- 密度 [g/cm3]: 1.44
- 缺口冲击强度: 7.0
- 弯曲模量 [MPa]: 8.50
- 热变形温度 [℃]: 210.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 | ||
| Filler Content | 30 % | 30 % | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 125 MPa @Temperature 23.0 °C | 18100 psi @Temperature 73.4 °F | ISO 527 | ||
| Elongation at Break | 2.0 % @Temperature 23.0 °C | 2.0 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 9.20 GPa @Temperature 23.0 °C | 1330 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 180 MPa @Temperature 23.0 °C | 26100 psi @Temperature 73.4 °F | ISO 178 | ||
| Flexural Modulus | 8.50 GPa @Temperature 23.0 °C | 1230 ksi @Temperature 73.4 °F | ISO 178 | ||
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | ||
| 7.00 kJ/m² @Temperature -30.0 °C | 3.33 ft-lb/in² @Temperature -22.0 °F | ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² @Temperature 23.0 °C | 21.4 ft-lb/in² @Temperature 73.4 °F | ISO 180/1U | ||
| 50.0 kJ/m² @Temperature -30.0 °C | 23.8 ft-lb/in² @Temperature -22.0 °F | ISO 180/1U | |||
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature -30.0 °C | 21.4 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 5.00 J/cm² @Temperature 23.0 °C | 23.8 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -30.0 °C | 3.33 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.900 J/cm² @Temperature 23.0 °C | 4.28 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75-1/-2 | ||
| UL RTI, Electrical | 130 °C @Thickness 0.750 mm | 266 °F @Thickness 0.0295 in | UL 746B | ||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL 746B | |||
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | UL 746B | |||
| 130 °C @Thickness 6.00 mm | 266 °F @Thickness 0.236 in | UL 746B | |||
| UL RTI, Mechanical with Impact | 125 °C @Thickness 0.750 mm | 257 °F @Thickness 0.0295 in | UL 746B | ||
| 125 °C @Thickness 1.50 mm | 257 °F @Thickness 0.0591 in | UL 746B | |||
| 130 °C @Thickness 6.00 mm | 266 °F @Thickness 0.236 in | UL 746B | |||
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | UL 746B | |||
| UL RTI, Mechanical without Impact | 130 °C @Thickness 0.750 mm | 266 °F @Thickness 0.0295 in | UL 746B | ||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL 746B | |||
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | UL 746B | |||
| 130 °C @Thickness 6.00 mm | 266 °F @Thickness 0.236 in | UL 746B | |||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | UL94 | ||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | UL94 | |||
| HB @Thickness 6.00 mm | HB @Thickness 0.236 in | UL94 | |||
| HB @Thickness 6.00 mm | HB @Thickness 0.236 in | IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | IEC 60695-11-10 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | IEC 60695-11-10 | |||
| Oxygen Index | 20 % | 20 % | ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| 250 °C | 482 °F | Optimum | |||
| 240 - 260 °C | 464 - 500 °F | ||||
| Mold Temperature | 80.0 °C | 176 °F | optimum | ||
| 30.0 - 130 °C | 86.0 - 266 °F | ||||
| Drying Temperature | 110 - 130 °C | 230 - 266 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | <= 0.040 % | <= 0.040 % | |||
| Descriptive Properties | |||||
| Additive | Lubricant | ||||
| Appearance | Black Color | ||||
| Drying Recommended | Yes | ||||
| Features | Appearance, Pleasing Surface | ||||
| Chemical Resistance, Good | |||||
| Dimensional Stability, Good | |||||
| Moisture Absorption, Low | |||||
| Processability, Good | |||||
| Warp Resistant | |||||
| Warpage, Low | |||||
| Filler | Glass fiber reinforcement | ||||
| Forms | Pellets | ||||
| Generic | PBT Alloy | ||||
| Material Status | Current | ||||
| Part Marking Code | >PBT+ASA-GF30< | ISO 11469 | |||
| Polymer Family | Polyester | ||||
| Polymer Type | PBT | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Glass Reinforced Resins | ||||
| Low Warp Resins | |||||
| Region Available - Global | Yes | ||||
| Resin Identification | PBT+ASA-GF30 | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||
| Uses | Automotive Applications | ||||
| Housings | |||||
| Industrial Applications | |||||