塑胶原料之家
  1. 首页
  2. 英文物性
  3. PBT
  4. DuPont Performance Polymers Crastin® SK603 NC010 PBT

DuPont Performance Polymers Crastin® SK603 NC010 PBT

DuPont Performance Polymers Crastin® SK603 NC010 PBT 物性表: DuPont Performance Polymers Crastin® SK603 NC010 PBT物性表及特性介绍,DuPont Performance Polymers Crastin® SK603 NC010 PBT注塑参数详情,如需DuPont Performance Polymers Crastin® SK603 NC010 PBT下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.45
  • 吸水率 [%]: 0.15
  • 缺口冲击强度: 0.64
  • 弯曲模量 [MPa]: 2.068
  • 热变形温度 [℃]: 220.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.45 g/cc1.45 g/ccASTM D792
Density 1.45 g/cc0.0524 lb/in³ISO 1183
Filler Content 20 %20 %
Water Absorption  0.15 %
@Temperature 23.0 °C		0.15 %
@Temperature 73.4 °F		Equilibrium 50%RH; ISO 62, Similar to
 0.40 %
@Temperature 23.0 °C		0.40 %
@Temperature 73.4 °F		Saturation, immersed; ISO 62, Similar to
Viscosity  63000 cP
@Shear Rate 10000 1/s,
Temperature 260 °C		63000 cP
@Shear Rate 10000 1/s,
Temperature 500 °F		ISO 11443
 79000 cP
@Shear Rate 10000 1/s,
Temperature 250 °C		79000 cP
@Shear Rate 10000 1/s,
Temperature 482 °F		ISO 11443
 87000 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		87000 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		ISO 11443
 101000 cP
@Shear Rate 10000 1/s,
Temperature 240 °C		101000 cP
@Shear Rate 10000 1/s,
Temperature 464 °F		ISO 11443
 109000 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		109000 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		ISO 11443
 133000 cP
@Shear Rate 2000 1/s,
Temperature 260 °C		133000 cP
@Shear Rate 2000 1/s,
Temperature 500 °F		ISO 11443
 140000 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		140000 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		ISO 11443
 168000 cP
@Shear Rate 2000 1/s,
Temperature 250 °C		168000 cP
@Shear Rate 2000 1/s,
Temperature 482 °F		ISO 11443
 181000 cP
@Shear Rate 1000 1/s,
Temperature 260 °C		181000 cP
@Shear Rate 1000 1/s,
Temperature 500 °F		ISO 11443
 216000 cP
@Shear Rate 2000 1/s,
Temperature 240 °C		216000 cP
@Shear Rate 2000 1/s,
Temperature 464 °F		ISO 11443
 230000 cP
@Shear Rate 1000 1/s,
Temperature 250 °C		230000 cP
@Shear Rate 1000 1/s,
Temperature 482 °F		ISO 11443
 241000 cP
@Shear Rate 500 1/s,
Temperature 260 °C		241000 cP
@Shear Rate 500 1/s,
Temperature 500 °F		ISO 11443
 297000 cP
@Shear Rate 1000 1/s,
Temperature 240 °C		297000 cP
@Shear Rate 1000 1/s,
Temperature 464 °F		ISO 11443
 311000 cP
@Shear Rate 500 1/s,
Temperature 250 °C		311000 cP
@Shear Rate 500 1/s,
Temperature 482 °F		ISO 11443
 401000 cP
@Shear Rate 100 1/s,
Temperature 260 °C		401000 cP
@Shear Rate 100 1/s,
Temperature 500 °F		ISO 11443
 406000 cP
@Shear Rate 500 1/s,
Temperature 240 °C		406000 cP
@Shear Rate 500 1/s,
Temperature 464 °F		ISO 11443
 552000 cP
@Shear Rate 100 1/s,
Temperature 250 °C		552000 cP
@Shear Rate 100 1/s,
Temperature 482 °F		ISO 11443
 764000 cP
@Shear Rate 100 1/s,
Temperature 240 °C		764000 cP
@Shear Rate 100 1/s,
Temperature 464 °F		ISO 11443
Linear Mold Shrinkage 0.0040 cm/cm0.0040 in/inFlow
 0.011 cm/cm0.011 in/inTransverse
Linear Mold Shrinkage, Flow 0.0050 cm/cm0.0050 in/inParallel; Annealed; ISO 294-4
 0.0035 cm/cm
@Thickness 2.00 mm		0.0035 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0135 cm/cm0.0135 in/inNormal; Annealed; ISO 294-4
 0.0105 cm/cm
@Thickness 2.00 mm		0.0105 in/in
@Thickness 0.0787 in		Normal; ISO 294-4
Melt Index of Compound 15 g/10 min
@Load 2.16 kg,
Temperature 250 °C		15 g/10 min
@Load 4.76 lb,
Temperature 482 °F		cm3/10 min; ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 125 MPa
@Temperature 23.0 °C		18100 psi
@Temperature 73.4 °F		ISO 527
Tensile Strength  48.0 MPa
@Temperature 149 °C		6960 psi
@Temperature 300 °F		ASTM D638
 63.0 MPa
@Temperature 90.0 °C		9140 psi
@Temperature 194 °F		ASTM D638
 117 MPa
@Temperature 23.0 °C		17000 psi
@Temperature 73.4 °F		ASTM D638
 182 MPa
@Temperature -40.0 °C		26400 psi
@Temperature -40.0 °F		ASTM D638
Tensile Stress  21.6 MPa
@Strain 0.300 %,
Temperature 23.0 °C		3130 psi
@Strain 0.300 %,
Temperature 73.4 °F		ISO 527
 41.1 MPa
@Strain 0.600 %,
Temperature 23.0 °C		5960 psi
@Strain 0.600 %,
Temperature 73.4 °F		ISO 527
 58.4 MPa
@Strain 0.900 %,
Temperature 23.0 °C		8470 psi
@Strain 0.900 %,
Temperature 73.4 °F		ISO 527
 73.5 MPa
@Strain 1.20 %,
Temperature 23.0 °C		10700 psi
@Strain 1.20 %,
Temperature 73.4 °F		ISO 527
 86.3 MPa
@Strain 1.50 %,
Temperature 23.0 °C		12500 psi
@Strain 1.50 %,
Temperature 73.4 °F		ISO 527
 96.7 MPa
@Strain 1.80 %,
Temperature 23.0 °C		14000 psi
@Strain 1.80 %,
Temperature 73.4 °F		ISO 527
 105 MPa
@Strain 2.10 %,
Temperature 23.0 °C		15200 psi
@Strain 2.10 %,
Temperature 73.4 °F		ISO 527
 111 MPa
@Strain 2.40 %,
Temperature 23.0 °C		16100 psi
@Strain 2.40 %,
Temperature 73.4 °F		ISO 527
 114 MPa
@Strain 2.70 %,
Temperature 23.0 °C		16500 psi
@Strain 2.70 %,
Temperature 73.4 °F		ISO 527
 115 MPa
@Strain 3.30 %,
Temperature 23.0 °C		16700 psi
@Strain 3.30 %,
Temperature 73.4 °F		Break; ISO 527
Elongation at Break  2.2 %
@Temperature -40.0 °C		2.2 %
@Temperature -40.0 °F		ASTM D638
 3.2 %
@Temperature 23.0 °C		3.2 %
@Temperature 73.4 °F		ISO 527
 3.3 %
@Temperature 23.0 °C		3.3 %
@Temperature 73.4 °F		ASTM D638
 4.8 %
@Temperature 90.0 °C		4.8 %
@Temperature 194 °F		ASTM D638
 5.2 %
@Temperature 150 °C		5.2 %
@Temperature 302 °F		ASTM D638
Tensile Modulus  7.40 GPa
@Temperature 23.0 °C		1070 ksi
@Temperature 73.4 °F		ISO 527
 7.482 GPa
@Temperature 23.0 °C		1085 ksi
@Temperature 73.4 °F		ASTM D638
Flexural Strength  61.0 MPa
@Temperature 149 °C		8850 psi
@Temperature 300 °F		ASTM D790
 72.0 MPa
@Temperature 90.0 °C		10400 psi
@Temperature 194 °F		ASTM D790
 179 MPa
@Temperature 23.0 °C		26000 psi
@Temperature 73.4 °F		ASTM D790
 180 MPa
@Temperature 23.0 °C		26100 psi
@Temperature 73.4 °F		ISO 178
 242 MPa
@Temperature -40.0 °C		35100 psi
@Temperature -40.0 °F		ASTM D790
Flexural Modulus  2.068 GPa
@Temperature 149 °C		299.9 ksi
@Temperature 300 °F		ASTM D790
 2.758 GPa
@Temperature 90.0 °C		400.0 ksi
@Temperature 194 °F		ASTM D790
 6.137 GPa
@Temperature 23.0 °C		890.1 ksi
@Temperature 73.4 °F		ASTM D790
 6.20 GPa
@Temperature 23.0 °C		899 ksi
@Temperature 73.4 °F		ISO 178
 7.241 GPa
@Temperature -40.0 °C		1050 ksi
@Temperature -40.0 °F		ASTM D790
Compressive Strength 161 MPa
@Temperature 23.0 °C		23400 psi
@Temperature 73.4 °F		ASTM D695
Shear Modulus  0.280 GPa
@Temperature 200 °C		40.6 ksi
@Temperature 392 °F		ISO 6721
 0.303 GPa
@Temperature 190 °C		43.9 ksi
@Temperature 374 °F		ISO 6721
 0.327 GPa
@Temperature 180 °C		47.4 ksi
@Temperature 356 °F		ISO 6721
 0.337 GPa
@Temperature 170 °C		48.9 ksi
@Temperature 338 °F		ISO 6721
 0.365 GPa
@Temperature 160 °C		52.9 ksi
@Temperature 320 °F		ISO 6721
 0.391 GPa
@Temperature 150 °C		56.7 ksi
@Temperature 302 °F		ISO 6721
 0.417 GPa
@Temperature 140 °C		60.5 ksi
@Temperature 284 °F		ISO 6721
 0.444 GPa
@Temperature 130 °C		64.4 ksi
@Temperature 266 °F		ISO 6721
 0.471 GPa
@Temperature 120 °C		68.3 ksi
@Temperature 248 °F		ISO 6721
 0.499 GPa
@Temperature 110 °C		72.4 ksi
@Temperature 230 °F		ISO 6721
 0.532 GPa
@Temperature 100 °C		77.2 ksi
@Temperature 212 °F		ISO 6721
 0.571 GPa
@Temperature 90.0 °C		82.8 ksi
@Temperature 194 °F		ISO 6721
 0.624 GPa
@Temperature 80.0 °C		90.5 ksi
@Temperature 176 °F		ISO 6721
 0.704 GPa
@Temperature 70.0 °C		102 ksi
@Temperature 158 °F		ISO 6721
 0.828 GPa
@Temperature 60.0 °C		120 ksi
@Temperature 140 °F		ISO 6721
 1.02 GPa
@Temperature 50.0 °C		148 ksi
@Temperature 122 °F		ISO 6721
 1.32 GPa
@Temperature 40.0 °C		191 ksi
@Temperature 104 °F		ISO 6721
 1.49 GPa
@Temperature 30.0 °C		216 ksi
@Temperature 86.0 °F		ISO 6721
 1.54 GPa
@Temperature 20.0 °C		223 ksi
@Temperature 68.0 °F		ISO 6721
 1.57 GPa
@Temperature 10.0 °C		228 ksi
@Temperature 50.0 °F		ISO 6721
 1.60 GPa
@Temperature 0.000 °C		232 ksi
@Temperature 32.0 °F		ISO 6721
 1.63 GPa
@Temperature -10.0 °C		236 ksi
@Temperature 14.0 °F		ISO 6721
 1.66 GPa
@Temperature -20.0 °C		241 ksi
@Temperature -4.00 °F		ISO 6721
 1.69 GPa
@Temperature -30.0 °C		245 ksi
@Temperature -22.0 °F		ISO 6721
 1.73 GPa
@Temperature -40.0 °C		251 ksi
@Temperature -40.0 °F		ISO 6721
 1.77 GPa
@Temperature -50.0 °C		257 ksi
@Temperature -58.0 °F		ISO 6721
Izod Impact, Notched  0.640 J/cm
@Temperature -40.0 °C		1.20 ft-lb/in
@Temperature -40.0 °F		ASTM D256
 0.690 J/cm
@Temperature 23.0 °C		1.29 ft-lb/in
@Temperature 73.4 °F		ASTM D256
Izod Impact, Unnotched  7.36 J/cm
@Temperature -40.0 °C		13.8 ft-lb/in
@Temperature -40.0 °F		ASTM D4812
 7.36 J/cm
@Temperature 23.0 °C		13.8 ft-lb/in
@Temperature 73.4 °F		ASTM D4812
Izod Impact, Notched (ISO)  8.00 kJ/m²
@Temperature -30.0 °C		3.81 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1A
 9.00 kJ/m²
@Temperature 23.0 °C		4.28 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1A
Izod Impact, Unnotched (ISO)  60.0 kJ/m²
@Temperature -30.0 °C		28.6 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1U
 60.0 kJ/m²
@Temperature 23.0 °C		28.6 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1U
Charpy Impact Unnotched  5.50 J/cm²
@Temperature -30.0 °C		26.2 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
 6.00 J/cm²
@Temperature 23.0 °C		28.6 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched  0.800 J/cm²
@Temperature 23.0 °C		3.81 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
 0.900 J/cm²
@Temperature -30.0 °C		4.28 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
Tensile Creep Modulus, 1 hour 7200 MPa
@Temperature 23.0 °C		1.04e+6 psi
@Temperature 73.4 °F		ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.152 %,
Temperature 23.0 °C		1450 psi
@Strain 0.152 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.143 %,
Temperature 23.0 °C		1450 psi
@Strain 0.143 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.286 %,
Temperature 23.0 °C		2900 psi
@Strain 0.286 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.303 %,
Temperature 23.0 °C		2900 psi
@Strain 0.303 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.456 %,
Temperature 23.0 °C		4350 psi
@Strain 0.456 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.433 %,
Temperature 23.0 °C		4350 psi
@Strain 0.433 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.585 %,
Temperature 23.0 °C		5800 psi
@Strain 0.585 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.615 %,
Temperature 23.0 °C		5800 psi
@Strain 0.615 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.785 %,
Temperature 23.0 °C		7250 psi
@Strain 0.785 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.745 %,
Temperature 23.0 °C		7250 psi
@Strain 0.745 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 60.0 MPa
@Strain 0.917 %,
Temperature 23.0 °C		8700 psi
@Strain 0.917 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 60.0 MPa
@Strain 0.971 %,
Temperature 23.0 °C		8700 psi
@Strain 0.971 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 70.0 MPa
@Strain 1.18 %,
Temperature 23.0 °C		10200 psi
@Strain 1.18 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 70.0 MPa
@Strain 1.11 %,
Temperature 23.0 °C		10200 psi
@Strain 1.11 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 80.0 MPa
@Strain 1.32 %,
Temperature 23.0 °C		11600 psi
@Strain 1.32 %,
Temperature 73.4 °F		1h; Break; Isochronous; ISO 899
 80.0 MPa
@Strain 1.45 %,
Temperature 23.0 °C		11600 psi
@Strain 1.45 %,
Temperature 73.4 °F		10h; Break; Isochronous; ISO 899
Tensile Creep Modulus, 1000 hours 5600 MPa
@Temperature 23.0 °C		812000 psi
@Temperature 73.4 °F		ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.170 %,
Temperature 23.0 °C		1450 psi
@Strain 0.170 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.179 %,
Temperature 23.0 °C		1450 psi
@Strain 0.179 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.360 %,
Temperature 23.0 °C		2900 psi
@Strain 0.360 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.340 %,
Temperature 23.0 °C		2900 psi
@Strain 0.340 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.512 %,
Temperature 23.0 °C		4350 psi
@Strain 0.512 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.550 %,
Temperature 23.0 °C		4350 psi
@Strain 0.550 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.752 %,
Temperature 23.0 °C		5800 psi
@Strain 0.752 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.690 %,
Temperature 23.0 °C		5800 psi
@Strain 0.690 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.881 %,
Temperature 23.0 °C		7250 psi
@Strain 0.881 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.975 %,
Temperature 23.0 °C		7250 psi
@Strain 0.975 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 60.0 MPa
@Strain 1.23 %,
Temperature 23.0 °C		8700 psi
@Strain 1.23 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 60.0 MPa
@Strain 1.09 %,
Temperature 23.0 °C		8700 psi
@Strain 1.09 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 70.0 MPa
@Strain 1.34 %,
Temperature 23.0 °C		10200 psi
@Strain 1.34 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 70.0 MPa
@Strain 1.56 %,
Temperature 23.0 °C		10200 psi
@Strain 1.56 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 80.0 MPa
@Strain 2.03 %,
Temperature 23.0 °C		11600 psi
@Strain 2.03 %,
Temperature 73.4 °F		1000h; Break; Isochronous; ISO 899
 80.0 MPa
@Strain 1.66 %,
Temperature 23.0 °C		11600 psi
@Strain 1.66 %,
Temperature 73.4 °F		100h; Break; Isochronous; ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  >= 1.00e+15 ohm-cm
@Temperature 23.0 °C		>= 1.00e+15 ohm-cm
@Temperature 73.4 °F		IEC 60093
 2.00e+15 ohm-cm
@Temperature 23.0 °C		2.00e+15 ohm-cm
@Temperature 73.4 °F		ASTM D257
Surface Resistance  1.60e+13 ohm
@Temperature 23.0 °C		1.60e+13 ohm
@Temperature 73.4 °F		ASTM D257
 1.00e+15 ohm
@Temperature 23.0 °C		1.00e+15 ohm
@Temperature 73.4 °F		IEC 60093
Dielectric Constant  3.6
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.6
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		ASTM D150
 3.6
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.6
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
 3.8
@Frequency 1000 Hz,
Temperature 23.0 °C		3.8
@Frequency 1000 Hz,
Temperature 73.4 °F		ASTM D150
 4.2
@Frequency 100 Hz,
Temperature 23.0 °C		4.2
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
Dielectric Strength  17.0 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C		432 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F		Short Time; ASTM D149
 22.0 kV/mm
@Thickness 1.60 mm,
Temperature 23.0 °C		559 kV/in
@Thickness 0.0630 in,
Temperature 73.4 °F		Short Time; ASTM D149
 29.0 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		737 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		IEC 60243-1
 17.0 kV/mm
@Thickness 2.00 mm,
Time 20.0 sec		432 kV/in
@Thickness 0.0787 in,
Time 0.00556 hour		IEC 60243-1
Dissipation Factor  0.0021
@Frequency 100 Hz,
Temperature 23.0 °C		0.0021
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
 0.0060
@Frequency 1000 Hz,
Temperature 23.0 °C		0.0060
@Frequency 1000 Hz,
Temperature 73.4 °F		ASTM D150
 0.019
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.019
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		ASTM D150
 0.019
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.019
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
Comparative Tracking Index  250 V
@Temperature 23.0 °C		250 V
@Temperature 73.4 °F		UL 746A
 400 V
@Temperature 23.0 °C		400 V
@Temperature 73.4 °F		IEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  100 µm/m-°C
@Temperature 23.0 - 55.0 °C		55.6 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 100 µm/m-°C
@Temperature 23.0 - 55.0 °C		55.6 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
Melting Point 225 °C437 °FASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 220 °C428 °FISO 75-1/-2
 220 °C428 °FASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 203 °C397 °FASTM D648
 204 °C399 °FISO 75-1/-2
Deflection Temperature at 5.0 MPa 164 °C327 °F4x100x100mm plaque; ISO 75-1/-2
Deflection Temperature at 8.0 MPa 93.0 °C199 °FISO 75-1/-2
UL RTI, Electrical  130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 6.00 mm		266 °F
@Thickness 0.236 in		UL 746B
 130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical with Impact  130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
 130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 6.00 mm		266 °F
@Thickness 0.236 in		UL 746B
UL RTI, Mechanical without Impact  130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
 130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 6.00 mm		266 °F
@Thickness 0.236 in		UL 746B
Flammability, UL94  HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		IEC 60695-11-10
 HB
@Thickness 6.00 mm		HB
@Thickness 0.236 in		IEC 60695-11-10
 HB
@Thickness 6.00 mm		HB
@Thickness 0.236 in		UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		UL94
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		UL94
Oxygen Index 19 %19 %ISO 4589-1/-2
 19 %
@Thickness 3.20 mm		19 %
@Thickness 0.126 in		ASTM D2863
Glow Wire Test 750 °C
@Thickness 3.00 mm		1380 °F
@Thickness 0.118 in		IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 225 °C437 °F10°C/min; ISO 11357-1/-3
 250 °C482 °FOptimum
 240 - 260 °C464 - 500 °F
Mold Temperature 80.0 °C176 °Foptimum
 30.0 - 130 °C86.0 - 266 °F
Drying Temperature 110 - 130 °C230 - 266 °F
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hour
Moisture Content <= 0.040 %<= 0.040 %
 
Descriptive Properties
AdditiveLubricant
AppearanceNatural Color
Drying RecommendedYes
FeaturesChemical Resistance, Good
 Dimensional Stability, Good
 Lubricated
 Moisture Absorption, Low
 Processability, Good
 Stiffness, Good
 Strength, Good
FillerGlass fiber reinforcement
FormsPellets
GenericPBT
Material StatusCurrent
Part Marking Code>PBT-GF20<ISO 11469
Polymer FamilyPolyester
Polymer TypePBT
Processing MethodInjection Molding
Product CategoryGlass Reinforced Resins
Region Available - GlobalYes
Resin IdentificationPBT-GF20ISO 1043
RoHS ComplianceContact Manufacturer
Ultrasonic WeldableYes
UsesAutomotive Applications
 General Purpose
 Industrial Applications
 Parts, Engineering
 Parts, Machine/Mechanical
 Structural Parts

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38092.html

免责声明: 本文 DuPont Performance Polymers Crastin® SK603 NC010 PBT 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4