- 密度 [g/cm3]: 1.61
- 弯曲模量 [MPa]: 12.65
- 热变形温度 [℃]: 226.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in³ | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 180 MPa | 26100 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 1.85 % | 1.85 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 13.62 GPa | 1975 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 270 MPa | 39200 psi | ISO 178 | ||
| Flexural Modulus | 12.65 GPa | 1835 ksi | ISO 178 | ||
| Charpy Impact, Notched | 3.20 J/cm² | 15.2 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 16.0 µm/m-°C | 8.89 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 87.0 µm/m-°C | 48.3 µin/in-°F | ISO 11359-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO 75-1, -2 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Feed Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |||
| Drying Temperature | 120 - 140 °C | 248 - 284 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Dew Point | <= -30.0 °C | <= -22.0 °F | Pre-drying | ||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||