- 密度 [g/cm3]: 1.44
- 缺口冲击强度: 4.4
- 弯曲模量 [MPa]: 5.30
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 | ||
| Moisture Absorption | 0.170 % | 0.170 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.00100 - 0.00600 cm/cm | 0.00100 - 0.00600 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.00700 cm/cm | 0.00700 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 2.50 % | 2.50 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 6.10 GPa | 885 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 | ||
| Flexural Modulus | 5.30 GPa | 769 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 4.40 kJ/m² | 2.09 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179/1eU | ||
| 1.70 J/cm² @Temperature -30.0 °C | 8.09 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.470 J/cm² | 2.24 ft-lb/in² | ISO 179/1eA | ||
| 0.450 J/cm² @Temperature -30.0 °C | 2.14 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 7.00e+16 ohm-cm | 7.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | 4.00e+15 ohm | 4.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 2.70 @Frequency 100 Hz | 2.70 @Frequency 100 Hz | IEC 60250 | ||
| 2.70 @Frequency 1.00e+6 Hz | 2.70 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Dielectric Strength | 17.0 kV/mm | 432 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0140 @Frequency 1.00e+6 Hz | 0.0140 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 225 V | 225 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 42.0 µm/m-°C | 23.3 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 73.0 µm/m-°C | 40.6 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Transformation Temperature, Tg | 50.0 °C | 122 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 75-1, -2 | ||
| Flammability, UL94 | HB | HB | UL94 | ||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 93.0 °C | 149 - 199 °F | Cavity temperature | |||
| Feed Temperature | 230 - 250 °C | 446 - 482 °F | |||
| Zone 1 | 230 - 250 °C | 446 - 482 °F | |||
| Zone 2 | 235 - 255 °C | 455 - 491 °F | |||
| Zone 3 | 235 - 255 °C | 455 - 491 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 265 °C | 482 - 509 °F | |||
| Melt Temperature | 235 - 265 °C | 455 - 509 °F | |||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Hot-Working Temperature | 250 - 265 °C | 482 - 509 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | lower the temperature to 100° C until processed. | <= 60 h | |||