- 熔体流动速率 [g/10min]: 3.2
- 密度 [g/cm3]: 1.25
- 缺口冲击强度: 11.0
- 拉伸强度 [MPa]: 48.0
- 热变形温度 [℃]: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | |
| Melt Flow | 3.2 g/10 min @Load 2.16 kg, Temperature 250 °C | 3.2 g/10 min @Load 4.76 lb, Temperature 482 °F | cm³/10 min |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | 50 mm/min |
| Elongation at Break | 20 % | 20 % | Nominal strain at break (50 mm/min) |
| Elongation at Yield | 3.6 % | 3.6 % | 50 mm/min |
| Tensile Modulus | 2.80 GPa | 406 ksi | 1 mm/min |
| Izod Impact, Unnotched | 9.50 J/cm | 17.8 ft-lb/in | J/cm² |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² @Temperature -30.0 °C | 5.23 ft-lb/in² @Temperature -22.0 °F | |
| Izod Impact, Unnotched (ISO) | 80.0 kJ/m² @Temperature -30.0 °C | 38.1 ft-lb/in² @Temperature -22.0 °F | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | |
| Vicat Softening Point | 123 °C | 253 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |