塑胶原料之家
  1. 首页
  2. 英文物性
  3. PBT
  4. DuPont Performance Polymers Crastin® LW9030 NC010 PBT

DuPont Performance Polymers Crastin® LW9030 NC010 PBT

DuPont Performance Polymers Crastin® LW9030 NC010 PBT 物性表: DuPont Performance Polymers Crastin® LW9030 NC010 PBT物性表及特性介绍,DuPont Performance Polymers Crastin® LW9030 NC010 PBT注塑参数详情,如需DuPont Performance Polymers Crastin® LW9030 NC010 PBT下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.44
  • 吸水率 [%]: 0.24
  • 缺口冲击强度: 8.0
  • 弯曲模量 [MPa]: 8.50
  • 热变形温度 [℃]: 215.0
 
Physical PropertiesMetricEnglishComments
Density 1.44 g/cc0.0520 lb/in³ISO 1183
Filler Content 30 %30 %
Water Absorption  0.24 %
@Temperature 23.0 °C		0.24 %
@Temperature 73.4 °F		Equilibrium 50%RH; ISO 62, Similar to
 0.72 %
@Temperature 23.0 °C		0.72 %
@Temperature 73.4 °F		Saturation, immersed; ISO 62, Similar to
Viscosity  43000 cP
@Shear Rate 10000 1/s,
Temperature 260 °C		43000 cP
@Shear Rate 10000 1/s,
Temperature 500 °F		ISO 11443
 49000 cP
@Shear Rate 10000 1/s,
Temperature 250 °C		49000 cP
@Shear Rate 10000 1/s,
Temperature 482 °F		ISO 11443
 57000 cP
@Shear Rate 10000 1/s,
Temperature 240 °C		57000 cP
@Shear Rate 10000 1/s,
Temperature 464 °F		ISO 11443
 67000 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		67000 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		ISO 11443
 77000 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		77000 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		ISO 11443
 89000 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		89000 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		ISO 11443
 120000 cP
@Shear Rate 2000 1/s,
Temperature 260 °C		120000 cP
@Shear Rate 2000 1/s,
Temperature 500 °F		ISO 11443
 138000 cP
@Shear Rate 2000 1/s,
Temperature 250 °C		138000 cP
@Shear Rate 2000 1/s,
Temperature 482 °F		ISO 11443
 160000 cP
@Shear Rate 2000 1/s,
Temperature 240 °C		160000 cP
@Shear Rate 2000 1/s,
Temperature 464 °F		ISO 11443
 185000 cP
@Shear Rate 1000 1/s,
Temperature 260 °C		185000 cP
@Shear Rate 1000 1/s,
Temperature 500 °F		ISO 11443
 213000 cP
@Shear Rate 1000 1/s,
Temperature 250 °C		213000 cP
@Shear Rate 1000 1/s,
Temperature 482 °F		ISO 11443
 249000 cP
@Shear Rate 1000 1/s,
Temperature 240 °C		249000 cP
@Shear Rate 1000 1/s,
Temperature 464 °F		ISO 11443
 278000 cP
@Shear Rate 500 1/s,
Temperature 260 °C		278000 cP
@Shear Rate 500 1/s,
Temperature 500 °F		ISO 11443
 325000 cP
@Shear Rate 500 1/s,
Temperature 250 °C		325000 cP
@Shear Rate 500 1/s,
Temperature 482 °F		ISO 11443
 383000 cP
@Shear Rate 500 1/s,
Temperature 240 °C		383000 cP
@Shear Rate 500 1/s,
Temperature 464 °F		ISO 11443
 613000 cP
@Shear Rate 100 1/s,
Temperature 260 °C		613000 cP
@Shear Rate 100 1/s,
Temperature 500 °F		ISO 11443
 763000 cP
@Shear Rate 100 1/s,
Temperature 250 °C		763000 cP
@Shear Rate 100 1/s,
Temperature 482 °F		ISO 11443
 947000 cP
@Shear Rate 100 1/s,
Temperature 240 °C		947000 cP
@Shear Rate 100 1/s,
Temperature 464 °F		ISO 11443
Linear Mold Shrinkage 0.0020 cm/cm0.0020 in/inFlow
 0.0050 cm/cm0.0050 in/inTransverse
Linear Mold Shrinkage, Flow 0.0040 cm/cm0.0040 in/inParallel; Annealed; ISO 294-4
 0.0025 cm/cm
@Thickness 2.00 mm		0.0025 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0095 cm/cm0.0095 in/inNormal; Annealed; ISO 294-4
 0.0065 cm/cm
@Thickness 2.00 mm		0.0065 in/in
@Thickness 0.0787 in		Normal; ISO 294-4
Melt Index of Compound 10 g/10 min
@Load 5.00 kg,
Temperature 250 °C		10 g/10 min
@Load 11.0 lb,
Temperature 482 °F		cm3/10 min; ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 130 MPa
@Temperature 23.0 °C		18900 psi
@Temperature 73.4 °F		ISO 527
Tensile Stress  3.26 MPa
@Strain 0.250 %,
Temperature 160 °C		473 psi
@Strain 0.250 %,
Temperature 320 °F		ISO 527
 5.06 MPa
@Strain 0.250 %,
Temperature 120 °C		734 psi
@Strain 0.250 %,
Temperature 248 °F		ISO 527
 6.25 MPa
@Strain 0.500 %,
Temperature 160 °C		906 psi
@Strain 0.500 %,
Temperature 320 °F		ISO 527
 9.75 MPa
@Strain 0.500 %,
Temperature 120 °C		1410 psi
@Strain 0.500 %,
Temperature 248 °F		ISO 527
 10.8 MPa
@Strain 1.00 %,
Temperature 160 °C		1570 psi
@Strain 1.00 %,
Temperature 320 °F		ISO 527
 11.0 MPa
@Strain 0.250 %,
Temperature 100 °C		1600 psi
@Strain 0.250 %,
Temperature 212 °F		ISO 527
 13.4 MPa
@Strain 1.50 %,
Temperature 160 °C		1940 psi
@Strain 1.50 %,
Temperature 320 °F		ISO 527
 14.9 MPa
@Strain 2.00 %,
Temperature 160 °C		2160 psi
@Strain 2.00 %,
Temperature 320 °F		ISO 527
 15.1 MPa
@Strain 0.250 %,
Temperature 80.0 °C		2190 psi
@Strain 0.250 %,
Temperature 176 °F		ISO 527
 16.0 MPa
@Strain 2.50 %,
Temperature 160 °C		2320 psi
@Strain 2.50 %,
Temperature 320 °F		ISO 527
 16.9 MPa
@Strain 1.00 %,
Temperature 120 °C		2450 psi
@Strain 1.00 %,
Temperature 248 °F		ISO 527
 17.0 MPa
@Strain 3.00 %,
Temperature 160 °C		2470 psi
@Strain 3.00 %,
Temperature 320 °F		Break; ISO 527
 17.1 MPa
@Strain 0.250 %,
Temperature 60.0 °C		2480 psi
@Strain 0.250 %,
Temperature 140 °F		ISO 527
 21.1 MPa
@Strain 1.50 %,
Temperature 120 °C		3060 psi
@Strain 1.50 %,
Temperature 248 °F		ISO 527
 21.3 MPa
@Strain 0.500 %,
Temperature 100 °C		3090 psi
@Strain 0.500 %,
Temperature 212 °F		ISO 527
 21.8 MPa
@Strain 0.250 %,
Temperature 40.0 °C		3160 psi
@Strain 0.250 %,
Temperature 104 °F		ISO 527
 23.5 MPa
@Strain 2.00 %,
Temperature 120 °C		3410 psi
@Strain 2.00 %,
Temperature 248 °F		ISO 527
 23.9 MPa
@Strain 0.250 %,
Temperature 23.0 °C		3470 psi
@Strain 0.250 %,
Temperature 73.4 °F		ISO 527
 25.3 MPa
@Strain 2.50 %,
Temperature 120 °C		3670 psi
@Strain 2.50 %,
Temperature 248 °F		ISO 527
 25.6 MPa
@Strain 0.250 %,
Temperature 0.000 °C		3710 psi
@Strain 0.250 %,
Temperature 32.0 °F		ISO 527
 25.9 MPa
@Strain 0.250 %,
Temperature -20.0 °C		3760 psi
@Strain 0.250 %,
Temperature -4.00 °F		ISO 527
 27.2 MPa
@Strain 3.00 %,
Temperature 120 °C		3950 psi
@Strain 3.00 %,
Temperature 248 °F		Break; ISO 527
 27.3 MPa
@Strain 0.250 %,
Temperature -40.0 °C		3960 psi
@Strain 0.250 %,
Temperature -40.0 °F		ISO 527
 28.9 MPa
@Strain 0.500 %,
Temperature 80.0 °C		4190 psi
@Strain 0.500 %,
Temperature 176 °F		ISO 527
 33.1 MPa
@Strain 0.500 %,
Temperature 60.0 °C		4800 psi
@Strain 0.500 %,
Temperature 140 °F		ISO 527
 35.9 MPa
@Strain 1.00 %,
Temperature 100 °C		5210 psi
@Strain 1.00 %,
Temperature 212 °F		ISO 527
 42.3 MPa
@Strain 0.500 %,
Temperature 40.0 °C		6140 psi
@Strain 0.500 %,
Temperature 104 °F		ISO 527
 42.7 MPa
@Strain 1.50 %,
Temperature 100 °C		6190 psi
@Strain 1.50 %,
Temperature 212 °F		ISO 527
 45.5 MPa
@Strain 2.00 %,
Temperature 100 °C		6600 psi
@Strain 2.00 %,
Temperature 212 °F		ISO 527
 46.5 MPa
@Strain 0.500 %,
Temperature 23.0 °C		6740 psi
@Strain 0.500 %,
Temperature 73.4 °F		ISO 527
 47.3 MPa
@Strain 2.50 %,
Temperature 100 °C		6860 psi
@Strain 2.50 %,
Temperature 212 °F		ISO 527
 49.4 MPa
@Strain 1.00 %,
Temperature 80.0 °C		7160 psi
@Strain 1.00 %,
Temperature 176 °F		ISO 527
 49.5 MPa
@Strain 3.00 %,
Temperature 100 °C		7180 psi
@Strain 3.00 %,
Temperature 212 °F		Break; ISO 527
 49.8 MPa
@Strain 0.500 %,
Temperature 0.000 °C		7220 psi
@Strain 0.500 %,
Temperature 32.0 °F		ISO 527
 50.8 MPa
@Strain 0.500 %,
Temperature -20.0 °C		7370 psi
@Strain 0.500 %,
Temperature -4.00 °F		ISO 527
 53.1 MPa
@Strain 0.500 %,
Temperature -40.0 °C		7700 psi
@Strain 0.500 %,
Temperature -40.0 °F		ISO 527
 57.8 MPa
@Strain 1.00 %,
Temperature 60.0 °C		8380 psi
@Strain 1.00 %,
Temperature 140 °F		ISO 527
 60.4 MPa
@Strain 1.50 %,
Temperature 80.0 °C		8760 psi
@Strain 1.50 %,
Temperature 176 °F		ISO 527
 65.8 MPa
@Strain 2.00 %,
Temperature 80.0 °C		9540 psi
@Strain 2.00 %,
Temperature 176 °F		ISO 527
 68.9 MPa
@Strain 2.50 %,
Temperature 80.0 °C		9990 psi
@Strain 2.50 %,
Temperature 176 °F		ISO 527
 71.5 MPa
@Strain 3.00 %,
Temperature 80.0 °C		10400 psi
@Strain 3.00 %,
Temperature 176 °F		Break; ISO 527
 72.2 MPa
@Strain 1.50 %,
Temperature 60.0 °C		10500 psi
@Strain 1.50 %,
Temperature 140 °F		ISO 527
 75.4 MPa
@Strain 1.00 %,
Temperature 40.0 °C		10900 psi
@Strain 1.00 %,
Temperature 104 °F		ISO 527
 79.7 MPa
@Strain 2.00 %,
Temperature 60.0 °C		11600 psi
@Strain 2.00 %,
Temperature 140 °F		ISO 527
 83.9 MPa
@Strain 2.50 %,
Temperature 60.0 °C		12200 psi
@Strain 2.50 %,
Temperature 140 °F		ISO 527
 84.7 MPa
@Strain 1.00 %,
Temperature 23.0 °C		12300 psi
@Strain 1.00 %,
Temperature 73.4 °F		ISO 527
 87.1 MPa
@Strain 3.00 %,
Temperature 60.0 °C		12600 psi
@Strain 3.00 %,
Temperature 140 °F		Break; ISO 527
 92.5 MPa
@Strain 1.00 %,
Temperature 0.000 °C		13400 psi
@Strain 1.00 %,
Temperature 32.0 °F		ISO 527
 95.9 MPa
@Strain 1.00 %,
Temperature -20.0 °C		13900 psi
@Strain 1.00 %,
Temperature -4.00 °F		ISO 527
 95.9 MPa
@Strain 1.50 %,
Temperature 40.0 °C		13900 psi
@Strain 1.50 %,
Temperature 104 °F		ISO 527
 100 MPa
@Strain 1.00 %,
Temperature -40.0 °C		14500 psi
@Strain 1.00 %,
Temperature -40.0 °F		ISO 527
 105 MPa
@Strain 2.00 %,
Temperature 40.0 °C		15200 psi
@Strain 2.00 %,
Temperature 104 °F		ISO 527
 105 MPa
@Strain 2.80 %,
Temperature 40.0 °C		15200 psi
@Strain 2.80 %,
Temperature 104 °F		Break; ISO 527
 111 MPa
@Strain 1.50 %,
Temperature 23.0 °C		16100 psi
@Strain 1.50 %,
Temperature 73.4 °F		ISO 527
 125 MPa
@Strain 1.50 %,
Temperature 0.000 °C		18100 psi
@Strain 1.50 %,
Temperature 32.0 °F		ISO 527
 126 MPa
@Strain 2.00 %,
Temperature 23.0 °C		18300 psi
@Strain 2.00 %,
Temperature 73.4 °F		ISO 527
 132 MPa
@Strain 1.50 %,
Temperature -20.0 °C		19100 psi
@Strain 1.50 %,
Temperature -4.00 °F		ISO 527
 135 MPa
@Strain 2.80 %,
Temperature 23.0 °C		19600 psi
@Strain 2.80 %,
Temperature 73.4 °F		Break; ISO 527
 138 MPa
@Strain 1.50 %,
Temperature -40.0 °C		20000 psi
@Strain 1.50 %,
Temperature -40.0 °F		ISO 527
 145 MPa
@Strain 2.00 %,
Temperature 0.000 °C		21000 psi
@Strain 2.00 %,
Temperature 32.0 °F		ISO 527
 154 MPa
@Strain 2.50 %,
Temperature 0.000 °C		22300 psi
@Strain 2.50 %,
Temperature 32.0 °F		Break; ISO 527
 157 MPa
@Strain 2.00 %,
Temperature -20.0 °C		22800 psi
@Strain 2.00 %,
Temperature -4.00 °F		ISO 527
 164 MPa
@Strain 2.00 %,
Temperature -40.0 °C		23800 psi
@Strain 2.00 %,
Temperature -40.0 °F		ISO 527
 170 MPa
@Strain 2.50 %,
Temperature -20.0 °C		24700 psi
@Strain 2.50 %,
Temperature -4.00 °F		Break; ISO 527
 175 MPa
@Strain 2.50 %,
Temperature -40.0 °C		25400 psi
@Strain 2.50 %,
Temperature -40.0 °F		Break; ISO 527
Elongation at Break 2.5 %
@Temperature 23.0 °C		2.5 %
@Temperature 73.4 °F		ISO 527
Tensile Modulus 9.50 GPa
@Temperature 23.0 °C		1380 ksi
@Temperature 73.4 °F		ISO 527
Flexural Strength 190 MPa
@Temperature 23.0 °C		27600 psi
@Temperature 73.4 °F		ISO 178
Flexural Modulus 8.50 GPa
@Temperature 23.0 °C		1230 ksi
@Temperature 73.4 °F		ISO 178
Izod Impact, Notched (ISO)  8.00 kJ/m²
@Temperature -30.0 °C		3.81 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1A
 8.00 kJ/m²
@Temperature 23.0 °C		3.81 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1A
Izod Impact, Unnotched (ISO)  50.0 kJ/m²
@Temperature -30.0 °C		23.8 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1U
 50.0 kJ/m²
@Temperature 23.0 °C		23.8 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1U
Charpy Impact Unnotched  6.00 J/cm²
@Temperature 23.0 °C		28.6 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
 6.50 J/cm²
@Temperature -30.0 °C		30.9 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
Charpy Impact, Notched  0.900 J/cm²
@Temperature -30.0 °C		4.28 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 1.00 J/cm²
@Temperature 23.0 °C		4.76 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
Tensile Creep Modulus, 1 hour 9000 MPa
@Temperature 23.0 °C		1.31e+6 psi
@Temperature 73.4 °F		ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.116 %,
Temperature 23.0 °C		1450 psi
@Strain 0.116 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.110 %,
Temperature 23.0 °C		1450 psi
@Strain 0.110 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.220 %,
Temperature 23.0 °C		2900 psi
@Strain 0.220 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.221 %,
Temperature 23.0 °C		2900 psi
@Strain 0.221 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.337 %,
Temperature 23.0 °C		4350 psi
@Strain 0.337 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.330 %,
Temperature 23.0 °C		4350 psi
@Strain 0.330 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.440 %,
Temperature 23.0 °C		5800 psi
@Strain 0.440 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.463 %,
Temperature 23.0 °C		5800 psi
@Strain 0.463 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.600 %,
Temperature 23.0 °C		7250 psi
@Strain 0.600 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.568 %,
Temperature 23.0 °C		7250 psi
@Strain 0.568 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 60.0 MPa
@Strain 0.715 %,
Temperature 23.0 °C		8700 psi
@Strain 0.715 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 60.0 MPa
@Strain 0.757 %,
Temperature 23.0 °C		8700 psi
@Strain 0.757 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 70.0 MPa
@Strain 0.936 %,
Temperature 23.0 °C		10200 psi
@Strain 0.936 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 70.0 MPa
@Strain 0.873 %,
Temperature 23.0 °C		10200 psi
@Strain 0.873 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 80.0 MPa
@Strain 1.06 %,
Temperature 23.0 °C		11600 psi
@Strain 1.06 %,
Temperature 73.4 °F		1h; Break; Isochronous; ISO 899
 80.0 MPa
@Strain 1.17 %,
Temperature 23.0 °C		11600 psi
@Strain 1.17 %,
Temperature 73.4 °F		10h; Break; Isochronous; ISO 899
Tensile Creep Modulus, 1000 hours 7300 MPa
@Temperature 23.0 °C		1.06e+6 psi
@Temperature 73.4 °F		ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.126 %,
Temperature 23.0 °C		1450 psi
@Strain 0.126 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.137 %,
Temperature 23.0 °C		1450 psi
@Strain 0.137 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.274 %,
Temperature 23.0 °C		2900 psi
@Strain 0.274 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.242 %,
Temperature 23.0 °C		2900 psi
@Strain 0.242 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.379 %,
Temperature 23.0 °C		4350 psi
@Strain 0.379 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.431 %,
Temperature 23.0 °C		4350 psi
@Strain 0.431 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.600 %,
Temperature 23.0 °C		5800 psi
@Strain 0.600 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.526 %,
Temperature 23.0 °C		5800 psi
@Strain 0.526 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.684 %,
Temperature 23.0 °C		7250 psi
@Strain 0.684 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.778 %,
Temperature 23.0 °C		7250 psi
@Strain 0.778 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 60.0 MPa
@Strain 0.968 %,
Temperature 23.0 °C		8700 psi
@Strain 0.968 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 60.0 MPa
@Strain 0.852 %,
Temperature 23.0 °C		8700 psi
@Strain 0.852 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 70.0 MPa
@Strain 1.06 %,
Temperature 23.0 °C		10200 psi
@Strain 1.06 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 70.0 MPa
@Strain 1.20 %,
Temperature 23.0 °C		10200 psi
@Strain 1.20 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 80.0 MPa
@Strain 1.49 %,
Temperature 23.0 °C		11600 psi
@Strain 1.49 %,
Temperature 73.4 °F		1000h; Break; Isochronous; ISO 899
 80.0 MPa
@Strain 1.33 %,
Temperature 23.0 °C		11600 psi
@Strain 1.33 %,
Temperature 73.4 °F		100h; Break; Isochronous; ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity >= 1.00e+15 ohm-cm
@Temperature 23.0 °C		>= 1.00e+15 ohm-cm
@Temperature 73.4 °F		IEC 60093
Surface Resistance 1.00e+14 ohm
@Temperature 23.0 °C		1.00e+14 ohm
@Temperature 73.4 °F		IEC 60093
Dielectric Constant  3.6
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.6
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
 3.8
@Frequency 100 Hz,
Temperature 23.0 °C		3.8
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
Dielectric Strength 36.0 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		914 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		IEC 60243-1
 21.0 kV/mm
@Thickness 2.00 mm,
Time 20.0 sec		533 kV/in
@Thickness 0.0787 in,
Time 0.00556 hour		IEC 60243-1
Dissipation Factor  0.0030
@Frequency 100 Hz,
Temperature 23.0 °C		0.0030
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
 0.017
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.017
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
Comparative Tracking Index  500 V
@Temperature 23.0 °C		500 V
@Temperature 73.4 °F		UL 746A
 550 V
@Temperature 23.0 °C		550 V
@Temperature 73.4 °F		IEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  100 µm/m-°C
@Temperature 23.0 - 55.0 °C		55.6 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
 100 µm/m-°C
@Temperature 23.0 - 55.0 °C		55.6 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 215 °C419 °FISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 175 °C347 °FISO 75-1/-2
Deflection Temperature at 8.0 MPa 97.0 °C207 °FISO 75-1/-2
Glass Transition Temp, Tg 120 °C248 °F10°C/min; ISO 11357-1/-2
UL RTI, Electrical  130 °C
@Thickness 6.00 mm		266 °F
@Thickness 0.236 in		UL 746B
 130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical with Impact  125 °C
@Thickness 0.750 mm		257 °F
@Thickness 0.0295 in		UL 746B
 125 °C
@Thickness 1.50 mm		257 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
 130 °C
@Thickness 6.00 mm		266 °F
@Thickness 0.236 in		UL 746B
UL RTI, Mechanical without Impact  130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 6.00 mm		266 °F
@Thickness 0.236 in		UL 746B
Flammability, UL94  HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		UL94
 HB
@Thickness 6.00 mm		HB
@Thickness 0.236 in		UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		UL94
 HB
@Thickness 6.00 mm		HB
@Thickness 0.236 in		IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		IEC 60695-11-10
Oxygen Index 19 %19 %ISO 4589-1/-2
Glow Wire Test 650 °C
@Thickness 3.00 mm		1200 °F
@Thickness 0.118 in		IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 225 °C437 °F10°C/min; ISO 11357-1/-3
 250 °C482 °FOptimum
 240 - 260 °C464 - 500 °F
Mold Temperature 80.0 °C176 °Foptimum
 30.0 - 130 °C86.0 - 266 °F
Drying Temperature 110 - 130 °C230 - 266 °F
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hour
Moisture Content <= 0.040 %<= 0.040 %
 
Descriptive Properties
AdditiveLubricant
AppearanceNatural Color
Drying RecommendedYes
FeaturesAppearance, Pleasing Surface
 Chemical Resistance, Good
 Dimensional Stability, Good
 Moisture Absorption, Low
 Processability, Good
 Warp Resistant
 Warpage, Low
FillerGlass fiber reinforcement
FormsPellets
GenericPBT Alloy
Material StatusCurrent
Part Marking Code>PBT+ASA-GF30<ISO 11469
Polymer FamilyPolyester
Polymer TypePBT
Processing MethodInjection Molding
Product CategoryGlass Reinforced Resins
 Low Warp Resins
Region Available - GlobalYes
Resin IdentificationPBT+ASA-GF30ISO 1043
RoHS ComplianceContact Manufacturer
Ultrasonic WeldableYes
UsesAutomotive Applications
 Housings
 Industrial Applications

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38055.html

免责声明: 本文 DuPont Performance Polymers Crastin® LW9030 NC010 PBT 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4