- 密度 [g/cm3]: 1.44
- 缺口冲击强度: 9.0
- 弯曲模量 [MPa]: 7.60
- 热变形温度 [℃]: 217.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.00300 - 0.00600 cm/cm | 0.00300 - 0.00600 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0140 - 0.0160 cm/cm | 0.0140 - 0.0160 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 62.0 | 62.0 | ISO 2039-2 | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 3.00 % | 3.00 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 8.10 GPa | 1170 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 | ||
| Flexural Modulus | 7.60 GPa | 1100 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | ISO 180/1U | ||
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179/1eU | ||
| 5.00 J/cm² @Temperature -30.0 °C | 23.8 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/1eA | ||
| 0.870 J/cm² @Temperature -30.0 °C | 4.14 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 23.0 µm/m-°C | 12.8 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 95.0 µm/m-°C | 52.8 µin/in-°F | ISO 11359-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 376 °F | ISO 75-1, -2 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 65.0 - 93.0 °C | 149 - 199 °F | Cavity temperature | ||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 265 °C | 455 - 509 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Pre-drying | 4 Hrs. at 250F, <0.02% moisture | ||||
| Special Information | Up to 25% regrind, clean and dry | ||||