- 密度 [g/cm3]: 1.43
- 缺口冲击强度: 7.0
- 弯曲模量 [MPa]: 10.4
- 热变形温度 [℃]: 217.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00100 - 0.00300 cm/cm | 0.00100 - 0.00300 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00500 - 0.00700 cm/cm | 0.00500 - 0.00700 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 140 MPa | 20300 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 2.00 % | 2.00 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 10.7 GPa | 1550 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 |
| Flexural Modulus | 10.4 GPa | 1510 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO 180/1A |
| Charpy Impact, Notched | 0.720 J/cm² | 3.43 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Dielectric Strength | 18.0 kV/mm | 457 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.000 @Frequency 100 Hz | 0.000 @Frequency 100 Hz | IEC 60250 |
| Arc Resistance | 93.0 sec | 93.0 sec | ASTM D495 |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 184 °C | 363 °F | ISO 75-1, -2 |
| Flammability, UL94 | HB | HB | UL94 |