- 弯曲模量 [MPa]: 13.0
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Tensile Strength at Break | 175 MPa | 25400 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 1.65 % | 1.65 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 14.5 GPa | 2100 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 265 MPa | 38400 psi | ISO 178 | ||
| Flexural Modulus | 13.0 GPa | 1890 ksi | ISO 178 | ||
| Charpy Impact, Notched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179/1eA | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 90.0 - 100 °C | 194 - 212 °F | Cavity temperature | ||
| Feed Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Die Temperature | 265 - 285 °C | 509 - 545 °F | |||
| Melt Temperature | 265 - 285 °C | 509 - 545 °F | |||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Dew Point | <= -30.0 °C | <= -22.0 °F | Pre-drying | ||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||