- 熔体流动速率 [g/10min]: 17.0
- 密度 [g/cm3]: 1.54
- 吸水率 [%]: 0.05
- 缺口冲击强度: 0.801
- 弯曲模量 [MPa]: 9.00
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ASTM D792 | ||
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.0500 % | 0.0500 % | 24hr immersion; ASTM D570 | ||
| Moisture Absorption | 0.200 % | 0.200 % | 23°C/50%RH; ISO 62 | ||
| Viscosity Test | 68.0 cm³/g | 68.0 cm³/g | ISO 307, 1157, 1628 | ||
| Linear Mold Shrinkage, Flow | 0.00300 - 0.00500 cm/cm | 0.00300 - 0.00500 in/in | ASTM D955 | ||
| 0.00300 - 0.00500 cm/cm | 0.00300 - 0.00500 in/in | ISO 294-4 | |||
| Melt Flow | 17.0 g/10 min | 17.0 g/10 min | ASTM D1238 | ||
| 20.0 g/10 min @Load 2.16 kg, Temperature 265 °C | 20.0 g/10 min @Load 4.76 lb, Temperature 509 °F | (MVR) cm³/10min; ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 93.0 | 93.0 | ISO 2039-2 | ||
| Tensile Strength at Break | 131 MPa | 19000 psi | ASTM D638 | ||
| 135 MPa | 19600 psi | 5mm/min; ISO 527-2/1A | |||
| Elongation at Break | 3.00 % | 3.00 % | 5mm/min; ISO 527-2/1A | ||
| 2.00 % @Temperature 22.8 °C | 2.00 % @Temperature 73.0 °F | ASTM D638 | |||
| Tensile Modulus | 10.0 GPa | 1450 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 200 MPa | 29000 psi | ASTM D790 | ||
| 200 MPa | 29000 psi | ISO 178 | |||
| Flexural Modulus | 9.00 GPa | 1310 ksi | ISO 178 | ||
| 8.96 GPa @Temperature 22.8 °C | 1300 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.801 J/cm | 1.50 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 8.30 kJ/m² | 3.95 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | 4.90 J/cm² | 23.3 ft-lb/in² | ISO 179/1eU | ||
| 4.80 J/cm² @Temperature -30.0 °C | 22.8 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.950 J/cm² | 4.52 ft-lb/in² | ISO 179/1eA | ||
| 0.900 J/cm² @Temperature -30.0 °C | 4.28 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | |||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.80 @Frequency 1.00e+6 Hz | 3.80 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 4.20 @Frequency 1.00e+6 Hz | 4.20 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| 4.60 @Frequency 100 Hz | 4.60 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 20.9 kV/mm | 530 kV/in | short term; ASTM D149 | ||
| 30.0 kV/mm | 762 kV/in | IEC 60243-1 | |||
| Dissipation Factor | 0.00200 @Frequency 1.00e+6 Hz | 0.00200 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| Comparative Tracking Index | 350 V | 350 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 24.0 µm/m-°C | 13.3 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 75.0 µm/m-°C | 41.7 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Transformation Temperature, Tg | 60.0 °C | 140 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1, -2 | ||
| 221 °C | 430 °F | ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1, -2 | ||
| 206 °C | 403 °F | ASTM D648 | |||
| Deflection Temperature at 8.0 MPa | 120 °C | 248 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 225 °C | 437 °F | B50 (50°C/h 50N); ISO 306 | ||
| Flammability, UL94 | HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | UL94 | ||
| Oxygen Index | 20.0 % | 20.0 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 93.0 °C | 149 - 199 °F | Cavity temperature | |||
| Feed Temperature | 230 - 250 °C | 446 - 482 °F | |||
| Zone 1 | 230 - 250 °C | 446 - 482 °F | |||
| Zone 2 | 235 - 255 °C | 455 - 491 °F | |||
| Zone 3 | 235 - 255 °C | 455 - 491 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 265 °C | 482 - 509 °F | |||
| Melt Temperature | 235 - 265 °C | 455 - 509 °F | |||
| 260 °C | 500 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 82.0 °C | 180 °F | Injection molding; ISO 294 | ||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Hold Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Hot-Working Temperature | 250 - 265 °C | 482 - 509 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | lower the temperature to 100° C until processed. | <= 60 h | |||
| Processing conditions | ISO 7792-2 | ||||