  4. DuPont Performance Polymers Crastin® SK641FR NC010 PBT

DuPont Performance Polymers Crastin® SK641FR NC010 PBT

DuPont Performance Polymers Crastin® SK641FR NC010 PBT 物性表: DuPont Performance Polymers Crastin® SK641FR NC010 PBT物性表及特性介绍,DuPont Performance Polymers Crastin® SK641FR NC010 PBT注塑参数详情,如需DuPont Performance Polymers Crastin® SK641FR NC010 PBT下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.54
  • 吸水率 [%]: 0.15
  • 缺口冲击强度: 5.0
  • 热变形温度 [℃]: 215.0
 
Physical PropertiesMetricEnglishComments
Density 1.54 g/cc0.0556 lb/in³ISO 1183
Water Absorption  0.15 %
@Temperature 23.0 °C		0.15 %
@Temperature 73.4 °F		Equilibrium 50%RH; ISO 62, Similar to
 0.35 %
@Temperature 23.0 °C		0.35 %
@Temperature 73.4 °F		Saturation, immersed; ISO 62, Similar to
Viscosity  48000 cP
@Shear Rate 10000 1/s,
Temperature 260 °C		48000 cP
@Shear Rate 10000 1/s,
Temperature 500 °F		ISO 11443
 65000 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		65000 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		ISO 11443
 65000 cP
@Shear Rate 10000 1/s,
Temperature 250 °C		65000 cP
@Shear Rate 10000 1/s,
Temperature 482 °F		ISO 11443
 87000 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		87000 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		ISO 11443
 89000 cP
@Shear Rate 10000 1/s,
Temperature 240 °C		89000 cP
@Shear Rate 10000 1/s,
Temperature 464 °F		ISO 11443
 94000 cP
@Shear Rate 2000 1/s,
Temperature 260 °C		94000 cP
@Shear Rate 2000 1/s,
Temperature 500 °F		ISO 11443
 119000 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		119000 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		ISO 11443
 122000 cP
@Shear Rate 1000 1/s,
Temperature 260 °C		122000 cP
@Shear Rate 1000 1/s,
Temperature 500 °F		ISO 11443
 127000 cP
@Shear Rate 2000 1/s,
Temperature 250 °C		127000 cP
@Shear Rate 2000 1/s,
Temperature 482 °F		ISO 11443
 154000 cP
@Shear Rate 500 1/s,
Temperature 260 °C		154000 cP
@Shear Rate 500 1/s,
Temperature 500 °F		ISO 11443
 166000 cP
@Shear Rate 1000 1/s,
Temperature 250 °C		166000 cP
@Shear Rate 1000 1/s,
Temperature 482 °F		ISO 11443
 175000 cP
@Shear Rate 2000 1/s,
Temperature 240 °C		175000 cP
@Shear Rate 2000 1/s,
Temperature 464 °F		ISO 11443
 215000 cP
@Shear Rate 500 1/s,
Temperature 250 °C		215000 cP
@Shear Rate 500 1/s,
Temperature 482 °F		ISO 11443
 223000 cP
@Shear Rate 100 1/s,
Temperature 260 °C		223000 cP
@Shear Rate 100 1/s,
Temperature 500 °F		ISO 11443
 232000 cP
@Shear Rate 1000 1/s,
Temperature 240 °C		232000 cP
@Shear Rate 1000 1/s,
Temperature 464 °F		ISO 11443
 305000 cP
@Shear Rate 500 1/s,
Temperature 240 °C		305000 cP
@Shear Rate 500 1/s,
Temperature 464 °F		ISO 11443
 336000 cP
@Shear Rate 100 1/s,
Temperature 250 °C		336000 cP
@Shear Rate 100 1/s,
Temperature 482 °F		ISO 11443
 514000 cP
@Shear Rate 100 1/s,
Temperature 240 °C		514000 cP
@Shear Rate 100 1/s,
Temperature 464 °F		ISO 11443
Linear Mold Shrinkage, Flow 0.0095 cm/cm0.0095 in/inParallel; Annealed; ISO 294-4
 0.0080 cm/cm
@Thickness 2.00 mm		0.0080 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.016 cm/cm0.016 in/inNormal; Annealed; ISO 294-4
 0.013 cm/cm
@Thickness 2.00 mm		0.013 in/in
@Thickness 0.0787 in		Normal; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 93.0 MPa
@Temperature 23.0 °C		13500 psi
@Temperature 73.4 °F		ISO 527
Tensile Stress  3.73 MPa
@Strain 0.250 %,
Temperature 160 °C		541 psi
@Strain 0.250 %,
Temperature 320 °F		ISO 527
 4.52 MPa
@Strain 0.250 %,
Temperature 120 °C		656 psi
@Strain 0.250 %,
Temperature 248 °F		ISO 527
 5.15 MPa
@Strain 0.250 %,
Temperature 100 °C		747 psi
@Strain 0.250 %,
Temperature 212 °F		ISO 527
 5.78 MPa
@Strain 0.250 %,
Temperature 80.0 °C		838 psi
@Strain 0.250 %,
Temperature 176 °F		ISO 527
 6.85 MPa
@Strain 0.500 %,
Temperature 160 °C		994 psi
@Strain 0.500 %,
Temperature 320 °F		ISO 527
 7.60 MPa
@Strain 0.250 %,
Temperature 60.0 °C		1100 psi
@Strain 0.250 %,
Temperature 140 °F		ISO 527
 8.48 MPa
@Strain 0.500 %,
Temperature 120 °C		1230 psi
@Strain 0.500 %,
Temperature 248 °F		ISO 527
 9.70 MPa
@Strain 0.500 %,
Temperature 100 °C		1410 psi
@Strain 0.500 %,
Temperature 212 °F		ISO 527
 10.4 MPa
@Strain 0.250 %,
Temperature 40.0 °C		1510 psi
@Strain 0.250 %,
Temperature 104 °F		ISO 527
 10.9 MPa
@Strain 0.500 %,
Temperature 80.0 °C		1580 psi
@Strain 0.500 %,
Temperature 176 °F		ISO 527
 11.8 MPa
@Strain 1.00 %,
Temperature 160 °C		1710 psi
@Strain 1.00 %,
Temperature 320 °F		ISO 527
 12.5 MPa
@Strain 0.250 %,
Temperature 23.0 °C		1810 psi
@Strain 0.250 %,
Temperature 73.4 °F		ISO 527
 14.2 MPa
@Strain 0.500 %,
Temperature 60.0 °C		2060 psi
@Strain 0.500 %,
Temperature 140 °F		ISO 527
 15.0 MPa
@Strain 0.250 %,
Temperature 0.000 °C		2180 psi
@Strain 0.250 %,
Temperature 32.0 °F		ISO 527
 15.3 MPa
@Strain 1.00 %,
Temperature 120 °C		2220 psi
@Strain 1.00 %,
Temperature 248 °F		ISO 527
 15.5 MPa
@Strain 1.50 %,
Temperature 160 °C		2250 psi
@Strain 1.50 %,
Temperature 320 °F		ISO 527
 16.3 MPa
@Strain 0.250 %,
Temperature -20.0 °C		2360 psi
@Strain 0.250 %,
Temperature -4.00 °F		ISO 527
 17.0 MPa
@Strain 0.250 %,
Temperature -40.0 °C		2470 psi
@Strain 0.250 %,
Temperature -40.0 °F		ISO 527
 17.4 MPa
@Strain 1.00 %,
Temperature 100 °C		2520 psi
@Strain 1.00 %,
Temperature 212 °F		ISO 527
 18.4 MPa
@Strain 2.00 %,
Temperature 160 °C		2670 psi
@Strain 2.00 %,
Temperature 320 °F		ISO 527
 19.6 MPa
@Strain 1.00 %,
Temperature 80.0 °C		2840 psi
@Strain 1.00 %,
Temperature 176 °F		ISO 527
 20.3 MPa
@Strain 0.500 %,
Temperature 40.0 °C		2940 psi
@Strain 0.500 %,
Temperature 104 °F		ISO 527
 20.6 MPa
@Strain 2.50 %,
Temperature 160 °C		2990 psi
@Strain 2.50 %,
Temperature 320 °F		ISO 527
 21.0 MPa
@Strain 1.50 %,
Temperature 120 °C		3050 psi
@Strain 1.50 %,
Temperature 248 °F		ISO 527
 22.4 MPa
@Strain 3.00 %,
Temperature 160 °C		3250 psi
@Strain 3.00 %,
Temperature 320 °F		ISO 527
 23.5 MPa
@Strain 1.50 %,
Temperature 100 °C		3410 psi
@Strain 1.50 %,
Temperature 212 °F		ISO 527
 23.8 MPa
@Strain 3.50 %,
Temperature 160 °C		3450 psi
@Strain 3.50 %,
Temperature 320 °F		Break; ISO 527
 24.6 MPa
@Strain 0.500 %,
Temperature 23.0 °C		3570 psi
@Strain 0.500 %,
Temperature 73.4 °F		ISO 527
 25.1 MPa
@Strain 1.00 %,
Temperature 60.0 °C		3640 psi
@Strain 1.00 %,
Temperature 140 °F		ISO 527
 25.7 MPa
@Strain 2.00 %,
Temperature 120 °C		3730 psi
@Strain 2.00 %,
Temperature 248 °F		ISO 527
 26.4 MPa
@Strain 1.50 %,
Temperature 80.0 °C		3830 psi
@Strain 1.50 %,
Temperature 176 °F		ISO 527
 28.5 MPa
@Strain 2.00 %,
Temperature 100 °C		4130 psi
@Strain 2.00 %,
Temperature 212 °F		ISO 527
 29.5 MPa
@Strain 2.50 %,
Temperature 120 °C		4280 psi
@Strain 2.50 %,
Temperature 248 °F		ISO 527
 29.6 MPa
@Strain 0.500 %,
Temperature 0.000 °C		4290 psi
@Strain 0.500 %,
Temperature 32.0 °F		ISO 527
 31.8 MPa
@Strain 2.00 %,
Temperature 80.0 °C		4610 psi
@Strain 2.00 %,
Temperature 176 °F		ISO 527
 32.1 MPa
@Strain 3.00 %,
Temperature 120 °C		4660 psi
@Strain 3.00 %,
Temperature 248 °F		ISO 527
 32.1 MPa
@Strain 0.500 %,
Temperature -20.0 °C		4660 psi
@Strain 0.500 %,
Temperature -4.00 °F		ISO 527
 32.2 MPa
@Strain 2.50 %,
Temperature 100 °C		4670 psi
@Strain 2.50 %,
Temperature 212 °F		ISO 527
 33.5 MPa
@Strain 3.50 %,
Temperature 120 °C		4860 psi
@Strain 3.50 %,
Temperature 248 °F		Break; ISO 527
 33.5 MPa
@Strain 0.500 %,
Temperature -40.0 °C		4860 psi
@Strain 0.500 %,
Temperature -40.0 °F		ISO 527
 33.6 MPa
@Strain 1.50 %,
Temperature 60.0 °C		4870 psi
@Strain 1.50 %,
Temperature 140 °F		ISO 527
 34.9 MPa
@Strain 3.00 %,
Temperature 100 °C		5060 psi
@Strain 3.00 %,
Temperature 212 °F		ISO 527
 36.1 MPa
@Strain 2.50 %,
Temperature 80.0 °C		5240 psi
@Strain 2.50 %,
Temperature 176 °F		ISO 527
 36.7 MPa
@Strain 3.50 %,
Temperature 100 °C		5320 psi
@Strain 3.50 %,
Temperature 212 °F		Break; ISO 527
 37.2 MPa
@Strain 1.00 %,
Temperature 40.0 °C		5400 psi
@Strain 1.00 %,
Temperature 104 °F		ISO 527
 39.5 MPa
@Strain 3.00 %,
Temperature 80.0 °C		5730 psi
@Strain 3.00 %,
Temperature 176 °F		ISO 527
 40.1 MPa
@Strain 2.00 %,
Temperature 60.0 °C		5820 psi
@Strain 2.00 %,
Temperature 140 °F		ISO 527
 42.1 MPa
@Strain 3.50 %,
Temperature 80.0 °C		6110 psi
@Strain 3.50 %,
Temperature 176 °F		Break; ISO 527
 44.9 MPa
@Strain 2.50 %,
Temperature 60.0 °C		6510 psi
@Strain 2.50 %,
Temperature 140 °F		ISO 527
 46.4 MPa
@Strain 1.00 %,
Temperature 23.0 °C		6730 psi
@Strain 1.00 %,
Temperature 73.4 °F		ISO 527
 48.1 MPa
@Strain 3.00 %,
Temperature 60.0 °C		6980 psi
@Strain 3.00 %,
Temperature 140 °F		ISO 527
 49.4 MPa
@Strain 1.50 %,
Temperature 40.0 °C		7160 psi
@Strain 1.50 %,
Temperature 104 °F		ISO 527
 50.1 MPa
@Strain 3.50 %,
Temperature 60.0 °C		7270 psi
@Strain 3.50 %,
Temperature 140 °F		Break; ISO 527
 55.6 MPa
@Strain 1.00 %,
Temperature 0.000 °C		8060 psi
@Strain 1.00 %,
Temperature 32.0 °F		ISO 527
 57.3 MPa
@Strain 2.00 %,
Temperature 40.0 °C		8310 psi
@Strain 2.00 %,
Temperature 104 °F		ISO 527
 59.5 MPa
@Strain 1.00 %,
Temperature -20.0 °C		8630 psi
@Strain 1.00 %,
Temperature -4.00 °F		ISO 527
 61.7 MPa
@Strain 2.50 %,
Temperature 40.0 °C		8950 psi
@Strain 2.50 %,
Temperature 104 °F		ISO 527
 62.0 MPa
@Strain 1.00 %,
Temperature -40.0 °C		8990 psi
@Strain 1.00 %,
Temperature -40.0 °F		ISO 527
 63.6 MPa
@Strain 3.00 %,
Temperature 40.0 °C		9220 psi
@Strain 3.00 %,
Temperature 104 °F		ISO 527
 63.6 MPa
@Strain 1.50 %,
Temperature 23.0 °C		9220 psi
@Strain 1.50 %,
Temperature 73.4 °F		ISO 527
 63.9 MPa
@Strain 3.30 %,
Temperature 40.0 °C		9270 psi
@Strain 3.30 %,
Temperature 104 °F		Break; ISO 527
 74.6 MPa
@Strain 1.50 %,
Temperature 0.000 °C		10800 psi
@Strain 1.50 %,
Temperature 32.0 °F		ISO 527
 75.3 MPa
@Strain 2.00 %,
Temperature 23.0 °C		10900 psi
@Strain 2.00 %,
Temperature 73.4 °F		ISO 527
 79.6 MPa
@Strain 1.50 %,
Temperature -20.0 °C		11500 psi
@Strain 1.50 %,
Temperature -4.00 °F		ISO 527
 82.0 MPa
@Strain 2.50 %,
Temperature 23.0 °C		11900 psi
@Strain 2.50 %,
Temperature 73.4 °F		ISO 527
 82.6 MPa
@Strain 1.50 %,
Temperature -40.0 °C		12000 psi
@Strain 1.50 %,
Temperature -40.0 °F		ISO 527
 84.8 MPa
@Strain 3.10 %,
Temperature 23.0 °C		12300 psi
@Strain 3.10 %,
Temperature 73.4 °F		Break; ISO 527
 86.6 MPa
@Strain 2.00 %,
Temperature 0.000 °C		12600 psi
@Strain 2.00 %,
Temperature 32.0 °F		ISO 527
 92.9 MPa
@Strain 2.00 %,
Temperature -20.0 °C		13500 psi
@Strain 2.00 %,
Temperature -4.00 °F		ISO 527
 93.1 MPa
@Strain 2.50 %,
Temperature 0.000 °C		13500 psi
@Strain 2.50 %,
Temperature 32.0 °F		ISO 527
 95.0 MPa
@Strain 2.80 %,
Temperature 0.000 °C		13800 psi
@Strain 2.80 %,
Temperature 32.0 °F		Break; ISO 527
 96.9 MPa
@Strain 2.00 %,
Temperature -40.0 °C		14100 psi
@Strain 2.00 %,
Temperature -40.0 °F		ISO 527
 102 MPa
@Strain 2.50 %,
Temperature -20.0 °C		14800 psi
@Strain 2.50 %,
Temperature -4.00 °F		ISO 527
 105 MPa
@Strain 2.80 %,
Temperature -20.0 °C		15200 psi
@Strain 2.80 %,
Temperature -4.00 °F		Break; ISO 527
 108 MPa
@Strain 2.50 %,
Temperature -40.0 °C		15700 psi
@Strain 2.50 %,
Temperature -40.0 °F		ISO 527
 114 MPa
@Strain 2.80 %,
Temperature -40.0 °C		16500 psi
@Strain 2.80 %,
Temperature -40.0 °F		Break; ISO 527
Elongation at Break 3.6 %
@Temperature 23.0 °C		3.6 %
@Temperature 73.4 °F		ISO 527
Tensile Modulus 6.00 GPa
@Temperature 23.0 °C		870 ksi
@Temperature 73.4 °F		ISO 527
Flexural Strength 140 MPa
@Temperature 23.0 °C		20300 psi
@Temperature 73.4 °F		ISO 178
Shear Modulus  0.255 GPa
@Temperature 200 °C		37.0 ksi
@Temperature 392 °F		ISO 6721
 0.324 GPa
@Temperature 190 °C		47.0 ksi
@Temperature 374 °F		ISO 6721
 0.364 GPa
@Temperature 180 °C		52.8 ksi
@Temperature 356 °F		ISO 6721
 0.397 GPa
@Temperature 170 °C		57.6 ksi
@Temperature 338 °F		ISO 6721
 0.424 GPa
@Temperature 160 °C		61.5 ksi
@Temperature 320 °F		ISO 6721
 0.451 GPa
@Temperature 150 °C		65.4 ksi
@Temperature 302 °F		ISO 6721
 0.477 GPa
@Temperature 140 °C		69.2 ksi
@Temperature 284 °F		ISO 6721
 0.504 GPa
@Temperature 130 °C		73.1 ksi
@Temperature 266 °F		ISO 6721
 0.539 GPa
@Temperature 120 °C		78.2 ksi
@Temperature 248 °F		ISO 6721
 0.561 GPa
@Temperature 110 °C		81.4 ksi
@Temperature 230 °F		ISO 6721
 0.594 GPa
@Temperature 100 °C		86.2 ksi
@Temperature 212 °F		ISO 6721
 0.634 GPa
@Temperature 90.0 °C		92.0 ksi
@Temperature 194 °F		ISO 6721
 0.692 GPa
@Temperature 80.0 °C		100 ksi
@Temperature 176 °F		ISO 6721
 0.778 GPa
@Temperature 70.0 °C		113 ksi
@Temperature 158 °F		ISO 6721
 0.908 GPa
@Temperature 60.0 °C		132 ksi
@Temperature 140 °F		ISO 6721
 1.11 GPa
@Temperature 50.0 °C		161 ksi
@Temperature 122 °F		ISO 6721
 1.33 GPa
@Temperature 40.0 °C		193 ksi
@Temperature 104 °F		ISO 6721
 1.46 GPa
@Temperature 30.0 °C		212 ksi
@Temperature 86.0 °F		ISO 6721
 1.51 GPa
@Temperature 20.0 °C		219 ksi
@Temperature 68.0 °F		ISO 6721
 1.55 GPa
@Temperature 10.0 °C		225 ksi
@Temperature 50.0 °F		ISO 6721
 1.58 GPa
@Temperature 0.000 °C		229 ksi
@Temperature 32.0 °F		ISO 6721
 1.62 GPa
@Temperature -10.0 °C		235 ksi
@Temperature 14.0 °F		ISO 6721
 1.64 GPa
@Temperature -20.0 °C		238 ksi
@Temperature -4.00 °F		ISO 6721
 1.68 GPa
@Temperature -30.0 °C		244 ksi
@Temperature -22.0 °F		ISO 6721
 1.73 GPa
@Temperature -40.0 °C		251 ksi
@Temperature -40.0 °F		ISO 6721
 1.77 GPa
@Temperature -50.0 °C		257 ksi
@Temperature -58.0 °F		ISO 6721
Izod Impact, Notched (ISO)  5.00 kJ/m²
@Temperature -30.0 °C		2.38 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1A
 5.00 kJ/m²
@Temperature 23.0 °C		2.38 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1A
Izod Impact, Unnotched (ISO)  27.0 kJ/m²
@Temperature -30.0 °C		12.8 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1U
 30.0 kJ/m²
@Temperature 23.0 °C		14.3 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1U
Charpy Impact Unnotched  3.70 J/cm²
@Temperature -30.0 °C		17.6 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
 5.10 J/cm²
@Temperature 23.0 °C		24.3 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched  0.470 J/cm²
@Temperature -30.0 °C		2.24 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 0.650 J/cm²
@Temperature 23.0 °C		3.09 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
Tensile Creep Modulus, 1 hour 4600 MPa
@Temperature 23.0 °C		667000 psi
@Temperature 73.4 °F		ISO 899
 2690 MPa
@Temperature 23.0 °C,
Time 3.60e+7 sec		390000 psi
@Temperature 73.4 °F,
Time 10000 hour		60MPa; ISO 899
 2810 MPa
@Temperature 23.0 °C,
Time 3.60e+7 sec		408000 psi
@Temperature 73.4 °F,
Time 10000 hour		50MPa; ISO 899
 2880 MPa
@Temperature 23.0 °C,
Time 3.60e+7 sec		418000 psi
@Temperature 73.4 °F,
Time 10000 hour		40MPa; ISO 899
 2910 MPa
@Temperature 23.0 °C,
Time 3.60e+6 sec		422000 psi
@Temperature 73.4 °F,
Time 1000 hour		60MPa; ISO 899
 2970 MPa
@Temperature 23.0 °C,
Time 3.60e+7 sec		431000 psi
@Temperature 73.4 °F,
Time 10000 hour		30MPa; ISO 899
 3050 MPa
@Temperature 23.0 °C,
Time 3.60e+7 sec		442000 psi
@Temperature 73.4 °F,
Time 10000 hour		20MPa; ISO 899
 3050 MPa
@Temperature 23.0 °C,
Time 3.60e+6 sec		442000 psi
@Temperature 73.4 °F,
Time 1000 hour		50MPa; ISO 899
 3120 MPa
@Temperature 23.0 °C,
Time 3.60e+6 sec		453000 psi
@Temperature 73.4 °F,
Time 1000 hour		40MPa; ISO 899
 3210 MPa
@Temperature 23.0 °C,
Time 360000 sec		466000 psi
@Temperature 73.4 °F,
Time 100 hour		60MPa; ISO 899
 3230 MPa
@Temperature 23.0 °C,
Time 3.60e+7 sec		468000 psi
@Temperature 73.4 °F,
Time 10000 hour		10MPa; ISO 899
 3260 MPa
@Temperature 23.0 °C,
Time 3.60e+6 sec		473000 psi
@Temperature 73.4 °F,
Time 1000 hour		30MPa; ISO 899
 3320 MPa
@Temperature 23.0 °C,
Time 3.60e+6 sec		482000 psi
@Temperature 73.4 °F,
Time 1000 hour		20MPa; ISO 899
 3360 MPa
@Temperature 23.0 °C,
Time 360000 sec		487000 psi
@Temperature 73.4 °F,
Time 100 hour		50MPa; ISO 899
 3480 MPa
@Temperature 23.0 °C,
Time 3.60e+6 sec		505000 psi
@Temperature 73.4 °F,
Time 1000 hour		10MPa; ISO 899
 3510 MPa
@Temperature 23.0 °C,
Time 360000 sec		509000 psi
@Temperature 73.4 °F,
Time 100 hour		40MPa; ISO 899
 3570 MPa
@Temperature 23.0 °C,
Time 36000 sec		518000 psi
@Temperature 73.4 °F,
Time 10.0 hour		60MPa; ISO 899
 3660 MPa
@Temperature 23.0 °C,
Time 360000 sec		531000 psi
@Temperature 73.4 °F,
Time 100 hour		30MPa; ISO 899
 3730 MPa
@Temperature 23.0 °C,
Time 36000 sec		541000 psi
@Temperature 73.4 °F,
Time 10.0 hour		50MPa; ISO 899
 3740 MPa
@Temperature 23.0 °C,
Time 360000 sec		542000 psi
@Temperature 73.4 °F,
Time 100 hour		20MPa; ISO 899
 3850 MPa
@Temperature 23.0 °C,
Time 360000 sec		558000 psi
@Temperature 73.4 °F,
Time 100 hour		10MPa; ISO 899
 3880 MPa
@Temperature 23.0 °C,
Time 36000 sec		563000 psi
@Temperature 73.4 °F,
Time 10.0 hour		40MPa; ISO 899
 4000 MPa
@Temperature 23.0 °C,
Time 3600 sec		580000 psi
@Temperature 73.4 °F,
Time 1.00 hour		60MPa; ISO 899
 4050 MPa
@Temperature 23.0 °C,
Time 36000 sec		587000 psi
@Temperature 73.4 °F,
Time 10.0 hour		30MPa; ISO 899
 4170 MPa
@Temperature 23.0 °C,
Time 36000 sec		605000 psi
@Temperature 73.4 °F,
Time 10.0 hour		20MPa; ISO 899
 4240 MPa
@Temperature 23.0 °C,
Time 3600 sec		615000 psi
@Temperature 73.4 °F,
Time 1.00 hour		50MPa; ISO 899
 4310 MPa
@Temperature 23.0 °C,
Time 36000 sec		625000 psi
@Temperature 73.4 °F,
Time 10.0 hour		10MPa; ISO 899
 4440 MPa
@Temperature 23.0 °C,
Time 3600 sec		644000 psi
@Temperature 73.4 °F,
Time 1.00 hour		40MPa; ISO 899
 4620 MPa
@Temperature 23.0 °C,
Time 3600 sec		670000 psi
@Temperature 73.4 °F,
Time 1.00 hour		30MPa; ISO 899
 4760 MPa
@Temperature 23.0 °C,
Time 3600 sec		690000 psi
@Temperature 73.4 °F,
Time 1.00 hour		20MPa; ISO 899
 4880 MPa
@Temperature 23.0 °C,
Time 3600 sec		708000 psi
@Temperature 73.4 °F,
Time 1.00 hour		10MPa; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.242 %,
Temperature 60.0 °C		725 psi
@Strain 0.242 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.253 %,
Temperature 60.0 °C		725 psi
@Strain 0.253 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.509 %,
Temperature 60.0 °C		1450 psi
@Strain 0.509 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.480 %,
Temperature 60.0 °C		1450 psi
@Strain 0.480 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.232 %,
Temperature 23.0 °C		1450 psi
@Strain 0.232 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.205 %,
Temperature 23.0 °C		1450 psi
@Strain 0.205 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 15.0 MPa
@Strain 0.723 %,
Temperature 60.0 °C		2180 psi
@Strain 0.723 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 15.0 MPa
@Strain 0.777 %,
Temperature 60.0 °C		2180 psi
@Strain 0.777 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 20.0 MPa
@Strain 1.07 %,
Temperature 60.0 °C		2900 psi
@Strain 1.07 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.480 %,
Temperature 23.0 °C		2900 psi
@Strain 0.480 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.982 %,
Temperature 60.0 °C		2900 psi
@Strain 0.982 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.420 %,
Temperature 23.0 °C		2900 psi
@Strain 0.420 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 25.0 MPa
@Strain 1.27 %,
Temperature 60.0 °C		3630 psi
@Strain 1.27 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 25.0 MPa
@Strain 1.39 %,
Temperature 60.0 °C		3630 psi
@Strain 1.39 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 30.0 MPa
@Strain 1.80 %,
Temperature 60.0 °C		4350 psi
@Strain 1.80 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.740 %,
Temperature 23.0 °C		4350 psi
@Strain 0.740 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 30.0 MPa
@Strain 1.63 %,
Temperature 60.0 °C		4350 psi
@Strain 1.63 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.650 %,
Temperature 23.0 °C		4350 psi
@Strain 0.650 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 35.0 MPa
@Strain 2.14 %,
Temperature 60.0 °C		5080 psi
@Strain 2.14 %,
Temperature 140 °F		1h; Break; Isochronous; ISO 899
 35.0 MPa
@Strain 2.38 %,
Temperature 60.0 °C		5080 psi
@Strain 2.38 %,
Temperature 140 °F		10h; Break; Isochronous; ISO 899
 40.0 MPa
@Strain 1.03 %,
Temperature 23.0 °C		5800 psi
@Strain 1.03 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.900 %,
Temperature 23.0 °C		5800 psi
@Strain 0.900 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 50.0 MPa
@Strain 1.34 %,
Temperature 23.0 °C		7250 psi
@Strain 1.34 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 50.0 MPa
@Strain 1.18 %,
Temperature 23.0 °C		7250 psi
@Strain 1.18 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 60.0 MPa
@Strain 1.50 %,
Temperature 23.0 °C		8700 psi
@Strain 1.50 %,
Temperature 73.4 °F		1h; Break; Isochronous; ISO 899
 60.0 MPa
@Strain 1.68 %,
Temperature 23.0 °C		8700 psi
@Strain 1.68 %,
Temperature 73.4 °F		10h; Break; Isochronous; ISO 899
Tensile Creep Modulus, 1000 hours 3500 MPa
@Temperature 23.0 °C		508000 psi
@Temperature 73.4 °F		ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.279 %,
Temperature 60.0 °C		725 psi
@Strain 0.279 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.275 %,
Temperature 60.0 °C		725 psi
@Strain 0.275 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.550 %,
Temperature 60.0 °C		1450 psi
@Strain 0.550 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.260 %,
Temperature 23.0 °C		1450 psi
@Strain 0.260 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.310 %,
Temperature 23.0 °C		1450 psi
@Strain 0.310 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.560 %,
Temperature 60.0 °C		1450 psi
@Strain 0.560 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.287 %,
Temperature 23.0 °C		1450 psi
@Strain 0.287 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 15.0 MPa
@Strain 0.834 %,
Temperature 60.0 °C		2180 psi
@Strain 0.834 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 15.0 MPa
@Strain 0.852 %,
Temperature 60.0 °C		2180 psi
@Strain 0.852 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 20.0 MPa
@Strain 1.17 %,
Temperature 60.0 °C		2900 psi
@Strain 1.17 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 20.0 MPa
@Strain 1.14 %,
Temperature 60.0 °C		2900 psi
@Strain 1.14 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.535 %,
Temperature 23.0 °C		2900 psi
@Strain 0.535 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.656 %,
Temperature 23.0 °C		2900 psi
@Strain 0.656 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.602 %,
Temperature 23.0 °C		2900 psi
@Strain 0.602 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 25.0 MPa
@Strain 1.48 %,
Temperature 60.0 °C		3630 psi
@Strain 1.48 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 25.0 MPa
@Strain 1.53 %,
Temperature 60.0 °C		3630 psi
@Strain 1.53 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 30.0 MPa
@Strain 1.99 %,
Temperature 60.0 °C		4350 psi
@Strain 1.99 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.820 %,
Temperature 23.0 °C		4350 psi
@Strain 0.820 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 30.0 MPa
@Strain 1.01 %,
Temperature 23.0 °C		4350 psi
@Strain 1.01 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.920 %,
Temperature 23.0 °C		4350 psi
@Strain 0.920 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 30.0 MPa
@Strain 1.90 %,
Temperature 60.0 °C		4350 psi
@Strain 1.90 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 35.0 MPa
@Strain 2.50 %,
Temperature 60.0 °C		5080 psi
@Strain 2.50 %,
Temperature 140 °F		100h; Break; Isochronous; ISO 899
 35.0 MPa
@Strain 2.70 %,
Temperature 60.0 °C		5080 psi
@Strain 2.70 %,
Temperature 140 °F		1000h; Break; Isochronous; ISO 899
 40.0 MPa
@Strain 1.28 %,
Temperature 23.0 °C		5800 psi
@Strain 1.28 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 40.0 MPa
@Strain 1.14 %,
Temperature 23.0 °C		5800 psi
@Strain 1.14 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 40.0 MPa
@Strain 1.39 %,
Temperature 23.0 °C		5800 psi
@Strain 1.39 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 50.0 MPa
@Strain 1.49 %,
Temperature 23.0 °C		7250 psi
@Strain 1.49 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 50.0 MPa
@Strain 1.64 %,
Temperature 23.0 °C		7250 psi
@Strain 1.64 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 50.0 MPa
@Strain 1.78 %,
Temperature 23.0 °C		7250 psi
@Strain 1.78 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 60.0 MPa
@Strain 2.23 %,
Temperature 23.0 °C		8700 psi
@Strain 2.23 %,
Temperature 73.4 °F		10000h; Break; Isochronous; ISO 899
 60.0 MPa
@Strain 2.06 %,
Temperature 23.0 °C		8700 psi
@Strain 2.06 %,
Temperature 73.4 °F		1000h; Break; Isochronous; ISO 899
 60.0 MPa
@Strain 1.87 %,
Temperature 23.0 °C		8700 psi
@Strain 1.87 %,
Temperature 73.4 °F		100h; Break; Isochronous; ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity >= 1.00e+15 ohm-cm
@Temperature 23.0 °C		>= 1.00e+15 ohm-cm
@Temperature 73.4 °F		IEC 60093
Surface Resistance 1.00e+15 ohm
@Temperature 23.0 °C		1.00e+15 ohm
@Temperature 73.4 °F		IEC 60093
Dielectric Constant  3.4
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.4
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
 3.6
@Frequency 100 Hz,
Temperature 23.0 °C		3.6
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
Dielectric Strength 26.0 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		660 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		IEC 60243-1
 17.0 kV/mm
@Thickness 2.00 mm,
Time 20.0 sec		432 kV/in
@Thickness 0.0787 in,
Time 0.00556 hour		IEC 60243-1
Dissipation Factor  0.0030
@Frequency 100 Hz,
Temperature 23.0 °C		0.0030
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
 0.017
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.017
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
Comparative Tracking Index  250 V
@Temperature 23.0 °C		250 V
@Temperature 73.4 °F		IEC 60112
 250 V
@Temperature 23.0 °C		250 V
@Temperature 73.4 °F		UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  110 µm/m-°C
@Temperature 23.0 - 55.0 °C		61.1 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 110 µm/m-°C
@Temperature 23.0 - 55.0 °C		61.1 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi) 215 °C419 °FISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 200 °C392 °FISO 75-1/-2
Deflection Temperature at 5.0 MPa 152 °C306 °F4x100x100mm plaque; ISO 75-1/-2
Deflection Temperature at 8.0 MPa 64.0 °C147 °FISO 75-1/-2
UL RTI, Electrical  140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		UL 746B
 140 °C
@Thickness 6.00 mm		284 °F
@Thickness 0.236 in		UL 746B
 140 °C
@Thickness 1.50 mm		284 °F
@Thickness 0.0591 in		UL 746B
UL RTI, Mechanical with Impact  130 °C
@Thickness 6.00 mm		266 °F
@Thickness 0.236 in		UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
 140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical without Impact  140 °C
@Thickness 6.00 mm		284 °F
@Thickness 0.236 in		UL 746B
 140 °C
@Thickness 1.50 mm		284 °F
@Thickness 0.0591 in		UL 746B
 140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		UL 746B
Flammability, UL94  V-0
@Thickness 3.00 mm		V-0
@Thickness 0.118 in		IEC 60695-11-10
 V-0
@Thickness 6.00 mm		V-0
@Thickness 0.236 in		IEC 60695-11-10
 V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		IEC 60695-11-10
 V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		UL94
 V-0
@Thickness 3.00 mm		V-0
@Thickness 0.118 in		UL94
 V-0
@Thickness 6.00 mm		V-0
@Thickness 0.236 in		UL94
Oxygen Index 31 %31 %ISO 4589-1/-2
Glow Wire Test 960 °C
@Thickness 3.00 mm		1760 °F
@Thickness 0.118 in		IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 225 °C437 °F10°C/min; ISO 11357-1/-3
 250 °C482 °FOptimum
 240 - 260 °C464 - 500 °F
Mold Temperature 80.0 °C176 °Foptimum
 30.0 - 130 °C86.0 - 266 °F
Drying Temperature 110 - 130 °C230 - 266 °F
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hour
Moisture Content <= 0.040 %<= 0.040 %
 
Descriptive Properties
Contains Flame RetardantYes
Drying RecommendedYes
FormsPellets
GenericPBT
Material StatusCurrent
Part Marking Code>PBT-GF10FR(17)<ISO 11469
Polymer FamilyPolyester
Polymer TypePBT
Processing Methodinjection Molding
Product CategoryFlame Retardant Resins
 Glass Reinforced Resins
Resin IdentificationPBT-GF10FR(17)ISO 1043
RoHS ComplianceContact Manufacturer
Ultrasonic WeldableYes

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38093.html

免责声明: 本文 DuPont Performance Polymers Crastin® SK641FR NC010 PBT 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4