- 密度 [g/cm3]: 1.69
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.69 g/cc | 0.0611 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0044 cm/cm @Thickness 2.00 mm | 0.0044 in/in @Thickness 0.0787 in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0124 cm/cm @Thickness 2.00 mm | 0.0124 in/in @Thickness 0.0787 in | Normal; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 114 MPa @Temperature 23.0 °C | 16500 psi @Temperature 73.4 °F | ISO 527 | ||
| Elongation at Break | 2.6 % @Temperature 23.0 °C | 2.6 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 10.33 GPa @Temperature 23.0 °C | 1498 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 180 MPa @Temperature 23.0 °C | 26100 psi @Temperature 73.4 °F | ISO 178 | ||
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature 23.0 °C | 23.8 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.800 J/cm² @Temperature 23.0 °C | 3.81 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| UL RTI, Electrical | 140 °C @Thickness 0.750 mm | 284 °F @Thickness 0.0295 in | UL 746B | ||
| UL RTI, Mechanical with Impact | 125 °C @Thickness 0.750 mm | 257 °F @Thickness 0.0295 in | UL 746B | ||
| UL RTI, Mechanical without Impact | 140 °C @Thickness 0.750 mm | 284 °F @Thickness 0.0295 in | UL 746B | ||
| Flammability, UL94 | V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| 240 - 260 °C | 464 - 500 °F | ||||
| Mold Temperature | 30.0 - 130 °C | 86.0 - 266 °F | |||
| 80.0 °C | 176 °F | optimum | |||
| Drying Temperature | 110 - 130 °C | 230 - 266 °F | |||
| Moisture Content | <= 0.040 % | <= 0.040 % | |||
| Descriptive Properties | |||||
| Appearance | Black Color | ||||
| Features | Flame Retardant | ||||
| Forms | Pellets | ||||
| Generic | PBT | ||||
| Material Status | Current | ||||
| Part Marking Code | >PBT-GF30(17)< | ISO 11469 | |||
| Processing Method | Injection Molding | ||||
| Product Category | Flame Retardant Resins | ||||
| Glass Reinforced Resins | |||||
| Region Available - Global | Yes | ||||
| Resin Identification | PBT-GF30(17) | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||