DuPont Performance Polymers Crastin® LW9330 NC010 PBT

DuPont Performance Polymers Crastin® LW9330 NC010 PBT 物性表: DuPont Performance Polymers Crastin® LW9330 NC010 PBT物性表及特性介绍,DuPont Performance Polymers Crastin® LW9330 NC010 PBT注塑参数详情,如需DuPont Performance Polymers Crastin® LW9330 NC010 PBT下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.42
  • 吸水率 [%]: 0.25
  • 成型收缩率 [%]: 0.002
  • 缺口冲击强度: 0.96
  • 弯曲模量 [MPa]: 1.30
  • 热变形温度 [℃]: 215.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.43 g/cc1.43 g/ccASTM D792
Density 1.42 g/cc0.0513 lb/in³ISO 1183
Filler Content 30 %30 %
Water Absorption  0.25 %
@Thickness 1.00 mm,
Temperature 23.0 °C		0.25 %
@Thickness 0.0394 in,
Temperature 73.4 °F		Equilibrium 50%RH; ISO 62, Similar to
 1.0 %
@Thickness 1.00 mm,
Temperature 23.0 °C		1.0 %
@Thickness 0.0394 in,
Temperature 73.4 °F		Saturation, immersed; ISO 62, Similar to
Viscosity  40000 cP
@Shear Rate 10000 1/s,
Temperature 270 °C		40000 cP
@Shear Rate 10000 1/s,
Temperature 518 °F		ISO 11443
 45000 cP
@Shear Rate 10000 1/s,
Temperature 260 °C		45000 cP
@Shear Rate 10000 1/s,
Temperature 500 °F		ISO 11443
 50000 cP
@Shear Rate 10000 1/s,
Temperature 250 °C		50000 cP
@Shear Rate 10000 1/s,
Temperature 482 °F		ISO 11443
 64000 cP
@Shear Rate 5000 1/s,
Temperature 270 °C		64000 cP
@Shear Rate 5000 1/s,
Temperature 518 °F		ISO 11443
 72000 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		72000 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		ISO 11443
 81000 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		81000 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		ISO 11443
 119000 cP
@Shear Rate 2000 1/s,
Temperature 270 °C		119000 cP
@Shear Rate 2000 1/s,
Temperature 518 °F		ISO 11443
 133000 cP
@Shear Rate 2000 1/s,
Temperature 260 °C		133000 cP
@Shear Rate 2000 1/s,
Temperature 500 °F		ISO 11443
 150000 cP
@Shear Rate 2000 1/s,
Temperature 250 °C		150000 cP
@Shear Rate 2000 1/s,
Temperature 482 °F		ISO 11443
 185000 cP
@Shear Rate 1000 1/s,
Temperature 270 °C		185000 cP
@Shear Rate 1000 1/s,
Temperature 518 °F		ISO 11443
 209000 cP
@Shear Rate 1000 1/s,
Temperature 260 °C		209000 cP
@Shear Rate 1000 1/s,
Temperature 500 °F		ISO 11443
 238000 cP
@Shear Rate 1000 1/s,
Temperature 250 °C		238000 cP
@Shear Rate 1000 1/s,
Temperature 482 °F		ISO 11443
 279000 cP
@Shear Rate 500 1/s,
Temperature 270 °C		279000 cP
@Shear Rate 500 1/s,
Temperature 518 °F		ISO 11443
 321000 cP
@Shear Rate 500 1/s,
Temperature 260 °C		321000 cP
@Shear Rate 500 1/s,
Temperature 500 °F		ISO 11443
 370000 cP
@Shear Rate 500 1/s,
Temperature 250 °C		370000 cP
@Shear Rate 500 1/s,
Temperature 482 °F		ISO 11443
 446000 cP
@Shear Rate 200 1/s,
Temperature 270 °C		446000 cP
@Shear Rate 200 1/s,
Temperature 518 °F		ISO 11443
 532000 cP
@Shear Rate 200 1/s,
Temperature 260 °C		532000 cP
@Shear Rate 200 1/s,
Temperature 500 °F		ISO 11443
 584000 cP
@Shear Rate 100 1/s,
Temperature 270 °C		584000 cP
@Shear Rate 100 1/s,
Temperature 518 °F		ISO 11443
 634000 cP
@Shear Rate 200 1/s,
Temperature 250 °C		634000 cP
@Shear Rate 200 1/s,
Temperature 482 °F		ISO 11443
 725000 cP
@Shear Rate 100 1/s,
Temperature 260 °C		725000 cP
@Shear Rate 100 1/s,
Temperature 500 °F		ISO 11443
 896000 cP
@Shear Rate 100 1/s,
Temperature 250 °C		896000 cP
@Shear Rate 100 1/s,
Temperature 482 °F		ISO 11443
Linear Mold Shrinkage  0.0020 cm/cm
@Thickness 3.20 mm		0.0020 in/in
@Thickness 0.126 in		Flow
 0.0060 cm/cm
@Thickness 3.20 mm		0.0060 in/in
@Thickness 0.126 in		Transverse
Linear Mold Shrinkage, Flow 0.0040 cm/cm0.0040 in/inParallel; Annealed; ISO 294-4
 0.0030 cm/cm
@Thickness 2.00 mm		0.0030 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0085 cm/cm0.0085 in/inNormal; Annealed; ISO 294-4
 0.0060 cm/cm
@Thickness 2.00 mm		0.0060 in/in
@Thickness 0.0787 in		Normal; ISO 294-4
Melt Index of Compound 10 g/10 min
@Load 2.16 kg,
Temperature 250 °C		10 g/10 min
@Load 4.76 lb,
Temperature 482 °F		cm3/10 min; ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break  23.0 MPa
@Temperature 150 °C		3340 psi
@Temperature 302 °F		ISO 527
 32.0 MPa
@Temperature 120 °C		4640 psi
@Temperature 248 °F		ISO 527
 67.0 MPa
@Temperature 90.0 °C		9720 psi
@Temperature 194 °F		ISO 527
 135 MPa
@Temperature 23.0 °C		19600 psi
@Temperature 73.4 °F		ISO 527
 180 MPa
@Temperature -40.0 °C		26100 psi
@Temperature -40.0 °F		ISO 527
Tensile Strength 131 MPa
@Temperature 23.0 °C		19000 psi
@Temperature 73.4 °F		ASTM D638
Tensile Stress  3.97 MPa
@Strain 0.250 %,
Temperature 150 °C		576 psi
@Strain 0.250 %,
Temperature 302 °F		ISO 527
 7.06 MPa
@Strain 0.120 %,
Temperature 60.0 °C		1020 psi
@Strain 0.120 %,
Temperature 140 °F		ISO 527
 7.18 MPa
@Strain 0.350 %,
Temperature 120 °C		1040 psi
@Strain 0.350 %,
Temperature 248 °F		ISO 527
 7.50 MPa
@Strain 0.510 %,
Temperature 150 °C		1090 psi
@Strain 0.510 %,
Temperature 302 °F		ISO 527
 8.22 MPa
@Strain 0.150 %,
Temperature 90.0 °C		1190 psi
@Strain 0.150 %,
Temperature 194 °F		ISO 527
 8.35 MPa
@Strain 0.110 %,
Temperature 40.0 °C		1210 psi
@Strain 0.110 %,
Temperature 104 °F		ISO 527
 8.63 MPa
@Strain 0.100 %,
Temperature 0.000 °C		1250 psi
@Strain 0.100 %,
Temperature 32.0 °F		ISO 527
 9.17 MPa
@Strain 0.100 %,
Temperature 23.0 °C		1330 psi
@Strain 0.100 %,
Temperature 73.4 °F		ISO 527
 9.43 MPa
@Strain 0.100 %,
Temperature -20.0 °C		1370 psi
@Strain 0.100 %,
Temperature -4.00 °F		ISO 527
 9.86 MPa
@Strain 0.760 %,
Temperature 150 °C		1430 psi
@Strain 0.760 %,
Temperature 302 °F		ISO 527
 11.74 MPa
@Strain 1.02 %,
Temperature 150 °C		1703 psi
@Strain 1.02 %,
Temperature 302 °F		ISO 527
 12.39 MPa
@Strain 0.680 %,
Temperature 120 °C		1797 psi
@Strain 0.680 %,
Temperature 248 °F		ISO 527
 13.13 MPa
@Strain 1.26 %,
Temperature 150 °C		1904 psi
@Strain 1.26 %,
Temperature 302 °F		ISO 527
 14.36 MPa
@Strain 1.52 %,
Temperature 150 °C		2083 psi
@Strain 1.52 %,
Temperature 302 °F		ISO 527
 15.28 MPa
@Strain 1.77 %,
Temperature 150 °C		2216 psi
@Strain 1.77 %,
Temperature 302 °F		ISO 527
 15.33 MPa
@Strain 0.240 %,
Temperature 60.0 °C		2223 psi
@Strain 0.240 %,
Temperature 140 °F		ISO 527
 16.05 MPa
@Strain 1.02 %,
Temperature 120 °C		2328 psi
@Strain 1.02 %,
Temperature 248 °F		ISO 527
 16.08 MPa
@Strain 0.210 %,
Temperature 40.0 °C		2332 psi
@Strain 0.210 %,
Temperature 104 °F		ISO 527
 16.15 MPa
@Strain 2.03 %,
Temperature 150 °C		2342 psi
@Strain 2.03 %,
Temperature 302 °F		ISO 527
 16.44 MPa
@Strain 0.310 %,
Temperature 90.0 °C		2384 psi
@Strain 0.310 %,
Temperature 194 °F		ISO 527
 16.75 MPa
@Strain 0.180 %,
Temperature 0.000 °C		2429 psi
@Strain 0.180 %,
Temperature 32.0 °F		ISO 527
 16.85 MPa
@Strain 2.27 %,
Temperature 150 °C		2444 psi
@Strain 2.27 %,
Temperature 302 °F		ISO 527
 17.49 MPa
@Strain 0.190 %,
Temperature 23.0 °C		2537 psi
@Strain 0.190 %,
Temperature 73.4 °F		ISO 527
 17.5 MPa
@Strain 2.53 %,
Temperature 150 °C		2540 psi
@Strain 2.53 %,
Temperature 302 °F		ISO 527
 18.04 MPa
@Strain 2.78 %,
Temperature 150 °C		2616 psi
@Strain 2.78 %,
Temperature 302 °F		ISO 527
 18.57 MPa
@Strain 3.04 %,
Temperature 150 °C		2693 psi
@Strain 3.04 %,
Temperature 302 °F		ISO 527
 18.69 MPa
@Strain 1.36 %,
Temperature 120 °C		2711 psi
@Strain 1.36 %,
Temperature 248 °F		ISO 527
 19.01 MPa
@Strain 3.28 %,
Temperature 150 °C		2757 psi
@Strain 3.28 %,
Temperature 302 °F		ISO 527
 19.09 MPa
@Strain 0.190 %,
Temperature -20.0 °C		2769 psi
@Strain 0.190 %,
Temperature -4.00 °F		ISO 527
 19.42 MPa
@Strain 3.54 %,
Temperature 150 °C		2817 psi
@Strain 3.54 %,
Temperature 302 °F		ISO 527
 19.78 MPa
@Strain 3.79 %,
Temperature 150 °C		2869 psi
@Strain 3.79 %,
Temperature 302 °F		ISO 527
 20.13 MPa
@Strain 4.05 %,
Temperature 150 °C		2920 psi
@Strain 4.05 %,
Temperature 302 °F		ISO 527
 20.45 MPa
@Strain 4.29 %,
Temperature 150 °C		2966 psi
@Strain 4.29 %,
Temperature 302 °F		ISO 527
 20.72 MPa
@Strain 4.54 %,
Temperature 150 °C		3005 psi
@Strain 4.54 %,
Temperature 302 °F		ISO 527
 20.72 MPa
@Strain 1.69 %,
Temperature 120 °C		3005 psi
@Strain 1.69 %,
Temperature 248 °F		ISO 527
 20.97 MPa
@Strain 4.80 %,
Temperature 150 °C		3041 psi
@Strain 4.80 %,
Temperature 302 °F		ISO 527
 21.19 MPa
@Strain 5.04 %,
Temperature 150 °C		3073 psi
@Strain 5.04 %,
Temperature 302 °F		ISO 527
 21.4 MPa
@Strain 5.30 %,
Temperature 150 °C		3100 psi
@Strain 5.30 %,
Temperature 302 °F		ISO 527
 21.56 MPa
@Strain 5.55 %,
Temperature 150 °C		3127 psi
@Strain 5.55 %,
Temperature 302 °F		ISO 527
 21.65 MPa
@Strain 5.81 %,
Temperature 150 °C		3140 psi
@Strain 5.81 %,
Temperature 302 °F		ISO 527
 21.7 MPa
@Strain 6.05 %,
Temperature 150 °C		3150 psi
@Strain 6.05 %,
Temperature 302 °F		ISO 527
 21.8 MPa
@Strain 6.30 %,
Temperature 150 °C		3160 psi
@Strain 6.30 %,
Temperature 302 °F		ISO 527
 22.33 MPa
@Strain 2.03 %,
Temperature 120 °C		3239 psi
@Strain 2.03 %,
Temperature 248 °F		ISO 527
 22.56 MPa
@Strain 0.350 %,
Temperature 60.0 °C		3272 psi
@Strain 0.350 %,
Temperature 140 °F		ISO 527
 23.49 MPa
@Strain 0.450 %,
Temperature 90.0 °C		3407 psi
@Strain 0.450 %,
Temperature 194 °F		ISO 527
 23.65 MPa
@Strain 2.36 %,
Temperature 120 °C		3430 psi
@Strain 2.36 %,
Temperature 248 °F		ISO 527
 24.51 MPa
@Strain 0.320 %,
Temperature 40.0 °C		3555 psi
@Strain 0.320 %,
Temperature 104 °F		ISO 527
 24.76 MPa
@Strain 2.70 %,
Temperature 120 °C		3591 psi
@Strain 2.70 %,
Temperature 248 °F		ISO 527
 25.57 MPa
@Strain 0.270 %,
Temperature 0.000 °C		3709 psi
@Strain 0.270 %,
Temperature 32.0 °F		ISO 527
 25.7 MPa
@Strain 3.04 %,
Temperature 120 °C		3730 psi
@Strain 3.04 %,
Temperature 248 °F		ISO 527
 26.5 MPa
@Strain 3.37 %,
Temperature 120 °C		3840 psi
@Strain 3.37 %,
Temperature 248 °F		ISO 527
 26.52 MPa
@Strain 0.280 %,
Temperature 23.0 °C		3846 psi
@Strain 0.280 %,
Temperature 73.4 °F		ISO 527
 27.21 MPa
@Strain 3.71 %,
Temperature 120 °C		3946 psi
@Strain 3.71 %,
Temperature 248 °F		ISO 527
 27.85 MPa
@Strain 4.05 %,
Temperature 120 °C		4039 psi
@Strain 4.05 %,
Temperature 248 °F		ISO 527
 28.41 MPa
@Strain 4.38 %,
Temperature 120 °C		4121 psi
@Strain 4.38 %,
Temperature 248 °F		ISO 527
 28.64 MPa
@Strain 0.280 %,
Temperature -20.0 °C		4154 psi
@Strain 0.280 %,
Temperature -4.00 °F		ISO 527
 28.88 MPa
@Strain 4.72 %,
Temperature 120 °C		4189 psi
@Strain 4.72 %,
Temperature 248 °F		ISO 527
 29.31 MPa
@Strain 5.06 %,
Temperature 120 °C		4251 psi
@Strain 5.06 %,
Temperature 248 °F		ISO 527
 29.48 MPa
@Strain 0.600 %,
Temperature 90.0 °C		4276 psi
@Strain 0.600 %,
Temperature 194 °F		ISO 527
 29.68 MPa
@Strain 5.39 %,
Temperature 120 °C		4305 psi
@Strain 5.39 %,
Temperature 248 °F		ISO 527
 30.01 MPa
@Strain 5.73 %,
Temperature 120 °C		4353 psi
@Strain 5.73 %,
Temperature 248 °F		ISO 527
 30.06 MPa
@Strain 0.470 %,
Temperature 60.0 °C		4360 psi
@Strain 0.470 %,
Temperature 140 °F		ISO 527
 30.31 MPa
@Strain 6.07 %,
Temperature 120 °C		4396 psi
@Strain 6.07 %,
Temperature 248 °F		ISO 527
 30.55 MPa
@Strain 6.38 %,
Temperature 120 °C		4431 psi
@Strain 6.38 %,
Temperature 248 °F		ISO 527
 30.76 MPa
@Strain 6.72 %,
Temperature 120 °C		4461 psi
@Strain 6.72 %,
Temperature 248 °F		ISO 527
 30.91 MPa
@Strain 7.06 %,
Temperature 120 °C		4483 psi
@Strain 7.06 %,
Temperature 248 °F		ISO 527
 31.02 MPa
@Strain 7.39 %,
Temperature 120 °C		4499 psi
@Strain 7.39 %,
Temperature 248 °F		ISO 527
 31.07 MPa
@Strain 7.73 %,
Temperature 120 °C		4506 psi
@Strain 7.73 %,
Temperature 248 °F		ISO 527
 32.08 MPa
@Strain 0.420 %,
Temperature 40.0 °C		4653 psi
@Strain 0.420 %,
Temperature 104 °F		ISO 527
 33.29 MPa
@Strain 0.350 %,
Temperature 0.000 °C		4828 psi
@Strain 0.350 %,
Temperature 32.0 °F		ISO 527
 34.6 MPa
@Strain 0.370 %,
Temperature 23.0 °C		5020 psi
@Strain 0.370 %,
Temperature 73.4 °F		ISO 527
 34.62 MPa
@Strain 0.740 %,
Temperature 90.0 °C		5021 psi
@Strain 0.740 %,
Temperature 194 °F		ISO 527
 36.48 MPa
@Strain 0.580 %,
Temperature 60.0 °C		5291 psi
@Strain 0.580 %,
Temperature 140 °F		ISO 527
 37.67 MPa
@Strain 0.370 %,
Temperature -20.0 °C		5464 psi
@Strain 0.370 %,
Temperature -4.00 °F		ISO 527
 39.39 MPa
@Strain 0.900 %,
Temperature 90.0 °C		5713 psi
@Strain 0.900 %,
Temperature 194 °F		ISO 527
 39.7 MPa
@Strain 0.530 %,
Temperature 40.0 °C		5760 psi
@Strain 0.530 %,
Temperature 104 °F		ISO 527
 41.9 MPa
@Strain 0.450 %,
Temperature 0.000 °C		6080 psi
@Strain 0.450 %,
Temperature 32.0 °F		ISO 527
 42.22 MPa
@Strain 0.700 %,
Temperature 60.0 °C		6124 psi
@Strain 0.700 %,
Temperature 140 °F		ISO 527
 43.02 MPa
@Strain 1.04 %,
Temperature 90.0 °C		6240 psi
@Strain 1.04 %,
Temperature 194 °F		ISO 527
 43.22 MPa
@Strain 0.460 %,
Temperature 23.0 °C		6269 psi
@Strain 0.460 %,
Temperature 73.4 °F		ISO 527
 46.15 MPa
@Strain 1.19 %,
Temperature 90.0 °C		6694 psi
@Strain 1.19 %,
Temperature 194 °F		ISO 527
 46.24 MPa
@Strain 0.630 %,
Temperature 40.0 °C		6707 psi
@Strain 0.630 %,
Temperature 104 °F		ISO 527
 46.35 MPa
@Strain 0.460 %,
Temperature -20.0 °C		6723 psi
@Strain 0.460 %,
Temperature -4.00 °F		ISO 527
 48.06 MPa
@Strain 0.820 %,
Temperature 60.0 °C		6971 psi
@Strain 0.820 %,
Temperature 140 °F		ISO 527
 48.94 MPa
@Strain 1.34 %,
Temperature 90.0 °C		7098 psi
@Strain 1.34 %,
Temperature 194 °F		ISO 527
 50.26 MPa
@Strain 0.540 %,
Temperature 0.000 °C		7290 psi
@Strain 0.540 %,
Temperature 32.0 °F		ISO 527
 51.16 MPa
@Strain 1.49 %,
Temperature 90.0 °C		7420 psi
@Strain 1.49 %,
Temperature 194 °F		ISO 527
 51.39 MPa
@Strain 0.560 %,
Temperature 23.0 °C		7454 psi
@Strain 0.560 %,
Temperature 73.4 °F		ISO 527
 52.91 MPa
@Strain 0.930 %,
Temperature 60.0 °C		7674 psi
@Strain 0.930 %,
Temperature 140 °F		ISO 527
 52.94 MPa
@Strain 1.63 %,
Temperature 90.0 °C		7678 psi
@Strain 1.63 %,
Temperature 194 °F		ISO 527
 53.08 MPa
@Strain 0.740 %,
Temperature 40.0 °C		7699 psi
@Strain 0.740 %,
Temperature 104 °F		ISO 527
 54.48 MPa
@Strain 1.78 %,
Temperature 90.0 °C		7902 psi
@Strain 1.78 %,
Temperature 194 °F		ISO 527
 54.92 MPa
@Strain 0.560 %,
Temperature -20.0 °C		7965 psi
@Strain 0.560 %,
Temperature -4.00 °F		ISO 527
 55.89 MPa
@Strain 1.93 %,
Temperature 90.0 °C		8106 psi
@Strain 1.93 %,
Temperature 194 °F		ISO 527
 56.98 MPa
@Strain 2.08 %,
Temperature 90.0 °C		8264 psi
@Strain 2.08 %,
Temperature 194 °F		ISO 527
 57.59 MPa
@Strain 0.620 %,
Temperature 0.000 °C		8353 psi
@Strain 0.620 %,
Temperature 32.0 °F		ISO 527
 57.8 MPa
@Strain 1.05 %,
Temperature 60.0 °C		8380 psi
@Strain 1.05 %,
Temperature 140 °F		ISO 527
 57.91 MPa
@Strain 2.22 %,
Temperature 90.0 °C		8399 psi
@Strain 2.22 %,
Temperature 194 °F		ISO 527
 58.28 MPa
@Strain 0.650 %,
Temperature 23.0 °C		8453 psi
@Strain 0.650 %,
Temperature 73.4 °F		ISO 527
 58.68 MPa
@Strain 0.830 %,
Temperature 40.0 °C		8511 psi
@Strain 0.830 %,
Temperature 104 °F		ISO 527
 58.68 MPa
@Strain 2.37 %,
Temperature 90.0 °C		8511 psi
@Strain 2.37 %,
Temperature 194 °F		ISO 527
 59.42 MPa
@Strain 2.53 %,
Temperature 90.0 °C		8618 psi
@Strain 2.53 %,
Temperature 194 °F		ISO 527
 59.96 MPa
@Strain 2.67 %,
Temperature 90.0 °C		8696 psi
@Strain 2.67 %,
Temperature 194 °F		ISO 527
 60.41 MPa
@Strain 2.81 %,
Temperature 90.0 °C		8762 psi
@Strain 2.81 %,
Temperature 194 °F		ISO 527
 60.78 MPa
@Strain 2.97 %,
Temperature 90.0 °C		8815 psi
@Strain 2.97 %,
Temperature 194 °F		ISO 527
 61.08 MPa
@Strain 3.12 %,
Temperature 90.0 °C		8859 psi
@Strain 3.12 %,
Temperature 194 °F		ISO 527
 61.29 MPa
@Strain 3.26 %,
Temperature 90.0 °C		8889 psi
@Strain 3.26 %,
Temperature 194 °F		ISO 527
 61.35 MPa
@Strain 3.41 %,
Temperature 90.0 °C		8898 psi
@Strain 3.41 %,
Temperature 194 °F		ISO 527
 61.43 MPa
@Strain 3.56 %,
Temperature 90.0 °C		8910 psi
@Strain 3.56 %,
Temperature 194 °F		ISO 527
 61.5 MPa
@Strain 3.70 %,
Temperature 90.0 °C		8920 psi
@Strain 3.70 %,
Temperature 194 °F		ISO 527
 61.65 MPa
@Strain 1.16 %,
Temperature 60.0 °C		8942 psi
@Strain 1.16 %,
Temperature 140 °F		ISO 527
 63.18 MPa
@Strain 0.650 %,
Temperature -20.0 °C		9164 psi
@Strain 0.650 %,
Temperature -4.00 °F		ISO 527
 64.56 MPa
@Strain 0.940 %,
Temperature 40.0 °C		9364 psi
@Strain 0.940 %,
Temperature 104 °F		ISO 527
 65.44 MPa
@Strain 0.710 %,
Temperature 0.000 °C		9491 psi
@Strain 0.710 %,
Temperature 32.0 °F		ISO 527
 65.6 MPa
@Strain 1.29 %,
Temperature 60.0 °C		9510 psi
@Strain 1.29 %,
Temperature 140 °F		ISO 527
 65.67 MPa
@Strain 0.740 %,
Temperature 23.0 °C		9525 psi
@Strain 0.740 %,
Temperature 73.4 °F		ISO 527
 68.77 MPa
@Strain 1.40 %,
Temperature 60.0 °C		9974 psi
@Strain 1.40 %,
Temperature 140 °F		ISO 527
 69.47 MPa
@Strain 1.04 %,
Temperature 40.0 °C		10080 psi
@Strain 1.04 %,
Temperature 104 °F		ISO 527
 71.03 MPa
@Strain 0.740 %,
Temperature -20.0 °C		10300 psi
@Strain 0.740 %,
Temperature -4.00 °F		ISO 527
 71.58 MPa
@Strain 1.51 %,
Temperature 60.0 °C		10380 psi
@Strain 1.51 %,
Temperature 140 °F		ISO 527
 72.25 MPa
@Strain 0.790 %,
Temperature 0.000 °C		10480 psi
@Strain 0.790 %,
Temperature 32.0 °F		ISO 527
 72.75 MPa
@Strain 0.840 %,
Temperature 23.0 °C		10550 psi
@Strain 0.840 %,
Temperature 73.4 °F		ISO 527
 74.27 MPa
@Strain 1.63 %,
Temperature 60.0 °C		10770 psi
@Strain 1.63 %,
Temperature 140 °F		ISO 527
 74.48 MPa
@Strain 1.15 %,
Temperature 40.0 °C		10800 psi
@Strain 1.15 %,
Temperature 104 °F		ISO 527
 76.5 MPa
@Strain 1.74 %,
Temperature 60.0 °C		11100 psi
@Strain 1.74 %,
Temperature 140 °F		ISO 527
 78.57 MPa
@Strain 1.87 %,
Temperature 60.0 °C		11400 psi
@Strain 1.87 %,
Temperature 140 °F		ISO 527
 78.69 MPa
@Strain 1.25 %,
Temperature 40.0 °C		11410 psi
@Strain 1.25 %,
Temperature 104 °F		ISO 527
 78.84 MPa
@Strain 0.920 %,
Temperature 23.0 °C		11430 psi
@Strain 0.920 %,
Temperature 73.4 °F		ISO 527
 78.9 MPa
@Strain 0.830 %,
Temperature -20.0 °C		11400 psi
@Strain 0.830 %,
Temperature -4.00 °F		ISO 527
 79.58 MPa
@Strain 0.890 %,
Temperature 0.000 °C		11540 psi
@Strain 0.890 %,
Temperature 32.0 °F		ISO 527
 80.22 MPa
@Strain 1.98 %,
Temperature 60.0 °C		11630 psi
@Strain 1.98 %,
Temperature 140 °F		ISO 527
 81.64 MPa
@Strain 2.09 %,
Temperature 60.0 °C		11840 psi
@Strain 2.09 %,
Temperature 140 °F		ISO 527
 82.9 MPa
@Strain 1.36 %,
Temperature 40.0 °C		12000 psi
@Strain 1.36 %,
Temperature 104 °F		ISO 527
 82.98 MPa
@Strain 2.21 %,
Temperature 60.0 °C		12040 psi
@Strain 2.21 %,
Temperature 140 °F		ISO 527
 83.96 MPa
@Strain 2.32 %,
Temperature 60.0 °C		12180 psi
@Strain 2.32 %,
Temperature 140 °F		ISO 527
 84.85 MPa
@Strain 2.45 %,
Temperature 60.0 °C		12310 psi
@Strain 2.45 %,
Temperature 140 °F		ISO 527
 85.21 MPa
@Strain 1.02 %,
Temperature 23.0 °C		12360 psi
@Strain 1.02 %,
Temperature 73.4 °F		ISO 527
 85.49 MPa
@Strain 2.56 %,
Temperature 60.0 °C		12400 psi
@Strain 2.56 %,
Temperature 140 °F		ISO 527
 85.96 MPa
@Strain 2.67 %,
Temperature 60.0 °C		12470 psi
@Strain 2.67 %,
Temperature 140 °F		ISO 527
 86.31 MPa
@Strain 2.79 %,
Temperature 60.0 °C		12520 psi
@Strain 2.79 %,
Temperature 140 °F		ISO 527
 86.4 MPa
@Strain 2.90 %,
Temperature 60.0 °C		12500 psi
@Strain 2.90 %,
Temperature 140 °F		ISO 527
 86.45 MPa
@Strain 0.920 %,
Temperature -20.0 °C		12540 psi
@Strain 0.920 %,
Temperature -4.00 °F		ISO 527
 86.52 MPa
@Strain 0.980 %,
Temperature 0.000 °C		12550 psi
@Strain 0.980 %,
Temperature 32.0 °F		ISO 527
 86.74 MPa
@Strain 1.47 %,
Temperature 40.0 °C		12580 psi
@Strain 1.47 %,
Temperature 104 °F		ISO 527
 89.84 MPa
@Strain 1.56 %,
Temperature 40.0 °C		13030 psi
@Strain 1.56 %,
Temperature 104 °F		ISO 527
 90.4 MPa
@Strain 1.10 %,
Temperature 23.0 °C		13100 psi
@Strain 1.10 %,
Temperature 73.4 °F		ISO 527
 92.56 MPa
@Strain 1.06 %,
Temperature 0.000 °C		13420 psi
@Strain 1.06 %,
Temperature 32.0 °F		ISO 527
 92.96 MPa
@Strain 1.67 %,
Temperature 40.0 °C		13480 psi
@Strain 1.67 %,
Temperature 104 °F		ISO 527
 93.63 MPa
@Strain 1.01 %,
Temperature -20.0 °C		13580 psi
@Strain 1.01 %,
Temperature -4.00 °F		ISO 527
 95.47 MPa
@Strain 1.77 %,
Temperature 40.0 °C		13850 psi
@Strain 1.77 %,
Temperature 104 °F		ISO 527
 95.98 MPa
@Strain 1.20 %,
Temperature 23.0 °C		13920 psi
@Strain 1.20 %,
Temperature 73.4 °F		ISO 527
 97.93 MPa
@Strain 1.88 %,
Temperature 40.0 °C		14200 psi
@Strain 1.88 %,
Temperature 104 °F		ISO 527
 99.02 MPa
@Strain 1.15 %,
Temperature 0.000 °C		14360 psi
@Strain 1.15 %,
Temperature 32.0 °F		ISO 527
 99.83 MPa
@Strain 1.98 %,
Temperature 40.0 °C		14480 psi
@Strain 1.98 %,
Temperature 104 °F		ISO 527
 100.59 MPa
@Strain 1.11 %,
Temperature -20.0 °C		14589 psi
@Strain 1.11 %,
Temperature -4.00 °F		ISO 527
 101.03 MPa
@Strain 1.30 %,
Temperature 23.0 °C		14653 psi
@Strain 1.30 %,
Temperature 73.4 °F		ISO 527
 101.68 MPa
@Strain 2.09 %,
Temperature 40.0 °C		14747 psi
@Strain 2.09 %,
Temperature 104 °F		ISO 527
 103.06 MPa
@Strain 2.19 %,
Temperature 40.0 °C		14948 psi
@Strain 2.19 %,
Temperature 104 °F		ISO 527
 104.27 MPa
@Strain 2.29 %,
Temperature 40.0 °C		15123 psi
@Strain 2.29 %,
Temperature 104 °F		ISO 527
 104.34 MPa
@Strain 1.23 %,
Temperature 0.000 °C		15133 psi
@Strain 1.23 %,
Temperature 32.0 °F		ISO 527
 105.2 MPa
@Strain 2.39 %,
Temperature 40.0 °C		15260 psi
@Strain 2.39 %,
Temperature 104 °F		ISO 527
 105.21 MPa
@Strain 1.38 %,
Temperature 23.0 °C		15259 psi
@Strain 1.38 %,
Temperature 73.4 °F		ISO 527
 105.92 MPa
@Strain 2.50 %,
Temperature 40.0 °C		15362 psi
@Strain 2.50 %,
Temperature 104 °F		ISO 527
 106.3 MPa
@Strain 2.60 %,
Temperature 40.0 °C		15420 psi
@Strain 2.60 %,
Temperature 104 °F		ISO 527
 107.31 MPa
@Strain 1.20 %,
Temperature -20.0 °C		15564 psi
@Strain 1.20 %,
Temperature -4.00 °F		ISO 527
 109.31 MPa
@Strain 1.48 %,
Temperature 23.0 °C		15854 psi
@Strain 1.48 %,
Temperature 73.4 °F		ISO 527
 110.09 MPa
@Strain 1.33 %,
Temperature 0.000 °C		15967 psi
@Strain 1.33 %,
Temperature 32.0 °F		ISO 527
 113.06 MPa
@Strain 1.57 %,
Temperature 23.0 °C		16398 psi
@Strain 1.57 %,
Temperature 73.4 °F		ISO 527
 113.61 MPa
@Strain 1.29 %,
Temperature -20.0 °C		16478 psi
@Strain 1.29 %,
Temperature -4.00 °F		ISO 527
 115.88 MPa
@Strain 1.42 %,
Temperature 0.000 °C		16807 psi
@Strain 1.42 %,
Temperature 32.0 °F		ISO 527
 116.02 MPa
@Strain 1.66 %,
Temperature 23.0 °C		16827 psi
@Strain 1.66 %,
Temperature 73.4 °F		ISO 527
 119.01 MPa
@Strain 1.75 %,
Temperature 23.0 °C		17261 psi
@Strain 1.75 %,
Temperature 73.4 °F		ISO 527
 119.48 MPa
@Strain 1.38 %,
Temperature -20.0 °C		17329 psi
@Strain 1.38 %,
Temperature -4.00 °F		ISO 527
 120.28 MPa
@Strain 1.50 %,
Temperature 0.000 °C		17445 psi
@Strain 1.50 %,
Temperature 32.0 °F		ISO 527
 121.36 MPa
@Strain 1.84 %,
Temperature 23.0 °C		17602 psi
@Strain 1.84 %,
Temperature 73.4 °F		ISO 527
 123.64 MPa
@Strain 1.94 %,
Temperature 23.0 °C		17932 psi
@Strain 1.94 %,
Temperature 73.4 °F		ISO 527
 124.94 MPa
@Strain 1.59 %,
Temperature 0.000 °C		18121 psi
@Strain 1.59 %,
Temperature 32.0 °F		ISO 527
 125.12 MPa
@Strain 1.47 %,
Temperature -20.0 °C		18147 psi
@Strain 1.47 %,
Temperature -4.00 °F		ISO 527
 125.56 MPa
@Strain 2.03 %,
Temperature 23.0 °C		18211 psi
@Strain 2.03 %,
Temperature 73.4 °F		ISO 527
 126.98 MPa
@Strain 2.12 %,
Temperature 23.0 °C		18417 psi
@Strain 2.12 %,
Temperature 73.4 °F		ISO 527
 128.44 MPa
@Strain 2.21 %,
Temperature 23.0 °C		18629 psi
@Strain 2.21 %,
Temperature 73.4 °F		ISO 527
 128.73 MPa
@Strain 1.67 %,
Temperature 0.000 °C		18671 psi
@Strain 1.67 %,
Temperature 32.0 °F		ISO 527
 129.1 MPa
@Strain 2.30 %,
Temperature 23.0 °C		18720 psi
@Strain 2.30 %,
Temperature 73.4 °F		ISO 527
 131.02 MPa
@Strain 1.57 %,
Temperature -20.0 °C		19003 psi
@Strain 1.57 %,
Temperature -4.00 °F		ISO 527
 132.68 MPa
@Strain 1.77 %,
Temperature 0.000 °C		19244 psi
@Strain 1.77 %,
Temperature 32.0 °F		ISO 527
 135.9 MPa
@Strain 1.67 %,
Temperature -20.0 °C		19710 psi
@Strain 1.67 %,
Temperature -4.00 °F		ISO 527
 136.46 MPa
@Strain 1.86 %,
Temperature 0.000 °C		19792 psi
@Strain 1.86 %,
Temperature 32.0 °F		ISO 527
 139.24 MPa
@Strain 1.94 %,
Temperature 0.000 °C		20195 psi
@Strain 1.94 %,
Temperature 32.0 °F		ISO 527
 140.47 MPa
@Strain 1.76 %,
Temperature -20.0 °C		20373 psi
@Strain 1.76 %,
Temperature -4.00 °F		ISO 527
 142.12 MPa
@Strain 2.03 %,
Temperature 0.000 °C		20613 psi
@Strain 2.03 %,
Temperature 32.0 °F		ISO 527
 144.47 MPa
@Strain 2.11 %,
Temperature 0.000 °C		20954 psi
@Strain 2.11 %,
Temperature 32.0 °F		ISO 527
 146.06 MPa
@Strain 1.85 %,
Temperature -20.0 °C		21184 psi
@Strain 1.85 %,
Temperature -4.00 °F		ISO 527
 146.88 MPa
@Strain 2.21 %,
Temperature 0.000 °C		21303 psi
@Strain 2.21 %,
Temperature 32.0 °F		ISO 527
 150.03 MPa
@Strain 1.94 %,
Temperature -20.0 °C		21760 psi
@Strain 1.94 %,
Temperature -4.00 °F		ISO 527
 153.56 MPa
@Strain 2.03 %,
Temperature -20.0 °C		22272 psi
@Strain 2.03 %,
Temperature -4.00 °F		ISO 527
 156.76 MPa
@Strain 2.12 %,
Temperature -20.0 °C		22736 psi
@Strain 2.12 %,
Temperature -4.00 °F		ISO 527
 159.41 MPa
@Strain 2.22 %,
Temperature -20.0 °C		23121 psi
@Strain 2.22 %,
Temperature -4.00 °F		ISO 527
 161.7 MPa
@Strain 2.30 %,
Temperature -20.0 °C		23450 psi
@Strain 2.30 %,
Temperature -4.00 °F		ISO 527
Elongation at Break  2.0 %
@Temperature 23.0 °C		2.0 %
@Temperature 73.4 °F		ASTM D638
 2.3 %
@Temperature 23.0 °C		2.3 %
@Temperature 73.4 °F		ISO 527
 2.4 %
@Temperature -40.0 °C		2.4 %
@Temperature -40.0 °F		ISO 527
 3.2 %
@Temperature 90.0 °C		3.2 %
@Temperature 194 °F		ISO 527
 4.3 %
@Temperature 120 °C		4.3 %
@Temperature 248 °F		ISO 527
 5.5 %
@Temperature 150 °C		5.5 %
@Temperature 302 °F		ISO 527
Tensile Modulus  1.527 GPa
@Temperature 150 °C		221.5 ksi
@Temperature 302 °F		DAM; ISO 527
 1.90 GPa
@Temperature 150 °C		276 ksi
@Temperature 302 °F		ISO 527
 2.021 GPa
@Temperature 120 °C		293.1 ksi
@Temperature 248 °F		DAM; ISO 527
 2.30 GPa
@Temperature 120 °C		334 ksi
@Temperature 248 °F		ISO 527
 5.254 GPa
@Temperature 90.0 °C		762.0 ksi
@Temperature 194 °F		DAM; ISO 527
 5.70 GPa
@Temperature 90.0 °C		827 ksi
@Temperature 194 °F		ISO 527
 6.468 GPa
@Temperature 60.0 °C		938.1 ksi
@Temperature 140 °F		DAM; ISO 527
 7.427 GPa
@Temperature 40.0 °C		1077 ksi
@Temperature 104 °F		DAM; ISO 527
 9.00 GPa
@Temperature 23.0 °C		1310 ksi
@Temperature 73.4 °F		ASTM D638
 9.753 GPa
@Temperature 0.000 °C		1415 ksi
@Temperature 32.0 °F		DAM; ISO 527
 9.80 GPa
@Temperature 23.0 °C		1420 ksi
@Temperature 73.4 °F		ISO 527
 10.3 GPa
@Temperature -40.0 °C		1490 ksi
@Temperature -40.0 °F		ISO 527
 10.439 GPa
@Temperature -20.0 °C		1514.1 ksi
@Temperature -4.00 °F		DAM; ISO 527
Flexural Strength 179 MPa
@Temperature 23.0 °C		26000 psi
@Temperature 73.4 °F		ASTM D790
Flexural Modulus  1.30 GPa
@Temperature 150 °C		189 ksi
@Temperature 302 °F		ISO 178
 1.60 GPa
@Temperature 120 °C		232 ksi
@Temperature 248 °F		ISO 178
 4.00 GPa
@Temperature 90.0 °C		580 ksi
@Temperature 194 °F		ISO 178
 8.275 GPa
@Temperature 23.0 °C		1200 ksi
@Temperature 73.4 °F		ASTM D790
 8.40 GPa
@Temperature 23.0 °C		1220 ksi
@Temperature 73.4 °F		ISO 178
 9.60 GPa
@Temperature -40.0 °C		1390 ksi
@Temperature -40.0 °F		ISO 178
Izod Impact, Notched  0.960 J/cm
@Temperature -40.0 °C		1.80 ft-lb/in
@Temperature -40.0 °F		ASTM D256
 0.960 J/cm
@Temperature 23.0 °C		1.80 ft-lb/in
@Temperature 73.4 °F		ASTM D256
Izod Impact, Unnotched  7.36 J/cm
@Temperature -40.0 °C		13.8 ft-lb/in
@Temperature -40.0 °F		ASTM D4812
 9.34 J/cm
@Temperature 23.0 °C		17.5 ft-lb/in
@Temperature 73.4 °F		ASTM D4812
Izod Impact, Notched (ISO)  7.00 kJ/m²
@Temperature -40.0 °C		3.33 ft-lb/in²
@Temperature -40.0 °F		ISO 180/1A
 7.00 kJ/m²
@Temperature 23.0 °C		3.33 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1A
Izod Impact, Unnotched (ISO)  45.0 kJ/m²
@Temperature -40.0 °C		21.4 ft-lb/in²
@Temperature -40.0 °F		ISO 180/1U
 45.0 kJ/m²
@Temperature 23.0 °C		21.4 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1U
Charpy Impact Unnotched  5.00 J/cm²
@Temperature -40.0 °C		23.8 ft-lb/in²
@Temperature -40.0 °F		ISO 179/1eU
 5.50 J/cm²
@Temperature 23.0 °C		26.2 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched  0.900 J/cm²
@Temperature 23.0 °C		4.28 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
 0.900 J/cm²
@Temperature -30.0 °C		4.28 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 0.900 J/cm²
@Temperature -40.0 °C		4.28 ft-lb/in²
@Temperature -40.0 °F		ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 3.20e+16 ohm-cm
@Temperature 23.0 °C		3.20e+16 ohm-cm
@Temperature 73.4 °F		ASTM D257
Surface Resistance  >= 1.00e+15 ohm
@Temperature 23.0 °C		>= 1.00e+15 ohm
@Temperature 73.4 °F		IEC 60093
 1.20e+15 ohm
@Temperature 23.0 °C		1.20e+15 ohm
@Temperature 73.4 °F		ASTM D257
Dielectric Constant  3.4
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.4
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		ASTM D150
 3.5
@Frequency 1000 Hz,
Temperature 23.0 °C		3.5
@Frequency 1000 Hz,
Temperature 73.4 °F		ASTM D150
Dielectric Strength 23.0 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C		584 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F		Short Time; ASTM D149
Dissipation Factor  0.0030
@Frequency 1000 Hz,
Temperature 23.0 °C		0.0030
@Frequency 1000 Hz,
Temperature 73.4 °F		ASTM D150
 0.013
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.013
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		ASTM D150
Comparative Tracking Index  450 V
@Temperature 23.0 °C		450 V
@Temperature 73.4 °F		UL 746A
 550 V
@Temperature 23.0 °C		550 V
@Temperature 73.4 °F		IEC 60112
 
Thermal PropertiesMetricEnglishComments
Melting Point 225 °C437 °FASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 215 °C419 °FASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 185 °C365 °FISO 75-1/-2
 190 °C374 °FASTM D648
UL RTI, Electrical  130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical with Impact  125 °C
@Thickness 1.50 mm		257 °F
@Thickness 0.0591 in		UL 746B
 125 °C
@Thickness 0.750 mm		257 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical without Impact  130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
 130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
Flammability, UL94  HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		IEC 60695-11-10
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		UL94
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		IEC 60695-11-10
Glow Wire Test  700 °C
@Thickness 1.50 mm		1290 °F
@Thickness 0.0591 in		IEC 60695-2-12
 700 °C
@Thickness 0.750 mm		1290 °F
@Thickness 0.0295 in		IEC 60695-2-12
 725 °C
@Thickness 1.50 mm		1340 °F
@Thickness 0.0591 in		Ignition; IEC 60695-2-13
 725 °C
@Thickness 0.750 mm		1340 °F
@Thickness 0.0295 in		Ignition; IEC 60695-2-13
 775 °C
@Thickness 3.00 mm		1430 °F
@Thickness 0.118 in		IEC 60695-2-12
 800 °C
@Thickness 3.00 mm		1470 °F
@Thickness 0.118 in		Ignition; IEC 60695-2-13
 
Processing PropertiesMetricEnglishComments
Melt Temperature 225 °C437 °F10°C/min; ISO 11357-1/-3
 250 °C482 °FOptimum
 240 - 260 °C464 - 500 °F
Mold Temperature 80.0 °C176 °Foptimum
 30.0 - 130 °C86.0 - 266 °F
Drying Temperature 110 - 130 °C230 - 266 °F
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hour
Moisture Content <= 0.040 %<= 0.040 %
 
Descriptive Properties
AdditiveLubricant
AppearanceNatural Color
Drying RecommendedYes
FeaturesAppearance, Pleasing Surface
 Chemical Resistance, Good
 Dimensional Stability, Good
 Moisture Absorption, Low
 Processability, Good
 Warp Resistant
 Warpage, Low
FillerGlass fiber reinforcement
FormsPellets
GenericPBT Alloy
Material StatusCurrent
Part Marking Code>PBT+SAN-GF30<ISO 11469
Polymer FamilyPolyester
Polymer TypePBT
Processing MethodInjection Molding
Product CategoryGlass Reinforced Resins
 Low Warp Resins
Region Available - GlobalYes
Resin IdentificationPBT+SAN-GF30ISO 1043
RoHS ComplianceContact Manufacturer
Ultrasonic WeldableYes
UsesAutomotive Applications
 Housings
 Industrial Applications

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38047.html

免责声明: 本文 DuPont Performance Polymers Crastin® LW9330 NC010 PBT 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4