  3. PBT
  4. DuPont Performance Polymers Crastin® S650FR NC010 PBT

DuPont Performance Polymers Crastin® S650FR NC010 PBT

DuPont Performance Polymers Crastin® S650FR NC010 PBT 物性表: DuPont Performance Polymers Crastin® S650FR NC010 PBT物性表及特性介绍,DuPont Performance Polymers Crastin® S650FR NC010 PBT注塑参数详情,如需DuPont Performance Polymers Crastin® S650FR NC010 PBT下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.46
  • 吸水率 [%]: 0.15
  • 缺口冲击强度: 4.0
  • 拉伸强度 [MPa]: 65.0
  • 热变形温度 [℃]: 160.0
 
Physical PropertiesMetricEnglishComments
Density 1.46 g/cc0.0527 lb/in³ISO 1183
Water Absorption  0.15 %
@Temperature 23.0 °C		0.15 %
@Temperature 73.4 °F		Equilibrium 50%RH; ISO 62, Similar to
 0.39 %
@Temperature 23.0 °C		0.39 %
@Temperature 73.4 °F		Saturation, immersed; ISO 62, Similar to
Viscosity  75000 cP
@Shear Rate 10000 1/s,
Temperature 260 °C		75000 cP
@Shear Rate 10000 1/s,
Temperature 500 °F		ISO 11443
 94000 cP
@Shear Rate 10000 1/s,
Temperature 250 °C		94000 cP
@Shear Rate 10000 1/s,
Temperature 482 °F		ISO 11443
 104000 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		104000 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		ISO 11443
 120000 cP
@Shear Rate 10000 1/s,
Temperature 240 °C		120000 cP
@Shear Rate 10000 1/s,
Temperature 464 °F		ISO 11443
 131000 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		131000 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		ISO 11443
 155000 cP
@Shear Rate 2000 1/s,
Temperature 260 °C		155000 cP
@Shear Rate 2000 1/s,
Temperature 500 °F		ISO 11443
 169000 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		169000 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		ISO 11443
 200000 cP
@Shear Rate 2000 1/s,
Temperature 250 °C		200000 cP
@Shear Rate 2000 1/s,
Temperature 482 °F		ISO 11443
 202000 cP
@Shear Rate 1000 1/s,
Temperature 260 °C		202000 cP
@Shear Rate 1000 1/s,
Temperature 500 °F		ISO 11443
 249000 cP
@Shear Rate 500 1/s,
Temperature 260 °C		249000 cP
@Shear Rate 500 1/s,
Temperature 500 °F		ISO 11443
 262000 cP
@Shear Rate 2000 1/s,
Temperature 240 °C		262000 cP
@Shear Rate 2000 1/s,
Temperature 464 °F		ISO 11443
 267000 cP
@Shear Rate 1000 1/s,
Temperature 250 °C		267000 cP
@Shear Rate 1000 1/s,
Temperature 482 °F		ISO 11443
 327000 cP
@Shear Rate 100 1/s,
Temperature 260 °C		327000 cP
@Shear Rate 100 1/s,
Temperature 500 °F		ISO 11443
 342000 cP
@Shear Rate 500 1/s,
Temperature 250 °C		342000 cP
@Shear Rate 500 1/s,
Temperature 482 °F		ISO 11443
 356000 cP
@Shear Rate 1000 1/s,
Temperature 240 °C		356000 cP
@Shear Rate 1000 1/s,
Temperature 464 °F		ISO 11443
 470000 cP
@Shear Rate 500 1/s,
Temperature 240 °C		470000 cP
@Shear Rate 500 1/s,
Temperature 464 °F		ISO 11443
 485000 cP
@Shear Rate 100 1/s,
Temperature 250 °C		485000 cP
@Shear Rate 100 1/s,
Temperature 482 °F		ISO 11443
 733000 cP
@Shear Rate 100 1/s,
Temperature 240 °C		733000 cP
@Shear Rate 100 1/s,
Temperature 464 °F		ISO 11443
Linear Mold Shrinkage, Flow 0.0225 cm/cm0.0225 in/inParallel; Annealed; ISO 294-4
 0.018 cm/cm
@Thickness 2.00 mm		0.018 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0215 cm/cm0.0215 in/inNormal; Annealed; ISO 294-4
 0.016 cm/cm
@Thickness 2.00 mm		0.016 in/in
@Thickness 0.0787 in		Normal; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Stress  1.35 MPa
@Strain 0.500 %,
Temperature 140 °C		196 psi
@Strain 0.500 %,
Temperature 284 °F		ISO 527
 1.74 MPa
@Strain 0.500 %,
Temperature 120 °C		252 psi
@Strain 0.500 %,
Temperature 248 °F		ISO 527
 1.83 MPa
@Strain 0.500 %,
Temperature 100 °C		265 psi
@Strain 0.500 %,
Temperature 212 °F		ISO 527
 2.51 MPa
@Strain 0.500 %,
Temperature 80.0 °C		364 psi
@Strain 0.500 %,
Temperature 176 °F		ISO 527
 2.60 MPa
@Strain 1.00 %,
Temperature 140 °C		377 psi
@Strain 1.00 %,
Temperature 284 °F		ISO 527
 3.30 MPa
@Strain 1.00 %,
Temperature 120 °C		479 psi
@Strain 1.00 %,
Temperature 248 °F		ISO 527
 3.65 MPa
@Strain 1.00 %,
Temperature 100 °C		529 psi
@Strain 1.00 %,
Temperature 212 °F		ISO 527
 3.78 MPa
@Strain 1.50 %,
Temperature 140 °C		548 psi
@Strain 1.50 %,
Temperature 284 °F		ISO 527
 4.57 MPa
@Strain 0.500 %,
Temperature 60.0 °C		663 psi
@Strain 0.500 %,
Temperature 140 °F		ISO 527
 4.72 MPa
@Strain 1.50 %,
Temperature 120 °C		685 psi
@Strain 1.50 %,
Temperature 248 °F		ISO 527
 4.89 MPa
@Strain 1.00 %,
Temperature 80.0 °C		709 psi
@Strain 1.00 %,
Temperature 176 °F		ISO 527
 4.92 MPa
@Strain 2.00 %,
Temperature 140 °C		714 psi
@Strain 2.00 %,
Temperature 284 °F		ISO 527
 5.43 MPa
@Strain 1.50 %,
Temperature 100 °C		788 psi
@Strain 1.50 %,
Temperature 212 °F		ISO 527
 6.04 MPa
@Strain 2.00 %,
Temperature 120 °C		876 psi
@Strain 2.00 %,
Temperature 248 °F		ISO 527
 6.04 MPa
@Strain 2.50 %,
Temperature 140 °C		876 psi
@Strain 2.50 %,
Temperature 284 °F		ISO 527
 7.14 MPa
@Strain 1.50 %,
Temperature 80.0 °C		1040 psi
@Strain 1.50 %,
Temperature 176 °F		ISO 527
 7.16 MPa
@Strain 3.00 %,
Temperature 140 °C		1040 psi
@Strain 3.00 %,
Temperature 284 °F		Break; ISO 527
 7.17 MPa
@Strain 2.00 %,
Temperature 100 °C		1040 psi
@Strain 2.00 %,
Temperature 212 °F		ISO 527
 7.28 MPa
@Strain 2.50 %,
Temperature 120 °C		1060 psi
@Strain 2.50 %,
Temperature 248 °F		ISO 527
 8.46 MPa
@Strain 3.00 %,
Temperature 120 °C		1230 psi
@Strain 3.00 %,
Temperature 248 °F		Break; ISO 527
 8.64 MPa
@Strain 1.00 %,
Temperature 60.0 °C		1250 psi
@Strain 1.00 %,
Temperature 140 °F		ISO 527
 8.86 MPa
@Strain 2.50 %,
Temperature 100 °C		1290 psi
@Strain 2.50 %,
Temperature 212 °F		ISO 527
 9.24 MPa
@Strain 2.00 %,
Temperature 80.0 °C		1340 psi
@Strain 2.00 %,
Temperature 176 °F		ISO 527
 10.5 MPa
@Strain 3.00 %,
Temperature 100 °C		1520 psi
@Strain 3.00 %,
Temperature 212 °F		Break; ISO 527
 11.2 MPa
@Strain 2.50 %,
Temperature 80.0 °C		1620 psi
@Strain 2.50 %,
Temperature 176 °F		ISO 527
 12.2 MPa
@Strain 1.50 %,
Temperature 60.0 °C		1770 psi
@Strain 1.50 %,
Temperature 140 °F		ISO 527
 13.0 MPa
@Strain 3.00 %,
Temperature 80.0 °C		1890 psi
@Strain 3.00 %,
Temperature 176 °F		Break; ISO 527
 13.0 MPa
@Strain 0.500 %,
Temperature 40.0 °C		1890 psi
@Strain 0.500 %,
Temperature 104 °F		ISO 527
 14.5 MPa
@Strain 0.500 %,
Temperature 23.0 °C		2100 psi
@Strain 0.500 %,
Temperature 73.4 °F		ISO 527
 14.9 MPa
@Strain 0.500 %,
Temperature 0.000 °C		2160 psi
@Strain 0.500 %,
Temperature 32.0 °F		ISO 527
 15.3 MPa
@Strain 2.00 %,
Temperature 60.0 °C		2220 psi
@Strain 2.00 %,
Temperature 140 °F		ISO 527
 15.5 MPa
@Strain 0.500 %,
Temperature -20.0 °C		2250 psi
@Strain 0.500 %,
Temperature -4.00 °F		ISO 527
 16.0 MPa
@Strain 0.500 %,
Temperature -40.0 °C		2320 psi
@Strain 0.500 %,
Temperature -40.0 °F		ISO 527
 17.9 MPa
@Strain 2.50 %,
Temperature 60.0 °C		2600 psi
@Strain 2.50 %,
Temperature 140 °F		ISO 527
 20.0 MPa
@Strain 3.00 %,
Temperature 60.0 °C		2900 psi
@Strain 3.00 %,
Temperature 140 °F		Break; ISO 527
 25.6 MPa
@Strain 1.00 %,
Temperature 40.0 °C		3710 psi
@Strain 1.00 %,
Temperature 104 °F		ISO 527
 28.6 MPa
@Strain 1.00 %,
Temperature 23.0 °C		4150 psi
@Strain 1.00 %,
Temperature 73.4 °F		ISO 527
 29.6 MPa
@Strain 1.00 %,
Temperature 0.000 °C		4290 psi
@Strain 1.00 %,
Temperature 32.0 °F		ISO 527
 31.0 MPa
@Strain 1.00 %,
Temperature -20.0 °C		4500 psi
@Strain 1.00 %,
Temperature -4.00 °F		ISO 527
 31.9 MPa
@Strain 1.00 %,
Temperature -40.0 °C		4630 psi
@Strain 1.00 %,
Temperature -40.0 °F		ISO 527
 36.3 MPa
@Strain 1.50 %,
Temperature 40.0 °C		5260 psi
@Strain 1.50 %,
Temperature 104 °F		ISO 527
 41.0 MPa
@Strain 1.50 %,
Temperature 23.0 °C		5950 psi
@Strain 1.50 %,
Temperature 73.4 °F		ISO 527
 43.5 MPa
@Strain 1.50 %,
Temperature 0.000 °C		6310 psi
@Strain 1.50 %,
Temperature 32.0 °F		ISO 527
 43.8 MPa
@Strain 2.00 %,
Temperature 40.0 °C		6350 psi
@Strain 2.00 %,
Temperature 104 °F		ISO 527
 45.8 MPa
@Strain 1.50 %,
Temperature -20.0 °C		6640 psi
@Strain 1.50 %,
Temperature -4.00 °F		ISO 527
 47.2 MPa
@Strain 1.50 %,
Temperature -40.0 °C		6850 psi
@Strain 1.50 %,
Temperature -40.0 °F		ISO 527
 47.9 MPa
@Strain 2.50 %,
Temperature 40.0 °C		6950 psi
@Strain 2.50 %,
Temperature 104 °F		ISO 527
 49.4 MPa
@Strain 3.00 %,
Temperature 40.0 °C		7160 psi
@Strain 3.00 %,
Temperature 104 °F		Break; ISO 527
 50.1 MPa
@Strain 2.00 %,
Temperature 23.0 °C		7270 psi
@Strain 2.00 %,
Temperature 73.4 °F		ISO 527
 55.7 MPa
@Strain 2.00 %,
Temperature 0.000 °C		8080 psi
@Strain 2.00 %,
Temperature 32.0 °F		ISO 527
 58.2 MPa
@Strain 3.00 %,
Temperature 23.0 °C		8440 psi
@Strain 3.00 %,
Temperature 73.4 °F		Break; ISO 527
 59.0 MPa
@Strain 2.00 %,
Temperature -20.0 °C		8560 psi
@Strain 2.00 %,
Temperature -4.00 °F		ISO 527
 60.9 MPa
@Strain 2.00 %,
Temperature -40.0 °C		8830 psi
@Strain 2.00 %,
Temperature -40.0 °F		ISO 527
 65.7 MPa
@Strain 2.50 %,
Temperature 0.000 °C		9530 psi
@Strain 2.50 %,
Temperature 32.0 °F		ISO 527
 69.8 MPa
@Strain 2.50 %,
Temperature -20.0 °C		10100 psi
@Strain 2.50 %,
Temperature -4.00 °F		ISO 527
 72.4 MPa
@Strain 2.50 %,
Temperature -40.0 °C		10500 psi
@Strain 2.50 %,
Temperature -40.0 °F		ISO 527
 73.4 MPa
@Strain 3.00 %,
Temperature 0.000 °C		10600 psi
@Strain 3.00 %,
Temperature 32.0 °F		Break; ISO 527
 78.1 MPa
@Strain 3.00 %,
Temperature -20.0 °C		11300 psi
@Strain 3.00 %,
Temperature -4.00 °F		Break; ISO 527
 81.5 MPa
@Strain 3.00 %,
Temperature -40.0 °C		11800 psi
@Strain 3.00 %,
Temperature -40.0 °F		Break; ISO 527
Tensile Strength, Yield 65.0 MPa
@Temperature 23.0 °C		9430 psi
@Temperature 73.4 °F		ISO 527
Elongation at Break  7.2 %
@Temperature 23.0 °C		7.2 %
@Temperature 73.4 °F		nominal; ISO 527
 9.0 %
@Temperature 23.0 °C		9.0 %
@Temperature 73.4 °F		ISO 527
Elongation at Yield 4.6 %
@Temperature 23.0 °C		4.6 %
@Temperature 73.4 °F		ISO 527
Tensile Modulus 3.00 GPa
@Temperature 23.0 °C		435 ksi
@Temperature 73.4 °F		ISO 527
Flexural Strength 100 MPa
@Temperature 23.0 °C		14500 psi
@Temperature 73.4 °F		ISO 178
Shear Modulus  0.0410 GPa
@Temperature 200 °C		5.95 ksi
@Temperature 392 °F		ISO 6721
 0.0440 GPa
@Temperature 190 °C		6.38 ksi
@Temperature 374 °F		ISO 6721
 0.0490 GPa
@Temperature 180 °C		7.11 ksi
@Temperature 356 °F		ISO 6721
 0.0550 GPa
@Temperature 170 °C		7.98 ksi
@Temperature 338 °F		ISO 6721
 0.0610 GPa
@Temperature 160 °C		8.85 ksi
@Temperature 320 °F		ISO 6721
 0.0680 GPa
@Temperature 150 °C		9.86 ksi
@Temperature 302 °F		ISO 6721
 0.0760 GPa
@Temperature 140 °C		11.0 ksi
@Temperature 284 °F		ISO 6721
 0.0910 GPa
@Temperature 130 °C		13.2 ksi
@Temperature 266 °F		ISO 6721
 0.107 GPa
@Temperature 120 °C		15.5 ksi
@Temperature 248 °F		ISO 6721
 0.127 GPa
@Temperature 110 °C		18.4 ksi
@Temperature 230 °F		ISO 6721
 0.151 GPa
@Temperature 100 °C		21.9 ksi
@Temperature 212 °F		ISO 6721
 0.186 GPa
@Temperature 90.0 °C		27.0 ksi
@Temperature 194 °F		ISO 6721
 0.250 GPa
@Temperature 80.0 °C		36.3 ksi
@Temperature 176 °F		ISO 6721
 0.364 GPa
@Temperature 70.0 °C		52.8 ksi
@Temperature 158 °F		ISO 6721
 0.546 GPa
@Temperature 60.0 °C		79.2 ksi
@Temperature 140 °F		ISO 6721
 0.747 GPa
@Temperature 50.0 °C		108 ksi
@Temperature 122 °F		ISO 6721
 0.847 GPa
@Temperature 40.0 °C		123 ksi
@Temperature 104 °F		ISO 6721
 0.886 GPa
@Temperature 30.0 °C		129 ksi
@Temperature 86.0 °F		ISO 6721
 0.916 GPa
@Temperature 20.0 °C		133 ksi
@Temperature 68.0 °F		ISO 6721
 0.943 GPa
@Temperature 10.0 °C		137 ksi
@Temperature 50.0 °F		ISO 6721
 0.969 GPa
@Temperature 0.000 °C		141 ksi
@Temperature 32.0 °F		ISO 6721
 0.995 GPa
@Temperature -10.0 °C		144 ksi
@Temperature 14.0 °F		ISO 6721
 1.03 GPa
@Temperature -20.0 °C		149 ksi
@Temperature -4.00 °F		ISO 6721
 1.07 GPa
@Temperature -30.0 °C		155 ksi
@Temperature -22.0 °F		ISO 6721
 1.10 GPa
@Temperature -40.0 °C		160 ksi
@Temperature -40.0 °F		ISO 6721
 1.14 GPa
@Temperature -50.0 °C		165 ksi
@Temperature -58.0 °F		ISO 6721
Izod Impact, Notched (ISO)  4.00 kJ/m²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1A
 4.00 kJ/m²
@Temperature 23.0 °C		1.90 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1A
Izod Impact, Unnotched (ISO)  42.0 kJ/m²
@Temperature -30.0 °C		20.0 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1U
 45.0 kJ/m²
@Temperature 23.0 °C		21.4 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1U
Charpy Impact Unnotched  6.70 J/cm²
@Temperature -30.0 °C		31.9 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
 7.00 J/cm²
@Temperature 23.0 °C		33.3 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched  0.330 J/cm²
@Temperature -30.0 °C		1.57 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 0.380 J/cm²
@Temperature 23.0 °C		1.81 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
Tensile Creep Modulus, 1 hour 2500 MPa
@Temperature 23.0 °C		363000 psi
@Temperature 73.4 °F		ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 2.50 MPa
@Strain 0.536 %,
Temperature 60.0 °C		363 psi
@Strain 0.536 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 2.50 MPa
@Strain 0.636 %,
Temperature 60.0 °C		363 psi
@Strain 0.636 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 5.00 MPa
@Strain 1.25 %,
Temperature 60.0 °C		725 psi
@Strain 1.25 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.218 %,
Temperature 23.0 °C		725 psi
@Strain 0.218 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 5.00 MPa
@Strain 1.06 %,
Temperature 60.0 °C		725 psi
@Strain 1.06 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.199 %,
Temperature 23.0 °C		725 psi
@Strain 0.199 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 7.50 MPa
@Strain 1.59 %,
Temperature 60.0 °C		1090 psi
@Strain 1.59 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 7.50 MPa
@Strain 1.86 %,
Temperature 60.0 °C		1090 psi
@Strain 1.86 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 2.49 %,
Temperature 60.0 °C		1450 psi
@Strain 2.49 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 2.14 %,
Temperature 60.0 °C		1450 psi
@Strain 2.14 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.437 %,
Temperature 23.0 °C		1450 psi
@Strain 0.437 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.399 %,
Temperature 23.0 °C		1450 psi
@Strain 0.399 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 12.5 MPa
@Strain 2.73 %,
Temperature 60.0 °C		1810 psi
@Strain 2.73 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 12.5 MPa
@Strain 3.17 %,
Temperature 60.0 °C		1810 psi
@Strain 3.17 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 15.0 MPa
@Strain 3.95 %,
Temperature 60.0 °C		2180 psi
@Strain 3.95 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 15.0 MPa
@Strain 3.42 %,
Temperature 60.0 °C		2180 psi
@Strain 3.42 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 15.0 MPa
@Strain 0.663 %,
Temperature 23.0 °C		2180 psi
@Strain 0.663 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 15.0 MPa
@Strain 0.602 %,
Temperature 23.0 °C		2180 psi
@Strain 0.602 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 17.0 MPa
@Strain 4.10 %,
Temperature 60.0 °C		2470 psi
@Strain 4.10 %,
Temperature 140 °F		1h; Break; Isochronous; ISO 899
 17.0 MPa
@Strain 4.73 %,
Temperature 60.0 °C		2470 psi
@Strain 4.73 %,
Temperature 140 °F		10h; Break; Isochronous; ISO 899
 20.0 MPa
@Strain 0.905 %,
Temperature 23.0 °C		2900 psi
@Strain 0.905 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.814 %,
Temperature 23.0 °C		2900 psi
@Strain 0.814 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 25.0 MPa
@Strain 1.17 %,
Temperature 23.0 °C		3630 psi
@Strain 1.17 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 25.0 MPa
@Strain 1.04 %,
Temperature 23.0 °C		3630 psi
@Strain 1.04 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 30.0 MPa
@Strain 1.28 %,
Temperature 23.0 °C		4350 psi
@Strain 1.28 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 30.0 MPa
@Strain 1.49 %,
Temperature 23.0 °C		4350 psi
@Strain 1.49 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 35.0 MPa
@Strain 1.91 %,
Temperature 23.0 °C		5080 psi
@Strain 1.91 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 35.0 MPa
@Strain 1.56 %,
Temperature 23.0 °C		5080 psi
@Strain 1.56 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 40.0 MPa
@Strain 1.90 %,
Temperature 23.0 °C		5800 psi
@Strain 1.90 %,
Temperature 73.4 °F		1h; Break; Isochronous; ISO 899
 40.0 MPa
@Strain 2.72 %,
Temperature 23.0 °C		5800 psi
@Strain 2.72 %,
Temperature 73.4 °F		10h; Break; Isochronous; ISO 899
Tensile Creep Modulus, 1000 hours 1800 MPa
@Temperature 23.0 °C		261000 psi
@Temperature 73.4 °F		ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 2.50 MPa
@Strain 0.794 %,
Temperature 60.0 °C		363 psi
@Strain 0.794 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 2.50 MPa
@Strain 0.692 %,
Temperature 60.0 °C		363 psi
@Strain 0.692 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 5.00 MPa
@Strain 1.37 %,
Temperature 60.0 °C		725 psi
@Strain 1.37 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 5.00 MPa
@Strain 1.56 %,
Temperature 60.0 °C		725 psi
@Strain 1.56 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.246 %,
Temperature 23.0 °C		725 psi
@Strain 0.246 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.280 %,
Temperature 23.0 °C		725 psi
@Strain 0.280 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 7.50 MPa
@Strain 2.06 %,
Temperature 60.0 °C		1090 psi
@Strain 2.06 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 7.50 MPa
@Strain 2.32 %,
Temperature 60.0 °C		1090 psi
@Strain 2.32 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 10.0 MPa
@Strain 3.11 %,
Temperature 60.0 °C		1450 psi
@Strain 3.11 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.493 %,
Temperature 23.0 °C		1450 psi
@Strain 0.493 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 10.0 MPa
@Strain 2.78 %,
Temperature 60.0 °C		1450 psi
@Strain 2.78 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.560 %,
Temperature 23.0 °C		1450 psi
@Strain 0.560 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 12.5 MPa
@Strain 3.56 %,
Temperature 60.0 °C		1810 psi
@Strain 3.56 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 12.5 MPa
@Strain 3.95 %,
Temperature 60.0 °C		1810 psi
@Strain 3.95 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 15.0 MPa
@Strain 4.90 %,
Temperature 60.0 °C		2180 psi
@Strain 4.90 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 15.0 MPa
@Strain 0.750 %,
Temperature 23.0 °C		2180 psi
@Strain 0.750 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 15.0 MPa
@Strain 4.46 %,
Temperature 60.0 °C		2180 psi
@Strain 4.46 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 15.0 MPa
@Strain 0.880 %,
Temperature 23.0 °C		2180 psi
@Strain 0.880 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 17.0 MPa
@Strain 5.33 %,
Temperature 60.0 °C		2470 psi
@Strain 5.33 %,
Temperature 140 °F		100h; Break; Isochronous; ISO 899
 17.0 MPa
@Strain 5.81 %,
Temperature 60.0 °C		2470 psi
@Strain 5.81 %,
Temperature 140 °F		1000h; Break; Isochronous; ISO 899
 20.0 MPa
@Strain 1.02 %,
Temperature 23.0 °C		2900 psi
@Strain 1.02 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 20.0 MPa
@Strain 1.30 %,
Temperature 23.0 °C		2900 psi
@Strain 1.30 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 25.0 MPa
@Strain 1.33 %,
Temperature 23.0 °C		3630 psi
@Strain 1.33 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 25.0 MPa
@Strain 1.80 %,
Temperature 23.0 °C		3630 psi
@Strain 1.80 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 30.0 MPa
@Strain 2.55 %,
Temperature 23.0 °C		4350 psi
@Strain 2.55 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 30.0 MPa
@Strain 1.70 %,
Temperature 23.0 °C		4350 psi
@Strain 1.70 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 35.0 MPa
@Strain 2.21 %,
Temperature 23.0 °C		5080 psi
@Strain 2.21 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 35.0 MPa
@Strain 3.80 %,
Temperature 23.0 °C		5080 psi
@Strain 3.80 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 40.0 MPa
@Strain 6.30 %,
Temperature 23.0 °C		5800 psi
@Strain 6.30 %,
Temperature 73.4 °F		1000h; Break; Isochronous; ISO 899
 40.0 MPa
@Strain 3.50 %,
Temperature 23.0 °C		5800 psi
@Strain 3.50 %,
Temperature 73.4 °F		100h; Break; Isochronous; ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity >= 1.00e+15 ohm-cm
@Temperature 23.0 °C		>= 1.00e+15 ohm-cm
@Temperature 73.4 °F		IEC 60093
Surface Resistance 1.00e+15 ohm
@Temperature 23.0 °C		1.00e+15 ohm
@Temperature 73.4 °F		IEC 60093
Dielectric Constant  3.5
@Frequency 100 Hz,
Temperature 23.0 °C		3.5
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
 3.5
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.5
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
Dielectric Strength 25.0 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		635 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		IEC 60243-1
 15.0 kV/mm
@Thickness 2.00 mm,
Time 20.0 sec		381 kV/in
@Thickness 0.0787 in,
Time 0.00556 hour		IEC 60243-1
Dissipation Factor  0.0017
@Frequency 100 Hz,
Temperature 23.0 °C		0.0017
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
 0.018
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.018
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
Comparative Tracking Index  225 V
@Temperature 23.0 °C		225 V
@Temperature 73.4 °F		IEC 60112
 250 V
@Temperature 23.0 °C		250 V
@Temperature 73.4 °F		UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  120 µm/m-°C
@Temperature 23.0 - 55.0 °C		66.7 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 120 µm/m-°C
@Temperature 23.0 - 55.0 °C		66.7 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi) 160 °C320 °FISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C149 °FISO 75-1/-2
UL RTI, Electrical  130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 6.00 mm		266 °F
@Thickness 0.236 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical with Impact  130 °C
@Thickness 6.00 mm		266 °F
@Thickness 0.236 in		UL 746B
 130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical without Impact  130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 6.00 mm		266 °F
@Thickness 0.236 in		UL 746B
Flammability, UL94  V-0
@Thickness 6.00 mm		V-0
@Thickness 0.236 in		IEC 60695-11-10
 V-0
@Thickness 3.00 mm		V-0
@Thickness 0.118 in		IEC 60695-11-10
 V-0
@Thickness 0.750 mm		V-0
@Thickness 0.0295 in		IEC 60695-11-10
 V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		IEC 60695-11-10
 V-0
@Thickness 6.00 mm		V-0
@Thickness 0.236 in		UL94
 V-0
@Thickness 0.750 mm		V-0
@Thickness 0.0295 in		UL94
 V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		UL94
 V-0
@Thickness 3.00 mm		V-0
@Thickness 0.118 in		UL94
Oxygen Index 30 %30 %ISO 4589-1/-2
Glow Wire Test 960 °C
@Thickness 3.00 mm		1760 °F
@Thickness 0.118 in		IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 225 °C437 °F10°C/min; ISO 11357-1/-3
 250 °C482 °FOptimum
 240 - 260 °C464 - 500 °F
Mold Temperature 80.0 °C176 °Foptimum
 30.0 - 130 °C86.0 - 266 °F
Drying Temperature 110 - 130 °C230 - 266 °F
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hour
Moisture Content <= 0.040 %<= 0.040 %
 
Descriptive Properties
AppearanceNatural Color
Contains Flame RetardantYes
Drying RecommendedYes
FeaturesFlame Retardant
FormsPellets
GenericPBT
Material StatusCurrent
Part Marking Code>PBT-FR(17)<ISO 11469
Polymer FamilyPolyester
Polymer TypePBT
Processing MethodInjection Molding
Product CategoryFlame Retardant Resins
 Unreinforced Resins
Region Available - GlobalYes
Resin IdentificationPBT-FR(17)ISO 1043
RoHS ComplianceContact Manufacturer
Ultrasonic WeldableYes

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38079.html

免责声明: 本文 DuPont Performance Polymers Crastin® S650FR NC010 PBT 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4