- 密度 [g/cm3]: 1.53
- 缺口冲击强度: 0.908
- 弯曲模量 [MPa]: 9.70
- 热变形温度 [℃]: 228.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.00300 - 0.00500 cm/cm | 0.00300 - 0.00500 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 90.0 | 90.0 | ISO 2039-2 | ||
| Tensile Strength at Break | 130 MPa | 18900 psi | 5mm/min; ISO 527-2/1A | ||
| 134 MPa | 19500 psi | ASTM D638 | |||
| Elongation at Break | 2.00 % @Temperature 22.8 °C | 2.00 % @Temperature 73.0 °F | ASTM D638 | ||
| Flexural Strength | 193 MPa | 28000 psi | ASTM D790 | ||
| 210 MPa | 30500 psi | ISO 178 | |||
| Flexural Modulus | 9.70 GPa | 1410 ksi | ISO 178 | ||
| 82.7 GPa @Temperature 22.8 °C | 12000 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.908 J/cm | 1.70 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 7.50 kJ/m² | 3.57 ft-lb/in² | ISO 180/1A | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 228 °C | 442 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ASTM D648 | ||
| Flammability, UL94 | HB | HB | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 93.0 °C | 149 - 199 °F | Cavity temperature | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Middle Barrel Temperature | 235 - 250 °C | 455 - 482 °F | |||
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| 235 - 260 °C | 455 - 500 °F | ||||
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |||
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Processing Notes | Fast Injection Speed | ||||
| Medium Screw Speed | |||||