- 密度 [g/cm3]: 1.31
- 吸水率 [%]: 0.09
- 缺口冲击强度: 0.267
- 拉伸强度 [MPa]: 55.2
- 弯曲模量 [MPa]: 2.20
- 热变形温度 [℃]: 154.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 | ||
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.0900 % | 0.0900 % | 24hr immersion; ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.0180 - 0.0200 cm/cm | 0.0180 - 0.0200 in/in | ASTM D955 | ||
| 0.0180 - 0.0200 cm/cm | 0.0180 - 0.0200 in/in | ISO 294-4 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 72.0 | 72.0 | ISO 2039-2 | ||
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 5mm/min; ISO 527-2/1A | ||
| Tensile Strength, Yield | 55.2 MPa | 8000 psi | ASTM D638 | ||
| Elongation at Break | 5.00 % | 5.00 % | 5mm/min; ISO 527-2/1A | ||
| 5.00 % @Temperature 22.8 °C | 5.00 % @Temperature 73.0 °F | ASTM D638 | |||
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 | ||
| 82.7 MPa | 12000 psi | ASTM D790 | |||
| Flexural Modulus | 2.20 GPa | 319 ksi | ISO 178 | ||
| 2.28 GPa @Temperature 22.8 °C | 330 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.267 J/cm | 0.500 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 3.10 kJ/m² | 1.48 ft-lb/in² | ISO 180/1A | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | |||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.20 @Frequency 1.00e+6 Hz | 3.20 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 3.20 @Frequency 1.00e+6 Hz | 3.20 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | IEC 60243-1 | ||
| 15.7 kV/mm | 400 kV/in | short term; ASTM D149 | |||
| Dissipation Factor | 0.00100 @Frequency 1.00e+6 Hz | 0.00100 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 0.0200 @Frequency 1.00e+6 Hz | 0.0200 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Transformation Temperature, Tg | 60.0 °C | 140 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 310 °F | ASTM D648 | ||
| 155 °C | 311 °F | ISO 75-1, -2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.4 °C | 130 °F | ASTM D648 | ||
| 57.0 °C | 135 °F | ISO 75-1, -2 | |||
| Flammability, UL94 | HB | HB | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 93.0 °C | 149 - 199 °F | Cavity temperature | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 243 °C | 469 °F | Injection molding; ISO 294 | ||
| 235 - 260 °C | 455 - 500 °F | ||||
| Mold Temperature | 82.0 °C | 180 °F | Injection molding; ISO 294 | ||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Hold Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | lower the temperature to 100° C until processed. | <= 60 h | |||
| Processing conditions | ISO 7792-2 | ||||