- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.272
- 缺口冲击强度: 16.9
- 拉伸强度 [MPa]: 50.0
- 弯曲模量 [MPa]: 2.015
- 热变形温度 [℃]: 135.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.272 g/cc | 0.04595 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.026 cm/cm @Thickness 2.00 mm | 0.026 in/in @Thickness 0.0787 in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.023 cm/cm @Thickness 2.00 mm | 0.023 in/in @Thickness 0.0787 in | Normal; ISO 294-4 | ||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 250 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 482 °F | Resin; ISO 1133 | ||
| 6.5 g/10 min @Load 2.16 kg, Temperature 250 °C | 6.5 g/10 min @Load 4.76 lb, Temperature 482 °F | Part; ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 37.0 MPa @Temperature 23.0 °C | 5370 psi @Temperature 73.4 °F | ISO 527 | ||
| Tensile Strength, Yield | 50.0 MPa @Temperature 23.0 °C | 7250 psi @Temperature 73.4 °F | ISO 527 | ||
| Elongation at Break | 16 % @Temperature 23.0 °C | 16 % @Temperature 73.4 °F | nominal; ISO 527 | ||
| 20 % @Temperature 23.0 °C | 20 % @Temperature 73.4 °F | ISO 527 | |||
| Elongation at Yield | 6.0 % @Temperature 23.0 °C | 6.0 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 2.30 GPa @Temperature 23.0 °C | 334 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 65.0 MPa @Temperature 23.0 °C | 9430 psi @Temperature 73.4 °F | ISO 178 | ||
| Flexural Modulus | 2.015 GPa @Temperature 23.0 °C | 292.3 ksi @Temperature 73.4 °F | ISO 178 | ||
| Izod Impact, Notched (ISO) | 16.9 kJ/m² @Temperature 23.0 °C | 8.04 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 209 kJ/m² @Temperature 23.0 °C | 99.5 ft-lb/in² @Temperature 73.4 °F | ISO 180/1U | ||
| Charpy Impact Unnotched | 28.0 J/cm² @Temperature 23.0 °C | 133 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.50 J/cm² @Temperature 23.0 °C | 7.14 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| 240 - 260 °C | 464 - 500 °F | ||||
| 250 °C | 482 °F | Optimum | |||
| Mold Temperature | 30.0 - 130 °C | 86.0 - 266 °F | |||
| 80.0 °C | 176 °F | optimum | |||
| Drying Temperature | 110 - 130 °C | 230 - 266 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | <= 0.040 % | <= 0.040 % | |||
| Descriptive Properties | |||||
| Drying Recommended | Yes | ||||
| Generic | PBT | ||||
| Product Category | Unreinforced Resins | ||||
| Unreinforced Resins | |||||