  3. PBT
  4. DuPont Performance Polymers Crastin® SK645FR NC010 PBT

DuPont Performance Polymers Crastin® SK645FR NC010 PBT

DuPont Performance Polymers Crastin® SK645FR NC010 PBT 物性表: DuPont Performance Polymers Crastin® SK645FR NC010 PBT物性表及特性介绍,DuPont Performance Polymers Crastin® SK645FR NC010 PBT注塑参数详情,如需DuPont Performance Polymers Crastin® SK645FR NC010 PBT下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.71
  • 吸水率 [%]: 0.1
  • 缺口冲击强度: 8.0
  • 热变形温度 [℃]: 220.0
 
Physical PropertiesMetricEnglishComments
Density 1.71 g/cc0.0618 lb/in³ISO 1183
Filler Content 30 %30 %
Water Absorption  0.10 %
@Temperature 23.0 °C		0.10 %
@Temperature 73.4 °F		Equilibrium 50%RH; ISO 62, Similar to
 0.30 %
@Temperature 23.0 °C		0.30 %
@Temperature 73.4 °F		Saturation, immersed; ISO 62, Similar to
Viscosity  52000 cP
@Shear Rate 10000 1/s,
Temperature 260 °C		52000 cP
@Shear Rate 10000 1/s,
Temperature 500 °F		ISO 11443
 70000 cP
@Shear Rate 10000 1/s,
Temperature 250 °C		70000 cP
@Shear Rate 10000 1/s,
Temperature 482 °F		ISO 11443
 73000 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		73000 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		ISO 11443
 97000 cP
@Shear Rate 10000 1/s,
Temperature 240 °C		97000 cP
@Shear Rate 10000 1/s,
Temperature 464 °F		ISO 11443
 98000 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		98000 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		ISO 11443
 113000 cP
@Shear Rate 2000 1/s,
Temperature 260 °C		113000 cP
@Shear Rate 2000 1/s,
Temperature 500 °F		ISO 11443
 136000 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		136000 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		ISO 11443
 152000 cP
@Shear Rate 2000 1/s,
Temperature 250 °C		152000 cP
@Shear Rate 2000 1/s,
Temperature 482 °F		ISO 11443
 158000 cP
@Shear Rate 1000 1/s,
Temperature 260 °C		158000 cP
@Shear Rate 1000 1/s,
Temperature 500 °F		ISO 11443
 211000 cP
@Shear Rate 2000 1/s,
Temperature 240 °C		211000 cP
@Shear Rate 2000 1/s,
Temperature 464 °F		ISO 11443
 212000 cP
@Shear Rate 1000 1/s,
Temperature 250 °C		212000 cP
@Shear Rate 1000 1/s,
Temperature 482 °F		ISO 11443
 219000 cP
@Shear Rate 500 1/s,
Temperature 260 °C		219000 cP
@Shear Rate 500 1/s,
Temperature 500 °F		ISO 11443
 295000 cP
@Shear Rate 1000 1/s,
Temperature 240 °C		295000 cP
@Shear Rate 1000 1/s,
Temperature 464 °F		ISO 11443
 295000 cP
@Shear Rate 500 1/s,
Temperature 250 °C		295000 cP
@Shear Rate 500 1/s,
Temperature 482 °F		ISO 11443
 411000 cP
@Shear Rate 500 1/s,
Temperature 240 °C		411000 cP
@Shear Rate 500 1/s,
Temperature 464 °F		ISO 11443
 454000 cP
@Shear Rate 100 1/s,
Temperature 260 °C		454000 cP
@Shear Rate 100 1/s,
Temperature 500 °F		ISO 11443
 624000 cP
@Shear Rate 100 1/s,
Temperature 250 °C		624000 cP
@Shear Rate 100 1/s,
Temperature 482 °F		ISO 11443
 878000 cP
@Shear Rate 100 1/s,
Temperature 240 °C		878000 cP
@Shear Rate 100 1/s,
Temperature 464 °F		ISO 11443
Linear Mold Shrinkage, Flow 0.0045 cm/cm0.0045 in/inParallel; Annealed; ISO 294-4
 0.0035 cm/cm
@Thickness 2.00 mm		0.0035 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.015 cm/cm0.015 in/inNormal; Annealed; ISO 294-4
 0.0125 cm/cm
@Thickness 2.00 mm		0.0125 in/in
@Thickness 0.0787 in		Normal; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 125 MPa
@Temperature 23.0 °C		18100 psi
@Temperature 73.4 °F		ISO 527
Tensile Stress  9.09 MPa
@Strain 0.250 %,
Temperature 160 °C		1320 psi
@Strain 0.250 %,
Temperature 320 °F		ISO 527
 12.4 MPa
@Strain 0.250 %,
Temperature 120 °C		1800 psi
@Strain 0.250 %,
Temperature 248 °F		ISO 527
 14.1 MPa
@Strain 0.250 %,
Temperature 100 °C		2050 psi
@Strain 0.250 %,
Temperature 212 °F		ISO 527
 15.5 MPa
@Strain 0.250 %,
Temperature 80.0 °C		2250 psi
@Strain 0.250 %,
Temperature 176 °F		ISO 527
 16.5 MPa
@Strain 0.500 %,
Temperature 160 °C		2390 psi
@Strain 0.500 %,
Temperature 320 °F		ISO 527
 18.8 MPa
@Strain 0.250 %,
Temperature 60.0 °C		2730 psi
@Strain 0.250 %,
Temperature 140 °F		ISO 527
 22.8 MPa
@Strain 0.500 %,
Temperature 120 °C		3310 psi
@Strain 0.500 %,
Temperature 248 °F		ISO 527
 23.6 MPa
@Strain 0.250 %,
Temperature 40.0 °C		3420 psi
@Strain 0.250 %,
Temperature 104 °F		ISO 527
 26.0 MPa
@Strain 0.500 %,
Temperature 100 °C		3770 psi
@Strain 0.500 %,
Temperature 212 °F		ISO 527
 27.4 MPa
@Strain 1.00 %,
Temperature 160 °C		3970 psi
@Strain 1.00 %,
Temperature 320 °F		ISO 527
 28.8 MPa
@Strain 0.500 %,
Temperature 80.0 °C		4180 psi
@Strain 0.500 %,
Temperature 176 °F		ISO 527
 29.6 MPa
@Strain 0.250 %,
Temperature 23.0 °C		4290 psi
@Strain 0.250 %,
Temperature 73.4 °F		ISO 527
 31.0 MPa
@Strain 0.250 %,
Temperature 0.000 °C		4500 psi
@Strain 0.250 %,
Temperature 32.0 °F		ISO 527
 32.6 MPa
@Strain 0.250 %,
Temperature -20.0 °C		4730 psi
@Strain 0.250 %,
Temperature -4.00 °F		ISO 527
 33.5 MPa
@Strain 0.250 %,
Temperature -40.0 °C		4860 psi
@Strain 0.250 %,
Temperature -40.0 °F		ISO 527
 34.1 MPa
@Strain 0.500 %,
Temperature 60.0 °C		4950 psi
@Strain 0.500 %,
Temperature 140 °F		ISO 527
 34.5 MPa
@Strain 1.50 %,
Temperature 160 °C		5000 psi
@Strain 1.50 %,
Temperature 320 °F		ISO 527
 38.5 MPa
@Strain 1.00 %,
Temperature 120 °C		5580 psi
@Strain 1.00 %,
Temperature 248 °F		ISO 527
 39.2 MPa
@Strain 2.00 %,
Temperature 160 °C		5690 psi
@Strain 2.00 %,
Temperature 320 °F		ISO 527
 42.1 MPa
@Strain 2.50 %,
Temperature 160 °C		6110 psi
@Strain 2.50 %,
Temperature 320 °F		ISO 527
 43.8 MPa
@Strain 3.00 %,
Temperature 160 °C		6350 psi
@Strain 3.00 %,
Temperature 320 °F		Break; ISO 527
 44.2 MPa
@Strain 1.00 %,
Temperature 100 °C		6410 psi
@Strain 1.00 %,
Temperature 212 °F		ISO 527
 44.9 MPa
@Strain 0.500 %,
Temperature 40.0 °C		6510 psi
@Strain 0.500 %,
Temperature 104 °F		ISO 527
 49.1 MPa
@Strain 1.50 %,
Temperature 120 °C		7120 psi
@Strain 1.50 %,
Temperature 248 °F		ISO 527
 49.5 MPa
@Strain 1.00 %,
Temperature 80.0 °C		7180 psi
@Strain 1.00 %,
Temperature 176 °F		ISO 527
 55.8 MPa
@Strain 2.00 %,
Temperature 120 °C		8090 psi
@Strain 2.00 %,
Temperature 248 °F		ISO 527
 56.1 MPa
@Strain 1.50 %,
Temperature 100 °C		8140 psi
@Strain 1.50 %,
Temperature 212 °F		ISO 527
 56.1 MPa
@Strain 0.500 %,
Temperature 23.0 °C		8140 psi
@Strain 0.500 %,
Temperature 73.4 °F		ISO 527
 56.7 MPa
@Strain 1.00 %,
Temperature 60.0 °C		8220 psi
@Strain 1.00 %,
Temperature 140 °F		ISO 527
 59.2 MPa
@Strain 0.500 %,
Temperature 0.000 °C		8590 psi
@Strain 0.500 %,
Temperature 32.0 °F		ISO 527
 60.0 MPa
@Strain 2.50 %,
Temperature 120 °C		8700 psi
@Strain 2.50 %,
Temperature 248 °F		ISO 527
 62.3 MPa
@Strain 3.00 %,
Temperature 120 °C		9040 psi
@Strain 3.00 %,
Temperature 248 °F		Break; ISO 527
 62.5 MPa
@Strain 0.500 %,
Temperature -20.0 °C		9060 psi
@Strain 0.500 %,
Temperature -4.00 °F		ISO 527
 63.5 MPa
@Strain 2.00 %,
Temperature 100 °C		9210 psi
@Strain 2.00 %,
Temperature 212 °F		ISO 527
 63.7 MPa
@Strain 1.50 %,
Temperature 80.0 °C		9240 psi
@Strain 1.50 %,
Temperature 176 °F		ISO 527
 64.7 MPa
@Strain 0.500 %,
Temperature -40.0 °C		9380 psi
@Strain 0.500 %,
Temperature -40.0 °F		ISO 527
 67.7 MPa
@Strain 2.50 %,
Temperature 100 °C		9820 psi
@Strain 2.50 %,
Temperature 212 °F		ISO 527
 69.7 MPa
@Strain 3.00 %,
Temperature 100 °C		10100 psi
@Strain 3.00 %,
Temperature 212 °F		Break; ISO 527
 71.5 MPa
@Strain 1.50 %,
Temperature 60.0 °C		10400 psi
@Strain 1.50 %,
Temperature 140 °F		ISO 527
 72.7 MPa
@Strain 2.00 %,
Temperature 80.0 °C		10500 psi
@Strain 2.00 %,
Temperature 176 °F		ISO 527
 77.8 MPa
@Strain 2.50 %,
Temperature 80.0 °C		11300 psi
@Strain 2.50 %,
Temperature 176 °F		ISO 527
 78.6 MPa
@Strain 1.00 %,
Temperature 40.0 °C		11400 psi
@Strain 1.00 %,
Temperature 104 °F		ISO 527
 80.2 MPa
@Strain 3.00 %,
Temperature 80.0 °C		11600 psi
@Strain 3.00 %,
Temperature 176 °F		Break; ISO 527
 80.8 MPa
@Strain 2.00 %,
Temperature 60.0 °C		11700 psi
@Strain 2.00 %,
Temperature 140 °F		ISO 527
 86.5 MPa
@Strain 2.50 %,
Temperature 60.0 °C		12500 psi
@Strain 2.50 %,
Temperature 140 °F		ISO 527
 89.7 MPa
@Strain 3.00 %,
Temperature 60.0 °C		13000 psi
@Strain 3.00 %,
Temperature 140 °F		Break; ISO 527
 97.3 MPa
@Strain 1.00 %,
Temperature 23.0 °C		14100 psi
@Strain 1.00 %,
Temperature 73.4 °F		ISO 527
 100 MPa
@Strain 1.50 %,
Temperature 40.0 °C		14500 psi
@Strain 1.50 %,
Temperature 104 °F		ISO 527
 104 MPa
@Strain 1.00 %,
Temperature 0.000 °C		15100 psi
@Strain 1.00 %,
Temperature 32.0 °F		ISO 527
 111 MPa
@Strain 1.00 %,
Temperature -20.0 °C		16100 psi
@Strain 1.00 %,
Temperature -4.00 °F		ISO 527
 112 MPa
@Strain 2.00 %,
Temperature 40.0 °C		16200 psi
@Strain 2.00 %,
Temperature 104 °F		ISO 527
 116 MPa
@Strain 2.50 %,
Temperature 40.0 °C		16800 psi
@Strain 2.50 %,
Temperature 104 °F		Break; ISO 527
 116 MPa
@Strain 1.00 %,
Temperature -40.0 °C		16800 psi
@Strain 1.00 %,
Temperature -40.0 °F		ISO 527
 123 MPa
@Strain 1.50 %,
Temperature 23.0 °C		17800 psi
@Strain 1.50 %,
Temperature 73.4 °F		ISO 527
 135 MPa
@Strain 2.00 %,
Temperature 23.0 °C		19600 psi
@Strain 2.00 %,
Temperature 73.4 °F		ISO 527
 135 MPa
@Strain 1.50 %,
Temperature 0.000 °C		19600 psi
@Strain 1.50 %,
Temperature 32.0 °F		ISO 527
 140 MPa
@Strain 2.50 %,
Temperature 23.0 °C		20300 psi
@Strain 2.50 %,
Temperature 73.4 °F		Break; ISO 527
 144 MPa
@Strain 1.50 %,
Temperature -20.0 °C		20900 psi
@Strain 1.50 %,
Temperature -4.00 °F		ISO 527
 151 MPa
@Strain 1.50 %,
Temperature -40.0 °C		21900 psi
@Strain 1.50 %,
Temperature -40.0 °F		ISO 527
 156 MPa
@Strain 2.00 %,
Temperature 0.000 °C		22600 psi
@Strain 2.00 %,
Temperature 32.0 °F		Break; ISO 527
 163 MPa
@Strain 2.00 %,
Temperature -20.0 °C		23600 psi
@Strain 2.00 %,
Temperature -4.00 °F		Break; ISO 527
 170 MPa
@Strain 2.00 %,
Temperature -40.0 °C		24700 psi
@Strain 2.00 %,
Temperature -40.0 °F		Break; ISO 527
Elongation at Break 2.4 %
@Temperature 23.0 °C		2.4 %
@Temperature 73.4 °F		ISO 527
Tensile Modulus 11.2 GPa
@Temperature 23.0 °C		1620 ksi
@Temperature 73.4 °F		ISO 527
Flexural Strength 215 MPa
@Temperature 23.0 °C		31200 psi
@Temperature 73.4 °F		ISO 178
Shear Modulus  0.385 GPa
@Temperature 200 °C		55.8 ksi
@Temperature 392 °F		ISO 6721
 0.480 GPa
@Temperature 190 °C		69.6 ksi
@Temperature 374 °F		ISO 6721
 0.558 GPa
@Temperature 180 °C		80.9 ksi
@Temperature 356 °F		ISO 6721
 0.625 GPa
@Temperature 170 °C		90.6 ksi
@Temperature 338 °F		ISO 6721
 0.674 GPa
@Temperature 160 °C		97.8 ksi
@Temperature 320 °F		ISO 6721
 0.717 GPa
@Temperature 150 °C		104 ksi
@Temperature 302 °F		ISO 6721
 0.759 GPa
@Temperature 140 °C		110 ksi
@Temperature 284 °F		ISO 6721
 0.800 GPa
@Temperature 130 °C		116 ksi
@Temperature 266 °F		ISO 6721
 0.839 GPa
@Temperature 120 °C		122 ksi
@Temperature 248 °F		ISO 6721
 0.884 GPa
@Temperature 110 °C		128 ksi
@Temperature 230 °F		ISO 6721
 0.932 GPa
@Temperature 100 °C		135 ksi
@Temperature 212 °F		ISO 6721
 0.988 GPa
@Temperature 90.0 °C		143 ksi
@Temperature 194 °F		ISO 6721
 1.07 GPa
@Temperature 80.0 °C		155 ksi
@Temperature 176 °F		ISO 6721
 1.19 GPa
@Temperature 70.0 °C		173 ksi
@Temperature 158 °F		ISO 6721
 1.35 GPa
@Temperature 60.0 °C		196 ksi
@Temperature 140 °F		ISO 6721
 1.59 GPa
@Temperature 50.0 °C		231 ksi
@Temperature 122 °F		ISO 6721
 1.87 GPa
@Temperature 40.0 °C		271 ksi
@Temperature 104 °F		ISO 6721
 2.04 GPa
@Temperature 30.0 °C		296 ksi
@Temperature 86.0 °F		ISO 6721
 2.11 GPa
@Temperature 20.0 °C		306 ksi
@Temperature 68.0 °F		ISO 6721
 2.17 GPa
@Temperature 10.0 °C		315 ksi
@Temperature 50.0 °F		ISO 6721
 2.21 GPa
@Temperature 0.000 °C		321 ksi
@Temperature 32.0 °F		ISO 6721
 2.26 GPa
@Temperature -10.0 °C		328 ksi
@Temperature 14.0 °F		ISO 6721
 2.31 GPa
@Temperature -20.0 °C		335 ksi
@Temperature -4.00 °F		ISO 6721
 2.35 GPa
@Temperature -30.0 °C		341 ksi
@Temperature -22.0 °F		ISO 6721
 2.39 GPa
@Temperature -40.0 °C		347 ksi
@Temperature -40.0 °F		ISO 6721
 2.43 GPa
@Temperature -50.0 °C		352 ksi
@Temperature -58.0 °F		ISO 6721
Izod Impact, Notched (ISO)  8.00 kJ/m²
@Temperature -30.0 °C		3.81 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1A
 9.00 kJ/m²
@Temperature 23.0 °C		4.28 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1A
Izod Impact, Unnotched (ISO)  40.0 kJ/m²
@Temperature -30.0 °C		19.0 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1U
 40.0 kJ/m²
@Temperature 23.0 °C		19.0 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1U
Charpy Impact Unnotched  5.30 J/cm²
@Temperature 23.0 °C		25.2 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
 5.70 J/cm²
@Temperature -30.0 °C		27.1 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
Charpy Impact, Notched  0.910 J/cm²
@Temperature 23.0 °C		4.33 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
 0.940 J/cm²
@Temperature -30.0 °C		4.47 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
Tensile Creep Modulus, 1 hour 11000 MPa
@Temperature 23.0 °C		1.60e+6 psi
@Temperature 73.4 °F		ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.170 %,
Temperature 60.0 °C		1450 psi
@Strain 0.170 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.0930 %,
Temperature 23.0 °C		1450 psi
@Strain 0.0930 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.0910 %,
Temperature 23.0 °C		1450 psi
@Strain 0.0910 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.160 %,
Temperature 60.0 °C		1450 psi
@Strain 0.160 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.330 %,
Temperature 60.0 °C		2900 psi
@Strain 0.330 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.190 %,
Temperature 23.0 °C		2900 psi
@Strain 0.190 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.197 %,
Temperature 23.0 °C		2900 psi
@Strain 0.197 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.350 %,
Temperature 60.0 °C		2900 psi
@Strain 0.350 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.530 %,
Temperature 60.0 °C		4350 psi
@Strain 0.530 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.313 %,
Temperature 23.0 °C		4350 psi
@Strain 0.313 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.297 %,
Temperature 23.0 °C		4350 psi
@Strain 0.297 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.490 %,
Temperature 60.0 °C		4350 psi
@Strain 0.490 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.660 %,
Temperature 60.0 °C		5800 psi
@Strain 0.660 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.412 %,
Temperature 23.0 °C		5800 psi
@Strain 0.412 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.439 %,
Temperature 23.0 °C		5800 psi
@Strain 0.439 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.720 %,
Temperature 60.0 °C		5800 psi
@Strain 0.720 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.960 %,
Temperature 60.0 °C		7250 psi
@Strain 0.960 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.575 %,
Temperature 23.0 °C		7250 psi
@Strain 0.575 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.860 %,
Temperature 60.0 °C		7250 psi
@Strain 0.860 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.536 %,
Temperature 23.0 °C		7250 psi
@Strain 0.536 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 60.0 MPa
@Strain 0.669 %,
Temperature 23.0 °C		8700 psi
@Strain 0.669 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 60.0 MPa
@Strain 1.11 %,
Temperature 60.0 °C		8700 psi
@Strain 1.11 %,
Temperature 140 °F		1h; Break; Isochronous; ISO 899
 60.0 MPa
@Strain 1.29 %,
Temperature 60.0 °C		8700 psi
@Strain 1.29 %,
Temperature 140 °F		10h; Break; Isochronous; ISO 899
 60.0 MPa
@Strain 0.720 %,
Temperature 23.0 °C		8700 psi
@Strain 0.720 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 70.0 MPa
@Strain 0.874 %,
Temperature 23.0 °C		10200 psi
@Strain 0.874 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 70.0 MPa
@Strain 0.811 %,
Temperature 23.0 °C		10200 psi
@Strain 0.811 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 80.0 MPa
@Strain 0.963 %,
Temperature 23.0 °C		11600 psi
@Strain 0.963 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 80.0 MPa
@Strain 1.04 %,
Temperature 23.0 °C		11600 psi
@Strain 1.04 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 90.0 MPa
@Strain 1.21 %,
Temperature 23.0 °C		13100 psi
@Strain 1.21 %,
Temperature 73.4 °F		10h; Break; Isochronous; ISO 899
 90.0 MPa
@Strain 1.12 %,
Temperature 23.0 °C		13100 psi
@Strain 1.12 %,
Temperature 73.4 °F		1h; Break; Isochronous; ISO 899
Tensile Creep Modulus, 1000 hours 8000 MPa
@Temperature 23.0 °C		1.16e+6 psi
@Temperature 73.4 °F		ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.103 %,
Temperature 23.0 °C		1450 psi
@Strain 0.103 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.180 %,
Temperature 60.0 °C		1450 psi
@Strain 0.180 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.175 %,
Temperature 60.0 °C		1450 psi
@Strain 0.175 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.123 %,
Temperature 23.0 °C		1450 psi
@Strain 0.123 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.256 %,
Temperature 23.0 °C		2900 psi
@Strain 0.256 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.360 %,
Temperature 60.0 °C		2900 psi
@Strain 0.360 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.380 %,
Temperature 60.0 °C		2900 psi
@Strain 0.380 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.213 %,
Temperature 23.0 °C		2900 psi
@Strain 0.213 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.332 %,
Temperature 23.0 °C		4350 psi
@Strain 0.332 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.570 %,
Temperature 60.0 °C		4350 psi
@Strain 0.570 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.550 %,
Temperature 60.0 °C		4350 psi
@Strain 0.550 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.401 %,
Temperature 23.0 °C		4350 psi
@Strain 0.401 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.560 %,
Temperature 23.0 °C		5800 psi
@Strain 0.560 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.760 %,
Temperature 60.0 °C		5800 psi
@Strain 0.760 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.780 %,
Temperature 60.0 °C		5800 psi
@Strain 0.780 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.462 %,
Temperature 23.0 °C		5800 psi
@Strain 0.462 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.606 %,
Temperature 23.0 °C		7250 psi
@Strain 0.606 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 50.0 MPa
@Strain 1.02 %,
Temperature 60.0 °C		7250 psi
@Strain 1.02 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.737 %,
Temperature 23.0 °C		7250 psi
@Strain 0.737 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 50.0 MPa
@Strain 1.00 %,
Temperature 60.0 °C		7250 psi
@Strain 1.00 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 60.0 MPa
@Strain 1.34 %,
Temperature 60.0 °C		8700 psi
@Strain 1.34 %,
Temperature 140 °F		100h; Break; Isochronous; ISO 899
 60.0 MPa
@Strain 0.766 %,
Temperature 23.0 °C		8700 psi
@Strain 0.766 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 60.0 MPa
@Strain 0.938 %,
Temperature 23.0 °C		8700 psi
@Strain 0.938 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 60.0 MPa
@Strain 1.36 %,
Temperature 60.0 °C		8700 psi
@Strain 1.36 %,
Temperature 140 °F		1000h; Break; Isochronous; ISO 899
 70.0 MPa
@Strain 1.17 %,
Temperature 23.0 °C		10200 psi
@Strain 1.17 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 70.0 MPa
@Strain 0.950 %,
Temperature 23.0 °C		10200 psi
@Strain 0.950 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 80.0 MPa
@Strain 1.17 %,
Temperature 23.0 °C		11600 psi
@Strain 1.17 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 80.0 MPa
@Strain 1.46 %,
Temperature 23.0 °C		11600 psi
@Strain 1.46 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 90.0 MPa
@Strain 1.83 %,
Temperature 23.0 °C		13100 psi
@Strain 1.83 %,
Temperature 73.4 °F		1000h; Break; Isochronous; ISO 899
 90.0 MPa
@Strain 1.44 %,
Temperature 23.0 °C		13100 psi
@Strain 1.44 %,
Temperature 73.4 °F		100h; Break; Isochronous; ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity >= 1.00e+15 ohm-cm
@Temperature 23.0 °C		>= 1.00e+15 ohm-cm
@Temperature 73.4 °F		IEC 60093
Surface Resistance 1.00e+15 ohm
@Temperature 23.0 °C		1.00e+15 ohm
@Temperature 73.4 °F		IEC 60093
Dielectric Constant  3.8
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.8
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
 4.5
@Frequency 100 Hz,
Temperature 23.0 °C		4.5
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
Dielectric Strength 28.0 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		711 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		IEC 60243-1
 17.0 kV/mm
@Thickness 2.00 mm,
Time 20.0 sec		432 kV/in
@Thickness 0.0787 in,
Time 0.00556 hour		IEC 60243-1
Dissipation Factor  0.0030
@Frequency 100 Hz,
Temperature 23.0 °C		0.0030
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
 0.016
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.016
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
Comparative Tracking Index  250 V
@Temperature 23.0 °C		250 V
@Temperature 73.4 °F		IEC 60112
 250 V
@Temperature 23.0 °C		250 V
@Temperature 73.4 °F		UL 746A
 250 - 400 V
@Temperature 23.0 °C		250 - 400 V
@Temperature 73.4 °F		UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  90.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		50.0 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 90.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		50.0 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi) 220 °C428 °FISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 210 °C410 °FISO 75-1/-2
Deflection Temperature at 5.0 MPa 186 °C367 °F4x100x100mm plaque; ISO 75-1/-2
Deflection Temperature at 8.0 MPa 164 °C327 °FISO 75-1/-2
UL RTI, Electrical  140 °C
@Thickness 1.50 mm		284 °F
@Thickness 0.0591 in		UL 746B
 140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		UL 746B
 140 °C
@Thickness 6.00 mm		284 °F
@Thickness 0.236 in		UL 746B
 140 °C
@Thickness 0.750 mm		284 °F
@Thickness 0.0295 in		UL 746B
UL RTI, Mechanical with Impact  125 °C
@Thickness 1.50 mm		257 °F
@Thickness 0.0591 in		UL 746B
 125 °C
@Thickness 0.750 mm		257 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 6.00 mm		266 °F
@Thickness 0.236 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical without Impact  140 °C
@Thickness 0.750 mm		284 °F
@Thickness 0.0295 in		UL 746B
 140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		UL 746B
 140 °C
@Thickness 1.50 mm		284 °F
@Thickness 0.0591 in		UL 746B
 140 °C
@Thickness 6.00 mm		284 °F
@Thickness 0.236 in		UL 746B
Flammability, UL94  V-0
@Thickness 0.750 mm		V-0
@Thickness 0.0295 in		IEC 60695-11-10
 V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		IEC 60695-11-10
 V-0
@Thickness 3.00 mm		V-0
@Thickness 0.118 in		IEC 60695-11-10
 V-0
@Thickness 6.00 mm		V-0
@Thickness 0.236 in		IEC 60695-11-10
 V-0
@Thickness 0.750 mm		V-0
@Thickness 0.0295 in		UL94
 V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		UL94
 V-0
@Thickness 3.00 mm		V-0
@Thickness 0.118 in		UL94
 V-0
@Thickness 6.00 mm		V-0
@Thickness 0.236 in		UL94
Oxygen Index 31 %31 %ISO 4589-1/-2
Glow Wire Test 960 °C
@Thickness 3.00 mm		1760 °F
@Thickness 0.118 in		IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 225 °C437 °F10°C/min; ISO 11357-1/-3
 250 °C482 °FOptimum
 240 - 260 °C464 - 500 °F
Mold Temperature 80.0 °C176 °Foptimum
 30.0 - 130 °C86.0 - 266 °F
Drying Temperature 110 - 130 °C230 - 266 °F
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hour
Moisture Content <= 0.040 %<= 0.040 %
 
Descriptive Properties
AppearanceNatural Color
Contains Flame RetardantYes
Drying RecommendedYes
FeaturesFlame Retardant
FillerGlass Reinforced
FormsPellets
GenericPBT
Material StatusCurrent
Part Marking Code>PBT-GF30FR(17)<ISO 11469
Polymer FamilyPolyester
Polymer TypePBT
Processing MethodInjection Molding
Product CategoryFlame Retardant Resins
 Glass Reinforced Resins
Region Available - GlobalYes
Resin IdentificationPBT-GF30FR(17)ISO 1043
RoHS ComplianceContact Manufacturer
Ultrasonic WeldableYes

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38109.html

免责声明: 本文 DuPont Performance Polymers Crastin® SK645FR NC010 PBT 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4