000 cP
@Shear Rate 100 1/s,
Temperature 500 °F		ISO 11443
 654000 cP
@Shear Rate 100 1/s,
Temperature 250 °C		654000 cP
@Shear Rate 100 1/s,
Temperature 482 °F		ISO 11443
 797000 cP
@Shear Rate 100 1/s,
Temperature 240 °C		797000 cP
@Shear Rate 100 1/s,
Temperature 464 °F		ISO 11443
Linear Mold Shrinkage 0.0030 cm/cm0.0030 in/inFlow
 0.0060 cm/cm0.0060 in/inTransverse
Linear Mold Shrinkage, Flow 0.0055 cm/cm0.0055 in/inParallel; Annealed; ISO 294-4
 0.0035 cm/cm
@Thickness 2.00 mm		0.0035 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm0.0090 in/inNormal; Annealed; ISO 294-4
 0.0065 cm/cm
@Thickness 2.00 mm		0.0065 in/in
@Thickness 0.0787 in		Normal; ISO 294-4
Melt Index of Compound 15 g/10 min
@Load 5.00 kg,
Temperature 250 °C		15 g/10 min
@Load 11.0 lb,
Temperature 482 °F		cm3/10 min; ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 110 MPa
@Temperature 23.0 °C		16000 psi
@Temperature 73.4 °F		ISO 527
Tensile Stress  2.204 MPa
@Strain 0.250 %,
Temperature 160 °C		319.7 psi
@Strain 0.250 %,
Temperature 320 °F		ISO 11403-1/-2
 3.563 MPa
@Strain 0.250 %,
Temperature 120 °C		516.8 psi
@Strain 0.250 %,
Temperature 248 °F		ISO 11403-1/-2
 4.133 MPa
@Strain 0.500 %,
Temperature 160 °C		599.4 psi
@Strain 0.500 %,
Temperature 320 °F		ISO 11403-1/-2
 6.84 MPa
@Strain 0.500 %,
Temperature 120 °C		992 psi
@Strain 0.500 %,
Temperature 248 °F		ISO 11403-1/-2
 7.22 MPa
@Strain 1.00 %,
Temperature 160 °C		1050 psi
@Strain 1.00 %,
Temperature 320 °F		ISO 11403-1/-2
 7.781 MPa
@Strain 0.250 %,
Temperature 100 °C		1129 psi
@Strain 0.250 %,
Temperature 212 °F		ISO 11403-1/-2
 9.405 MPa
@Strain 1.50 %,
Temperature 160 °C		1364 psi
@Strain 1.50 %,
Temperature 320 °F		ISO 11403-1/-2
 10.83 MPa
@Strain 0.250 %,
Temperature 80.0 °C		1571 psi
@Strain 0.250 %,
Temperature 176 °F		ISO 11403-1/-2
 10.925 MPa
@Strain 2.00 %,
Temperature 160 °C		1584.5 psi
@Strain 2.00 %,
Temperature 320 °F		ISO 11403-1/-2
 11.78 MPa
@Strain 0.250 %,
Temperature 60.0 °C		1709 psi
@Strain 0.250 %,
Temperature 140 °F		ISO 11403-1/-2
 11.875 MPa
@Strain 2.50 %,
Temperature 160 °C		1722.3 psi
@Strain 2.50 %,
Temperature 320 °F		ISO 11403-1/-2
 12.445 MPa
@Strain 1.00 %,
Temperature 120 °C		1805.0 psi
@Strain 1.00 %,
Temperature 248 °F		ISO 11403-1/-2
 12.54 MPa
@Strain 3.20 %,
Temperature 160 °C		1819 psi
@Strain 3.20 %,
Temperature 320 °F		Break; ISO 11403-1/-2
 14.82 MPa
@Strain 0.250 %,
Temperature 40.0 °C		2149 psi
@Strain 0.250 %,
Temperature 104 °F		ISO 11403-1/-2
 14.82 MPa
@Strain 0.500 %,
Temperature 100 °C		2149 psi
@Strain 0.500 %,
Temperature 212 °F		ISO 11403-1/-2
 16.625 MPa
@Strain 1.50 %,
Temperature 120 °C		2411.3 psi
@Strain 1.50 %,
Temperature 248 °F		ISO 11403-1/-2
 17.5 MPa
@Strain 0.250 %,
Temperature 23.0 °C		2540 psi
@Strain 0.250 %,
Temperature 73.4 °F		ISO 11403-1/-2
 17.955 MPa
@Strain 0.250 %,
Temperature 0.000 °C		2604.2 psi
@Strain 0.250 %,
Temperature 32.0 °F		ISO 11403-1/-2
 18.335 MPa
@Strain 0.250 %,
Temperature -20.0 °C		2659.3 psi
@Strain 0.250 %,
Temperature -4.00 °F		ISO 11403-1/-2
 18.81 MPa
@Strain 0.250 %,
Temperature -40.0 °C		2728 psi
@Strain 0.250 %,
Temperature -40.0 °F		ISO 11403-1/-2
 19.475 MPa
@Strain 2.00 %,
Temperature 120 °C		2824.6 psi
@Strain 2.00 %,
Temperature 248 °F		ISO 11403-1/-2
 20.805 MPa
@Strain 0.500 %,
Temperature 80.0 °C		3017.5 psi
@Strain 0.500 %,
Temperature 176 °F		ISO 11403-1/-2
 21.28 MPa
@Strain 2.50 %,
Temperature 120 °C		3086 psi
@Strain 2.50 %,
Temperature 248 °F		ISO 11403-1/-2
 22.325 MPa
@Strain 3.20 %,
Temperature 120 °C		3238.0 psi
@Strain 3.20 %,
Temperature 248 °F		Break; ISO 11403-1/-2
 22.8 MPa
@Strain 0.500 %,
Temperature 60.0 °C		3310 psi
@Strain 0.500 %,
Temperature 140 °F		ISO 11403-1/-2
 26.22 MPa
@Strain 1.00 %,
Temperature 100 °C		3803 psi
@Strain 1.00 %,
Temperature 212 °F		ISO 11403-1/-2
 28.975 MPa
@Strain 0.500 %,
Temperature 40.0 °C		4202.5 psi
@Strain 0.500 %,
Temperature 104 °F		ISO 11403-1/-2
 33.775 MPa
@Strain 0.500 %,
Temperature 23.0 °C		4898.7 psi
@Strain 0.500 %,
Temperature 73.4 °F		ISO 11403-1/-2
 34.01 MPa
@Strain 1.50 %,
Temperature 100 °C		4933 psi
@Strain 1.50 %,
Temperature 212 °F		ISO 11403-1/-2
 35.435 MPa
@Strain 0.500 %,
Temperature 0.000 °C		5139.4 psi
@Strain 0.500 %,
Temperature 32.0 °F		ISO 11403-1/-2
 36.29 MPa
@Strain 0.500 %,
Temperature -20.0 °C		5263 psi
@Strain 0.500 %,
Temperature -4.00 °F		ISO 11403-1/-2
 37.24 MPa
@Strain 1.00 %,
Temperature 80.0 °C		5401 psi
@Strain 1.00 %,
Temperature 176 °F		ISO 11403-1/-2
 37.335 MPa
@Strain 0.500 %,
Temperature -40.0 °C		5415.0 psi
@Strain 0.500 %,
Temperature -40.0 °F		ISO 11403-1/-2
 38.665 MPa
@Strain 2.00 %,
Temperature 100 °C		5607.9 psi
@Strain 2.00 %,
Temperature 212 °F		ISO 11403-1/-2
 41.04 MPa
@Strain 2.50 %,
Temperature 100 °C		5952 psi
@Strain 2.50 %,
Temperature 212 °F		ISO 11403-1/-2
 41.61 MPa
@Strain 1.00 %,
Temperature 60.0 °C		6035 psi
@Strain 1.00 %,
Temperature 140 °F		ISO 11403-1/-2
 41.8 MPa
@Strain 3.20 %,
Temperature 100 °C		6060 psi
@Strain 3.20 %,
Temperature 212 °F		Break; ISO 11403-1/-2
 48.735 MPa
@Strain 1.50 %,
Temperature 80.0 °C		7068.4 psi
@Strain 1.50 %,
Temperature 176 °F		ISO 11403-1/-2
 53.58 MPa
@Strain 1.00 %,
Temperature 40.0 °C		7771 psi
@Strain 1.00 %,
Temperature 104 °F		ISO 11403-1/-2
 55.48 MPa
@Strain 1.50 %,
Temperature 60.0 °C		8047 psi
@Strain 1.50 %,
Temperature 140 °F		ISO 11403-1/-2
 56.05 MPa
@Strain 2.00 %,
Temperature 80.0 °C		8129 psi
@Strain 2.00 %,
Temperature 176 °F		ISO 11403-1/-2
 60.04 MPa
@Strain 2.50 %,
Temperature 80.0 °C		8708 psi
@Strain 2.50 %,
Temperature 176 °F		ISO 11403-1/-2
 61.56 MPa
@Strain 3.20 %,
Temperature 80.0 °C		8929 psi
@Strain 3.20 %,
Temperature 176 °F		Break; ISO 11403-1/-2
 62.5 MPa
@Strain 1.00 %,
Temperature 23.0 °C		9060 psi
@Strain 1.00 %,
Temperature 73.4 °F		ISO 11403-1/-2
 64.41 MPa
@Strain 2.00 %,
Temperature 60.0 °C		9342 psi
@Strain 2.00 %,
Temperature 140 °F		ISO 11403-1/-2
 67.07 MPa
@Strain 1.00 %,
Temperature 0.000 °C		9728 psi
@Strain 1.00 %,
Temperature 32.0 °F		ISO 11403-1/-2
 69.35 MPa
@Strain 2.50 %,
Temperature 60.0 °C		10060 psi
@Strain 2.50 %,
Temperature 140 °F		ISO 11403-1/-2
 69.445 MPa
@Strain 1.00 %,
Temperature -20.0 °C		10072 psi
@Strain 1.00 %,
Temperature -4.00 °F		ISO 11403-1/-2
 71.44 MPa
@Strain 3.20 %,
Temperature 60.0 °C		10360 psi
@Strain 3.20 %,
Temperature 140 °F		Break; ISO 11403-1/-2
 71.535 MPa
@Strain 1.50 %,
Temperature 40.0 °C		10375 psi
@Strain 1.50 %,
Temperature 104 °F		ISO 11403-1/-2
 71.82 MPa
@Strain 1.00 %,
Temperature -40.0 °C		10420 psi
@Strain 1.00 %,
Temperature -40.0 °F		ISO 11403-1/-2
 82.745 MPa
@Strain 2.00 %,
Temperature 40.0 °C		12001 psi
@Strain 2.00 %,
Temperature 104 °F		ISO 11403-1/-2
 83.315 MPa
@Strain 1.50 %,
Temperature 23.0 °C		12084 psi
@Strain 1.50 %,
Temperature 73.4 °F		ISO 11403-1/-2
 88.445 MPa
@Strain 2.50 %,
Temperature 40.0 °C		12828 psi
@Strain 2.50 %,
Temperature 104 °F		ISO 11403-1/-2
 90.155 MPa
@Strain 3.20 %,
Temperature 40.0 °C		13076 psi
@Strain 3.20 %,
Temperature 104 °F		Break; ISO 11403-1/-2
 92.815 MPa
@Strain 1.50 %,
Temperature 0.000 °C		13462 psi
@Strain 1.50 %,
Temperature 32.0 °F		ISO 11403-1/-2
 97.85 MPa
@Strain 1.50 %,
Temperature -20.0 °C		14190 psi
@Strain 1.50 %,
Temperature -4.00 °F		ISO 11403-1/-2
 98.8 MPa
@Strain 2.00 %,
Temperature 23.0 °C		14300 psi
@Strain 2.00 %,
Temperature 73.4 °F		ISO 11403-1/-2
 100.7 MPa
@Strain 1.50 %,
Temperature -40.0 °C		14610 psi
@Strain 1.50 %,
Temperature -40.0 °F		ISO 11403-1/-2
 108.3 MPa
@Strain 2.50 %,
Temperature 23.0 °C		15710 psi
@Strain 2.50 %,
Temperature 73.4 °F		ISO 11403-1/-2
 111.15 MPa
@Strain 2.00 %,
Temperature 0.000 °C		16121 psi
@Strain 2.00 %,
Temperature 32.0 °F		ISO 11403-1/-2
 113 MPa
@Strain 3.00 %,
Temperature 23.0 °C		16400 psi
@Strain 3.00 %,
Temperature 73.4 °F		Break; ISO 11403-1/-2
 119.7 MPa
@Strain 2.00 %,
Temperature -20.0 °C		17360 psi
@Strain 2.00 %,
Temperature -4.00 °F		ISO 11403-1/-2
 123.5 MPa
@Strain 2.00 %,
Temperature -40.0 °C		17910 psi
@Strain 2.00 %,
Temperature -40.0 °F		ISO 11403-1/-2
 127.3 MPa
@Strain 2.70 %,
Temperature 0.000 °C		18460 psi
@Strain 2.70 %,
Temperature 32.0 °F		Break; ISO 11403-1/-2
 140.6 MPa
@Strain 2.70 %,
Temperature -20.0 °C		20390 psi
@Strain 2.70 %,
Temperature -4.00 °F		Break; ISO 11403-1/-2
 144.4 MPa
@Strain 2.70 %,
Temperature -40.0 °C		20940 psi
@Strain 2.70 %,
Temperature -40.0 °F		Break; ISO 11403-1/-2
Elongation at Break 2.9 %
@Temperature 23.0 °C		2.9 %
@Temperature 73.4 °F		ISO 527
Tensile Modulus 7.00 GPa
@Temperature 23.0 °C		1020 ksi
@Temperature 73.4 °F		ISO 527
Flexural Strength 170 MPa
@Temperature 23.0 °C		24700 psi
@Temperature 73.4 °F		ISO 178
Flexural Modulus 6.30 GPa
@Temperature 23.0 °C		914 ksi
@Temperature 73.4 °F		ISO 178
Shear Modulus  0.147 GPa
@Temperature 200 °C		21.3 ksi
@Temperature 392 °F		ISO 6721
 0.166 GPa
@Temperature 190 °C		24.1 ksi
@Temperature 374 °F		ISO 6721
 0.181 GPa
@Temperature 180 °C		26.3 ksi
@Temperature 356 °F		ISO 6721
 0.195 GPa
@Temperature 170 °C		28.3 ksi
@Temperature 338 °F		ISO 6721
 0.210 GPa
@Temperature 160 °C		30.5 ksi
@Temperature 320 °F		ISO 6721
 0.228 GPa
@Temperature 150 °C		33.1 ksi
@Temperature 302 °F		ISO 6721
 0.260 GPa
@Temperature 140 °C		37.7 ksi
@Temperature 284 °F		ISO 6721
 0.369 GPa
@Temperature 130 °C		53.5 ksi
@Temperature 266 °F		ISO 6721
 0.640 GPa
@Temperature 120 °C		92.8 ksi
@Temperature 248 °F		ISO 6721
 0.794 GPa
@Temperature 110 °C		115 ksi
@Temperature 230 °F		ISO 6721
 0.873 GPa
@Temperature 100 °C		127 ksi
@Temperature 212 °F		ISO 6721
 0.944 GPa
@Temperature 90.0 °C		137 ksi
@Temperature 194 °F		ISO 6721
 1.03 GPa
@Temperature 80.0 °C		149 ksi
@Temperature 176 °F		ISO 6721
 1.15 GPa
@Temperature 70.0 °C		167 ksi
@Temperature 158 °F		ISO 6721
 1.33 GPa
@Temperature 60.0 °C		193 ksi
@Temperature 140 °F		ISO 6721
 1.57 GPa
@Temperature 50.0 °C		228 ksi
@Temperature 122 °F		ISO 6721
 1.74 GPa
@Temperature 40.0 °C		252 ksi
@Temperature 104 °F		ISO 6721
 1.78 GPa
@Temperature 30.0 °C		258 ksi
@Temperature 86.0 °F		ISO 6721
 1.81 GPa
@Temperature 20.0 °C		263 ksi
@Temperature 68.0 °F		ISO 6721
 1.84 GPa
@Temperature 10.0 °C		267 ksi
@Temperature 50.0 °F		ISO 6721
 1.87 GPa
@Temperature 0.000 °C		271 ksi
@Temperature 32.0 °F		ISO 6721
 1.89 GPa
@Temperature -10.0 °C		274 ksi
@Temperature 14.0 °F		ISO 6721
 1.92 GPa
@Temperature -20.0 °C		278 ksi
@Temperature -4.00 °F		ISO 6721
 1.96 GPa
@Temperature -30.0 °C		284 ksi
@Temperature -22.0 °F		ISO 6721
 2.03 GPa
@Temperature -40.0 °C		294 ksi
@Temperature -40.0 °F		ISO 6721
 2.14 GPa
@Temperature -50.0 °C		310 ksi
@Temperature -58.0 °F		ISO 6721
Izod Impact, Notched (ISO)  7.00 kJ/m²
@Temperature -30.0 °C		3.33 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1A
 8.00 kJ/m²
@Temperature 23.0 °C		3.81 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1A
Izod Impact, Unnotched (ISO)  50.0 kJ/m²
@Temperature -30.0 °C		23.8 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1U
 50.0 kJ/m²
@Temperature 23.0 °C		23.8 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1U
Charpy Impact Unnotched  4.30 J/cm²
@Temperature -30.0 °C		20.5 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
 6.00 J/cm²
@Temperature 23.0 °C		28.6 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched  0.750 J/cm²
@Temperature -30.0 °C		3.57 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 0.950 J/cm²
@Temperature 23.0 °C		4.52 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
Tensile Creep Modulus, 1 hour 6500 MPa
@Temperature 23.0 °C		943000 psi
@Temperature 73.4 °F		ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.170 %,
Temperature 23.0 °C		1450 psi
@Strain 0.170 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.158 %,
Temperature 23.0 °C		1450 psi
@Strain 0.158 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.310 %,
Temperature 23.0 °C		2900 psi
@Strain 0.310 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.337 %,
Temperature 23.0 °C		2900 psi
@Strain 0.337 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.507 %,
Temperature 23.0 °C		4350 psi
@Strain 0.507 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.460 %,
Temperature 23.0 °C		4350 psi
@Strain 0.460 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.613 %,
Temperature 23.0 °C		5800 psi
@Strain 0.613 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.684 %,
Temperature 23.0 °C		5800 psi
@Strain 0.684 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.875 %,
Temperature 23.0 °C		7250 psi
@Strain 0.875 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.774 %,
Temperature 23.0 °C		7250 psi
@Strain 0.774 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 60.0 MPa
@Strain 0.948 %,
Temperature 23.0 °C		8700 psi
@Strain 0.948 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 60.0 MPa
@Strain 1.09 %,
Temperature 23.0 °C		8700 psi
@Strain 1.09 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 70.0 MPa
@Strain 1.36 %,
Temperature 23.0 °C		10200 psi
@Strain 1.36 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 70.0 MPa
@Strain 1.15 %,
Temperature 23.0 °C		10200 psi
@Strain 1.15 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 80.0 MPa
@Strain 1.40 %,
Temperature 23.0 °C		11600 psi
@Strain 1.40 %,
Temperature 73.4 °F		1h; Break; Isochronous; ISO 899
 80.0 MPa
@Strain 1.77 %,
Temperature 23.0 °C		11600 psi
@Strain 1.77 %,
Temperature 73.4 °F		10h; Break; Isochronous; ISO 899
Tensile Creep Modulus, 1000 hours 4800 MPa
@Temperature 23.0 °C		696000 psi
@Temperature 73.4 °F		ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.196 %,
Temperature 23.0 °C		1450 psi
@Strain 0.196 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.211 %,
Temperature 23.0 °C		1450 psi
@Strain 0.211 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.416 %,
Temperature 23.0 °C		2900 psi
@Strain 0.416 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.384 %,
Temperature 23.0 °C		2900 psi
@Strain 0.384 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.573 %,
Temperature 23.0 °C		4350 psi
@Strain 0.573 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.623 %,
Temperature 23.0 °C		4350 psi
@Strain 0.623 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.839 %,
Temperature 23.0 °C		5800 psi
@Strain 0.839 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.768 %,
Temperature 23.0 °C		5800 psi
@Strain 0.768 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.979 %,
Temperature 23.0 °C		7250 psi
@Strain 0.979 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 50.0 MPa
@Strain 1.08 %,
Temperature 23.0 °C		7250 psi
@Strain 1.08 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 60.0 MPa
@Strain 1.35 %,
Temperature 23.0 °C		8700 psi
@Strain 1.35 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 60.0 MPa
@Strain 1.22 %,
Temperature 23.0 °C		8700 psi
@Strain 1.22 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 70.0 MPa
@Strain 1.53 %,
Temperature 23.0 °C		10200 psi
@Strain 1.53 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 70.0 MPa
@Strain 1.71 %,
Temperature 23.0 °C		10200 psi
@Strain 1.71 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 80.0 MPa
@Strain 2.46 %,
Temperature 23.0 °C		11600 psi
@Strain 2.46 %,
Temperature 73.4 °F		1000h; Break; Isochronous; ISO 899
 80.0 MPa
@Strain 2.07 %,
Temperature 23.0 °C		11600 psi
@Strain 2.07 %,
Temperature 73.4 °F		100h; Break; Isochronous; ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity >= 1.00e+15 ohm-cm
@Temperature 23.0 °C		>= 1.00e+15 ohm-cm
@Temperature 73.4 °F		IEC 60093
Surface Resistance 1.00e+14 ohm
@Temperature 23.0 °C		1.00e+14 ohm
@Temperature 73.4 °F		IEC 60093
Dielectric Constant  3.4
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.4
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
 3.6
@Frequency 100 Hz,
Temperature 23.0 °C		3.6
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
Dielectric Strength 35.0 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		889 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		IEC 60243-1
 20.0 kV/mm
@Thickness 2.00 mm,
Time 20.0 sec		508 kV/in
@Thickness 0.0787 in,
Time 0.00556 hour		IEC 60243-1
Dissipation Factor  0.0030
@Frequency 100 Hz,
Temperature 23.0 °C		0.0030
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
 0.018
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.018
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
Comparative Tracking Index  500 V
@Temperature 23.0 °C		500 V
@Temperature 73.4 °F		UL 746A
 550 V
@Temperature 23.0 °C		550 V
@Temperature 73.4 °F		IEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  100 µm/m-°C
@Temperature 23.0 - 55.0 °C		55.6 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 100 µm/m-°C
@Temperature 23.0 - 55.0 °C		55.6 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi) 210 °C410 °FISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 160 °C320 °FISO 75-1/-2
Deflection Temperature at 8.0 MPa 88.0 °C190 °FISO 75-1/-2
Glass Transition Temp, Tg 110 °C230 °F10°C/min; ISO 11357-1/-2
UL RTI, Electrical  130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
 130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
UL RTI, Mechanical with Impact  125 °C
@Thickness 0.750 mm		257 °F
@Thickness 0.0295 in		UL 746B
 125 °C
@Thickness 1.50 mm		257 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical without Impact  130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
Flammability, UL94  HB
@Thickness 6.00 mm		HB
@Thickness 0.236 in		IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		UL94
 HB
@Thickness 6.00 mm		HB
@Thickness 0.236 in		UL94
Oxygen Index 19 %19 %ISO 4589-1/-2
Glow Wire Test 650 °C
@Thickness 3.00 mm		1200 °F
@Thickness 0.118 in		IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 225 °C437 °F10°C/min; ISO 11357-1/-3
 250 °C482 °FOptimum
 240 - 260 °C464 - 500 °F
Mold Temperature 80.0 °C176 °Foptimum
 30.0 - 130 °C86.0 - 266 °F
Drying Temperature 110 - 130 °C230 - 266 °F
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hour
Moisture Content <= 0.040 %<= 0.040 %
 
Descriptive Properties
AdditiveLubricant
AppearanceNatural Color
Drying RecommendedYes
FeaturesChemical Resistance, Good
 Dimensional Stability, Good
 Moisture Absorption, Low
 Processability, Good
 Warp Resistant
 Warpage, Low
FillerGlass fiber reinforcement
FormsPellets
GenericPBT Alloy
Material StatusCurrent
Part Marking Code>PBT+ASA-GF20<ISO 11469
Polymer FamilyPolyester
Polymer TypePBT
Processing MethodInjection Molding
Product CategoryGlass Reinforced Resins
 Low Warp Resins
Region Available - GlobalYes
Resin IdentificationPBT+ASA-GF20ISO 1043
RoHS ComplianceContact Manufacturer
Ultrasonic WeldableYes
UsesAutomotive Applications
 Housings
 Industrial Applications

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38046.html

免责声明: 本文 DuPont Performance Polymers Crastin® LW9020 NC010 PBT 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4